Pa 6 kompozitlerinin termal, mekanik ve tribolojik özelliklerinin incelenmesi

The investigation of mechanical, thermal and tribological properties of polyamide 6 composite materials

PDF İndir

  1. Tez No: 274797
  2. Yazar: TACETTİN SAYLAN
  3. Danışmanlar: PROF. DR. HÜSEYİN ÜNAL
  4. Tez Türü: Yüksek Lisans
  5. Konular: Metalurji Mühendisliği, Teknik Eğitim, Metallurgical Engineering, Technical Education
  6. Anahtar Kelimeler: Belirtilmemiş.
  7. Yıl: 2010
  8. Dil: Türkçe
  9. Üniversite: Sakarya Üniversitesi
  10. Enstitü: Fen Bilimleri Enstitüsü
  11. Ana Bilim Dalı: Metal Eğitimi Ana Bilim Dalı
  12. Bilim Dalı: Belirtilmemiş.
  13. Sayfa Sayısı: 180

Özet

Poliamid 6 malzemesine ağırlıkça %30'a kadar kısa cam elyaf ve mika dolguları katılarak ekstrüzyon ve enjeksiyon makinelerinde üretilmiştir. Kısa cam elyaf ve mika dolgular, ağırlıkça %10'dan başlayıp %30'a kadar değişik kombinasyonlarda malzeme ile referans olarak katkısız poliamid 6 malzemesi üretildi. Cam elyaf ve mika dolgu ilavesinin poliamid 6 malzemeye aşınma deneyleri, mekanik, tribolojik ve termal etkisini araştırmak için Dinamik mekanik analiz, diferansiyel taramalı kalorimetre, Vicat yumuşama sıcaklığı, yük altında eğilme sıcaklığı ve aşınma testleri uygulandı. Bu testlerde katkısız poliamid ve kompozitlerinin ergime sıcaklığı, camsı geçiş sıcaklığı, Vicat ve HDT değerleri, kayıp modülü, kayıp modülü, tan deltası, sürtünme katsayısı ve aşınma oranları değerleri elde edildi. Sonuç olarak erime ve camsı geçiş sıcaklığının cam elyaf ve mika ile arttığını, Vicat yumuşama sıcaklığı değerleri mika dolgu oranı arttıkça azalırken cam elyaf katkı oranı arttıkça artmaktadır. Depolama modülü ve kayıp modülü katkısız poliamid malzeme ile kıyaslandığında cam elyaf ve mika dolgularıyla artmıştır. Aşınma testleri pim disk aşınma cihazında yapıldı. Malzemeler %30 cam elyaf, %30 mika ve %6 vaks katkılı disk malzemelerine 20N, 30N ve 40N yük ile 0,5m/sn kayma hızında 1500 metre kayma yolunda yapıldı. Tüm malzeme kombinasyonları için yük miktarı arttıkça sürtünme katsayısı arttığı görülmüştür. Malzemelerin farklı sürtünme katsayıları ve özgül aşınma oranları elde edildi ve aşınma yüzeyleri optik mikroskop ile incelenmiştir.

Özet (Çeviri)

