Korozyon ve yüksek sıcaklık durumunun betonarme çeliklerinin fiziko-mekanik özelliklerine etkisi

The effect of corrosion and high temperature on the physico-mechanical properties of reinforced concrete steels

  1. Tez No: 284508
  2. Yazar: GÖKHAN KÜRKLÜ
  3. Danışmanlar: YRD. DOÇ. DR. ALİ ERGÜN, YRD. DOÇ. DR. M. SERHAT BAŞPINAR
  4. Tez Türü: Doktora
  5. Konular: Teknik Eğitim, İnşaat Mühendisliği, Technical Education, Civil Engineering
  6. Anahtar Kelimeler: Belirtilmemiş.
  7. Yıl: 2011
  8. Dil: Türkçe
  9. Üniversite: Afyon Kocatepe Üniversitesi
  10. Enstitü: Fen Bilimleri Enstitüsü
  11. Ana Bilim Dalı: Metal Eğitimi Ana Bilim Dalı
  12. Bilim Dalı: Belirtilmemiş.
  13. Sayfa Sayısı: 202

Özet

Bu çalışmada betonarme elemanlar üzerinde yüksek sıcaklık ve korozyon durumlarının etkileri incelenmiştir. Bunun için üç farklı basınç dayanımına sahip beton üretilmiştir. Çelik olarak S220a, S420a ve S500a sınıfı betonarme çelikleri kullanılmıştır. Çubuk çapı olarak 12, 16 ve 20 mm seçilmiştir. Korozyonun etkisini belirlemek için üç farklı durum dikkate alınmıştır. Korozyonsuz normal durum, sabit süreli korozyon ve beton çatlağı oluşana kadar korozyon durumlarıdır. Betonarme numuneler üzerinde hızlandırılmış korozyon düzeneği kullanılarak korozyon akımı ve korozyon süresi belirlenmiştir. Ayrıca bu numuneler üzerinde korozyon potansiyeli, korozyon hızı, aderans dayanımı, SEM ve EDS çalışmaları yapılmıştır. Yüksek sıcaklık durumu olarak 100, 200, 400, 600, 800 ve bazı deneyler için 1000 °C sıcaklıklar dikkate alınmıştır. Beton numuneler üzerinde, basınç dayanımı, eğilmede çekme dayanımı testleri gerçekleştirilmiş, ultrases hızı ölçümü, birim hacim ağırlık, porozite, su emme, ağırlık kaybı, dinamik elastisite modülü ve paspayına bağlı ısı geçişi değerleri belirlenmiştir. Çelik numuneler üzerinde ise çekme deneyi, darbe tokluk deneyi gerçekleştirilmiş, tufal kalınlığı ölçümü, mikro sertlik deneyi ve mikro yapı incelemeleri yapılmıştır. Bunun yanında farklı sıcaklık durumlarında aderans dayanımları ölçümleri belirlenmiştir.Deney sonuçlarına göre beton dayanımındaki artışlar, hem normal durumda hem de yüksek sıcaklık ve korozyon durumda aderans dayanımını artırmıştır. Korozyon oluşumu S220a sınıfı düz çubuklarda korozyonsuz duruma göre aderans dayanımını artırırken S420a ve S500a sınıfı nervürlü çubuklarda ise azalma sergilemiştir. Yüksek sıcaklık etkisi altında 100 °C de aderans dayanımlarında bir miktar artış gözlense de tüm seriler sıcaklık artışlarından olumsuz şekilde etkilenmişlerdir. Aynı yüzey geometrisine sahip S420a ve S500a sınıfı çeliklerde korozyon ve yüksek sıcaklık etkileri altında mikro yapı etkili olmuştur.Bu tez çalışmasının sonuçlarına göre normal koşullar altında fiziko-mekanik özellikler açısından S500a önerilirken, korozyon ve yüksek sıcaklık durumlarında dengeli bir değişim sergilediğinden S420a sınıfı çelik önerilmektedir.

