Kriyojenik işlemin vermiküler grafitli dökme demirin aşınma davranışına etkisi
Effect of cryogenic treatment on wear behavior of compacted graphite cast iron
- Tez No: 382607
- Danışmanlar: DOÇ. DR. HAKAN GAŞAN
- Tez Türü: Yüksek Lisans
- Konular: Metalurji Mühendisliği, Metallurgical Engineering
- Anahtar Kelimeler: Belirtilmemiş.
- Yıl: 2015
- Dil: Türkçe
- Üniversite: Eskişehir Osmangazi Üniversitesi
- Enstitü: Fen Bilimleri Enstitüsü
- Ana Bilim Dalı: Metalurji Mühendisliği Ana Bilim Dalı
- Bilim Dalı: Belirtilmemiş.
- Sayfa Sayısı: 94
Özet
Bu çalışmada, otomobillerde debriyaj baskı plakası parçası olarak kullanılan vermiküler grafitli dökme demire (CGI 300) 4, 12, 24 ve 36 saat sürelerle kriyojenik işlem uygulanmıştır. Kriyojenik işlem sonrası malzemelerin mikroyapısal incelemeleri yapılmış, makro ve mikro sertlikleri ölçülmüş, aşınma deneyleri gerçekleştirilerek işlem görmemiş malzeme ile karşılaştırılmıştır. Kriyojenik işlem, dakikada 2 °C soğutma hızıyla -196 °C‟ye soğutularak belirlenen sürelerde bu sıcaklıkta tutularak gerçekleştirilmiştir. -196 °C‟den oda sıcaklığına yine dakikada 2 °C ısıtma hızı ile ulaşılmıştır. Mikroyapıda meydana gelen değişikliklerin ve aşınma yüzeylerinin incelenmesinde optik mikroskop ve SEM teknikleri kullanılmıştır. Makrosertlik ve mikrosertliklerde meydana gelen değişikliklerin belirlenmesinde Rockwell B ve Vikers sertlik birimi kullanılmıştır. Aşınma deneyleri ball-on-disc metodu ile her kriyojenik işleme tabi tutulan ve işlem görmemiş numuneler için 5 N ve 10 N yüklerle, 2,5 mm yarıçapta, 100 metre aşınma mesafesi, 10 cm/s hızla kurukoşullarda gerçekleştirilmiştir. Kriyojenik işleme tabi tutulmuş ve işlem görmemiş numunelerin özgül aşınma oranları hesaplanmış ve karşılaştırmalar yapılmıştır. Karşılaştırma sonucu kriyojenik işlem uygulanmış numunelerin tümünün aşınma oranlarında işlem uygulanmamış numuneye göre iyileşme olduğu görülmüştür. 5 N yük uygulanan aşınma deneyinde, 12 saat kriyojenik işlem uygulanan numunenin aşınma direncinde %68,7 oranında artış meydana gelirken, 10 N uygulanan aşınma deneyinde 24 saat kriyojenik işlem uygulanan numunenin aşınma direncinde %69,5 oranında artış olmuştur.
Özet (Çeviri)
In this study, cryogenic treatment is applied at 4, 12, 24 and 36 hours to compacted graphite cast iron which is used for clutch pressure plate in automobile. After cryogenic treatment, microstructural investigations, macro and micro hardness test and wear tests were carried out. Cryogenic treatment is applied which the cooling rate of 2 °C per minute to -196 °C and had stood at this temperature at specified times. It was reached at room temperature again with heating rate of 2 °C per minute. Optical microscope and SEM techniques were used to examine the changes in the microstructure and worn surface. Rocwell B and Vickers were drawn on in determining the macrohardness and microhardness changes. Wear tests were carried out dry conditions by using ball-on-disc method for each times of cryogenic treated and untreated samples with 5 N and 10 N normal loads, 2,5 mm radius, 100 meters sliding distance and 10 cm/s sliding velocity. Specific wear rates of cryogenic treated and untreated samples compared each other. Result of the comparisons, both wear rates of cryogenic treated samples decrease according to untreated samples. Test with 5 N normal load, wear resistance of the sample which cryogenic treated at 12 hours was improved %68,7; Test with 10 N normal load, wear resistance of the sample which cryogenic treated at 24 hours was improved %69,5.
Benzer Tezler
- Kriyojenik işlemin AISI D3 soğuk iş takım çeliğinin performansına etkilerinin incelenmesi
Determining the effects cryogenic treatment on the performance of AISI D3 cold work steel
YUSUF ARSLAN
- Kriyojenik işlemin sarıçam odunu mekanik özellikleri üzerindeki etkisi
Effect of cryogenic threatment on mechanical properties of scotch pine
ERSİN PAMUKCU
Yüksek Lisans
Türkçe
2019
Ağaç İşleriDüzce ÜniversitesiAğaç İşleri Endüstri Mühendisliği Ana Bilim Dalı
DR. ÖĞR. ÜYESİ HASAN HÜSEYİN CİRİTCİOĞLU
- Kriyojenik işlemin AISI 431 paslanmaz çeliğinin mekanik özellikleri üzerine etkilerinin araştırılması
Investigation of the effects of cryogenic treatment on the mechanical properties of AISI 431 stainless steel
EMRE YILDIZ
Yüksek Lisans
Türkçe
2022
Mühendislik BilimleriDüzce Üniversitesiİmalat Mühendisliği Ana Bilim Dalı
DR. ÖĞR. ÜYESİ NURSEL ALTAN ÖZBEK
- Kriyojenik işlemin, lazer kaynaklı otomotiv sacı birleştirilmelerinin mekanik ve mikroyapı özelliklerine etkisi
Effect of cryogenic treatment on mechanical and microstructural properties of laser welded automotive sheet joints
YUSUF ÖZDEMİR
Yüksek Lisans
Türkçe
2023
Makine MühendisliğiKarabük ÜniversitesiMakine Mühendisliği Ana Bilim Dalı
PROF. DR. BİLGE DEMİR
- Kriyojenik işlemin AM355 paslanmaz çeliğinin aşınma özelliklerine etkilerinin incelenmesi
Investigation on effect of cryogenic treatment on wear properties of AM355 stainless steel
ANIL UZER
Yüksek Lisans
Türkçe
2022
Metalurji MühendisliğiEskişehir Osmangazi ÜniversitesiMetalurji ve Malzeme Mühendisliği Ana Bilim Dalı
PROF. DR. HAKAN GAŞAN