Polyamide 6 fillers with up to 30 wt% short glass fiber and mica, were prepared by extrusion and injection molding machine. Short glass fiber and mica fillers, with weight percentages varying between 10 and 30 wt% as single and as mixed, were added to Polyamide 6 thermoplastic matrix. In this study, dynamic mechanical analysis test, thermal properties such as differential scanning calorimeter test, vicat softening temperature, heat deflection temperature and tribological tests were used to examine the effect of short glass fiber and mica fillers addition on the mechanical behavior of polyamide 6 thermoplastic material. Storage modulus, loss modulus and tan deltha, melting temperature, glass transition temperature, vicat and HDT values, friction coefficient and wear rate values of unfilled polyamide and its composites were obtained. The results showed that the melting and glass transition temperature values increased with increment of glass fiber and mica. Vicat softening temperature values increased with the addition of glass fiber while Vicat softening temperature values decreased with the increase in mica filler. Storage modulus and loss modulus increased with the increment of glass fiber and mica filler while storage modulus and loss modulus decreased with the increase in glass fiber and mica filler. In addition, in this thesis, dry sliding wear characteristics of polyamide and its composites were investigated using a pin-on-disc wear test machine. Three different polymer composite disc materials are used for wear test. Discs are; 30%wt. glass fiber reinforced polyamide 6 composite, 30%wt. mica filled polyamide 6 composite and 6% wax filled polyamide 6 composite. Wear tests were carried out at the sliding speeds of 0.5 m/s and applied loads of 20N, 30N and 40N and under atmospheric conditions of temperature and humidity. Friction coefficient and specific wear rate values for different combinations of the materials were obtained and compared. For all material combinations, it was observed that, the coefficient of friction increases linearly with the increase in applied load values. Furthermore, their specific wear rate slightly increases with the increase in applied loads and sliding speed values. Moreover, wear surface investigations of all polymer composites used were done by using optical microscope.

Benzer Tezler

  1. Tez No

    398591

    PA 6/ PE / nano-kil kompozitlerin özelliklerinin incelenmesi

    Investigation on the properties of PA 6/PE/nanoclay composites

    ALİM KAŞTAN

    Doktora

    Türkçe

    Türkçe

    2015

    Mühendislik BilimleriAfyon Kocatepe Üniversitesi

    Metal Eğitimi Ana Bilim Dalı

    PROF. DR. YILMAZ YALÇIN

    PROF. DR. HÜSEYİN ÜNAL

  2. Tez No

    516301

    Karbon elyaf, PTFE ve yağ katkılı PA6 polimer kompozitlerinin mekanik ve tribolojik özelliklerinin incelenmesi

    The examination of mechanical and tribological properties of carbon fiber, PTFE and wax filled Pa6 polymer composites materials

    MEHMET TAŞKIRAN

    Yüksek Lisans

    Türkçe

    Türkçe

    2018

    Polimer Bilim ve TeknolojisiDumlupınar Üniversitesi

    İleri Teknolojiler Ana Bilim Dalı

    DR. ÖĞR. ÜYESİ SALİH HAKAN YETGİN

  3. Tez No

    576701

    Karbon elyaf,grafen nanoplatelet ve zincir uzatıcı katkıların poliamit 6,6 kompozitlerin özellikleri üzerine eş zamanlı etkisinin incelenmesi

    Synergetic effect of graphene nanoplatelet,carbon fiber and coupling agent addition on the tribological,mechanical and thermal properties of polyamide 6,6 composites

    ECEM KARATAŞ DEMİRAY

    Yüksek Lisans

    Türkçe

    Türkçe

    2019

    Makine MühendisliğiKocaeli Üniversitesi

    Makine Mühendisliği Ana Bilim Dalı

    PROF. DR. TANER YILMAZ

  4. Tez No

    882248

    Elyaf takviyeli poliketon ve poliketon/poliamid 6 kompozit üretimi

    Fiber reinforced polyketone and polyketone/polyamide 6 composite production

    İREM NEHİR UYSAL

    Doktora

    Türkçe

    Türkçe

    2024

    Polimer Bilim ve TeknolojisiYalova Üniversitesi

    Polimer Malzeme Mühendisliği Ana Bilim Dalı

    PROF. DR. MEHMET ATİLLA TAŞDELEN

  5. Tez No

    285608

    Production and characterization of boron containing flame retardant polyamide-6 and polypropylene composites and fibers

    Bor içeren güç tutuşur polamid-6 ve polipropilen kompozitlerin ve liflerin üretilmesi ve karakterizasyonu

    MEHMET DOĞAN

    Doktora

    İngilizce

    İngilizce

    2011

    Polimer Bilim ve TeknolojisiOrta Doğu Teknik Üniversitesi

    Polimer Bilim ve Teknolojisi Bölümü

    PROF. DR. ERDAL BAYRAMLI

Geri Dön