CCA ile emprenyeli ağaç malzemeden krom, bakır, arseniğin uzaklaştırılmasında perasetik asit ve ozonun kullanılması

Removal of copper, chromium and arsenic from CCA treated wood by using peracetic acid and ozone

  1. Tez No: 309758
  2. Yazar: BÜŞRA AYDOĞAN
  3. Danışmanlar: YRD. DOÇ. DR. ENGİN DERYA GEZER
  4. Tez Türü: Yüksek Lisans
  5. Konular: Ormancılık ve Orman Mühendisliği, Forestry and Forest Engineering
  6. Anahtar Kelimeler: Belirtilmemiş.
  7. Yıl: 2012
  8. Dil: Türkçe
  9. Üniversite: Karadeniz Teknik Üniversitesi
  10. Enstitü: Fen Bilimleri Enstitüsü
  11. Ana Bilim Dalı: Orman Endüstri Mühendisliği Ana Bilim Dalı
  12. Bilim Dalı: Belirtilmemiş.
  13. Sayfa Sayısı: 196

Özet

Bu çalışmada, atıl haldeki CCA ile emprenyeli sarıçam odun örneklerinden ozon ve perasidik asit kullanılarak bakır, krom ve arseniğin odundan uzaklaştırılmasına çalışılmıştır. Çözücü maddenin, odun boyutunun, perasetik asit ve ozon konsantrasyonunun ve perasetik asitte ve ozonda bekletilme sürelerinin, perasetik asitte bekletildikten sonra ozon uygulanmasının odun örneklerinden uzaklaştırılan krom, bakır ve arsenik miktarları üzerine etkileri belirlenmiştir. Örneklerin remidasyon çözeltilerindeki Cr+6 miktarları tespit edilmiştir. Remidasyona maruz kalan örneklerden bazıları termogravimetrik ve SEM/EDX analizlerine tabi tutulmuştur. CCA ile emprenyeli Odun tozları (40mesh) perasetik asidin beş (%1,%10,%25,%50 ve %100) konsantrasyonunda farklı sürelerde bekletildikten sonra 15 veya 30 dk. süreyle ozona tabii tutulmuştur. Perasetik asitte bekletilen örneklere ozon uygulanmasının remidasyon üzerinde önemli ölçüde etkili olmadığı saptanmıştır. Remidasyon etkinliği anlamında örneklerin perasetik asitte bekletildiği konsantrasyon miktarı ve bekletilme süreleri arttıkça olumlu sonuçlar elde edilmiş, arseniğin %99'u, kromun %99'u ve bakırın %98'i odun tozlarından uzaklaştırılmıştır. Perasetik asidin %25'lik konsantrasyonunda 6 saat bekletilip ozon uygulandığında örneklerden arseniğin %98'i, kromun %98'i bakırın %96'sı uzaklaştırılmıştır. 80oC'de remidasyon çözeltisindeki Cr+6 miktarının, oda sıcaklığında elde edilen miktardan fazla olduğu bulunmuş, toplam kromun % 99'u Cr+6 olarak elde edilmiştir.

Özet (Çeviri)

In this study, the removal of copper, chromium and arsenic from chromated copper arsenate (CCA)-treated waste of yellow pine wood samples using ozone and peracetic acid was studied. The effect of solvent, wood size, concentrations of peracetic acid and ozone, and extraction time in peracetic acid and ozone on the amount of chromium, copper and arsenic removed by application of ozone after extracted in peracetic acid was determined. The amount of Cr+6 of the samples in remediation solvents was established. Some of the samples exposed to remediation were used thermogravimetric and SEM/EDX analysis. CCA treated sawdust (40mesh) was applied ozone for 15/30 minutes after having been extracted in five different concentrations (1%, 10%, 25%, 50%, 100%) at different times. It was found out that ozone application to the samples extracted in peracetic acid was not considerably effective on remediation. As for the remediation activity, increase in the amount of concentration extracted in peracetic acid and extraction time yielded positive results, to be specific, 99% of arsenic, 99% of chromium, 98% of copper were removed from sawdust. When applied and extracted with ozone in 25% of peracetic acid for 6h, 98% of arsenic, 90% of chromium, 96% of copper was extracted from the samples. The amount of Cr+6 in remediation solvent at 80oC was much more than that of in room temperature; 99% of chromium was Cr+6.

Benzer Tezler

  1. Servis ömrünü tamamlamış tel direklerinden odun plastik kompozit üretimi

    Production of wood plastic composites from treated utility poles removed from service

    MÜRŞİT TUFAN

    Doktora

    Türkçe

    Türkçe

    2013

    Ağaç İşleriDüzce Üniversitesi

    Orman Endüstri Mühendisliği Ana Bilim Dalı

    DOÇ. DR. CİHAT TAŞÇIOĞLU

  2. CCA ve CCB emprenye maddeleri ile korunan ağaç malzemenin dayanıklılık, yıkanma ve direnç özellikleri

    The Biological Resistance, Leachability and Strength Properties of Wood Treated with CCA and CCB Preservatives

    SAİP NAMİ KARTAL

    Doktora

    Türkçe

    Türkçe

    1998

    Ormancılık ve Orman Mühendisliğiİstanbul Üniversitesi

    Orman Endüstri Mühendisliği Ana Bilim Dalı

    PROF. DR. RAMAZAN KANTAY

  3. Benzetilmiş dış ortam koşullarının emprenyeli ağaç malzemeye etkileri

    The effect of simulated weathering on preservative treated wood

    ALİ TEMİZ

    Doktora

    Türkçe

    Türkçe

    2005

    Ormancılık ve Orman MühendisliğiKaradeniz Teknik Üniversitesi

    Orman Endüstri Mühendisliği Ana Bilim Dalı

    PROF. DR. ÜMİT CAFER YILMAZ

  4. Farklı ağaç malzemelerden üretilen emprenyeli lamine ağaç malzemelerin ısı iletkenliklerinin belirlenmesi

    Determine of thermal conductivity coefficient of produced from different wood materials impregnated laminated veneer lumbers (LVL)

    CEMAL ÖZCAN

    Yüksek Lisans

    Türkçe

    Türkçe

    2007

    Ağaç İşleriZonguldak Karaelmas Üniversitesi

    Mobilya ve Dekorasyon Eğitimi Ana Bilim Dalı

    PROF. DR. BURHANETTİN UYSAL

  5. Açık hava koşullarının ahşap malzemenin özelliklerine etkisi

    The effect of open air conditions on the properties of wooden material

    MUSTAFA ORDU

    Yüksek Lisans

    Türkçe

    Türkçe

    2007

    Ağaç İşleriDumlupınar Üniversitesi

    Mobilya ve Dekorasyon Eğitimi Ana Bilim Dalı

    YRD. DOÇ. DR. MURAT ÖZALP