Özet (Çeviri)

The main objective of this study was to investigate the reinforced concrete components under high temperature exposure and corrosion condition. For this reason, concrete samples, which have three different compression strength, were produced. S220a, S420a and S500a reinforced concrete steels were used. 12, 16 and 20 mm bar diameter were chosen. Three different corrosion condition; noncorrosive, corrosion with constant period and corrosion until concrete crack formed, were chosen to determine the corrosion effect. Corrosion current and period of reinforced concrete samples were considered with accelerated corrosion mechanism. Furthermore, corrosion potential, corrosion rate, bond strength, SEM and EDX studies were performed on the samples. 100, 200, 400, 600, 800 and 1000 °C temperatures for were selected for high temperature conditions. Compressive, tension strengths under bending, ultrasonic sound velocity, bulk density, porosity, water absorption, loss on ignition, dynamic elasticity modulus and heat transfer measurements depending on the bar cover were carried out. Pull out test, impact toughness, oxide layer measurement, micro hardness and investigation of micro structure were performed on steel samples. In addition, a measuring of bond strength was carried out for all of the temperature conditions.Higher bond strengths were measured with increase in the concrete strength in normal condition and also in high temperature and corrosion conditions. Formation of corrosion products increased the bond strength of S220a class non-ribbed steel as compared to normal condition, on the other hand decrease in the bond strength was measured in S420a and S500a ribbed steels. All of the sample series were affected negatively from increasing of temperature; nevertheless bond strengths of the samples were increased slightly at 100 oC. It was concluded that, the differences in the micro structures of S420a and S500a steels which were the some surface structure, the main reason for the difference in the bond strengths under high temperature and corrosion condition.According to the results of this study, S500a is recommended in terms of physico-mechanical properties under normal conditions. S420a steel is recommended because exhibit balanced exchange in corrosion and high temperature conditions.

Benzer Tezler

  1. Investigation of alternative strategies for optimum reliability in condition assessment of existing RC buildings using NDT methods

    Mevcut binaların NDT yöntemleri kullanılarak durum tespitinde optimum güvenilirlik sağlanması için alternatif yöntemlerin incelenmesi

    HADI ABBASZADEH

    Yüksek Lisans

    İngilizce

    İngilizce

    2018

    Mühendislik Bilimleriİstanbul Teknik Üniversitesi

    İnşaat Mühendisliği Ana Bilim Dalı

    DR. ÖĞR. ÜYESİ OĞUZ GÜNEŞ

  2. Kür koşulları ve yalıtımın yüksek dayanımlı betonların geçirimlilik, iç-yapı ve mekanik özeliklerine etkileri

    Effects of curing conditions and insulation on permeability, microstructure and mechanical properties of high strength concrete

    FATİH ÖZALP

    Doktora

    Türkçe

    Türkçe

    2016

    İnşaat Mühendisliğiİstanbul Teknik Üniversitesi

    İnşaat Mühendisliği Ana Bilim Dalı

    DOÇ. DR. ÖZKAN ŞENGÜL

  3. Sıcaklık etkisine maruz bırakılan güçlendirilmiş betonarme kirişin davranışı

    Behavior of reinforced concrete beam exposed to the effect of temperature

    MELTEM KORKMAZ

    Yüksek Lisans

    Türkçe

    Türkçe

    2022

    İnşaat MühendisliğiRecep Tayyip Erdoğan Üniversitesi

    İnşaat Mühendisliği Ana Bilim Dalı

    DR. ÖĞR. ÜYESİ ALİ GÜRBÜZ

  4. 13 cr mo 4-5 yüksek sıcaklık dirençli çelik kaynaklı bağlantılarının tekrarlı ısıl işlem koşullarında dayanım özelliklerinin değişimi

    Change of 13crmo4-5 creep resistant steels mechanical properties under cyclic post weld heat treatment conditions

    FEVZİ BARBAROS GÜLŞAH

    Yüksek Lisans

    Türkçe

    Türkçe

    2018

    Makine MühendisliğiKocaeli Üniversitesi

    Makine Mühendisliği Ana Bilim Dalı

    DOÇ. DR. EMEL TABAN

  5. Farklı çevre koşullarının tabakalı kompozitlerin statik ve dinamik dayanımlarına etkisi

    The effect of different environmental condition on the static and dynamic strength of laminated composites

    HÜSEYİN ERSEN BALCIOĞLU

    Doktora

    Türkçe

    Türkçe

    2017

    Makine MühendisliğiUşak Üniversitesi

    Makine Mühendisliği Ana Bilim Dalı

    PROF. DR. HALİT GÜN