Hidroksiapatit/jelatin hidrojelleriyle atık sulardan kurşun (II)'nin gideriminin araştırılması

Investigation of lead (II) removal from waste waters by hydroxyapatite/gelatin hydrogels

  1. Tez No: 425930
  2. Yazar: FEYZA ÜNEL
  3. Danışmanlar: PROF. DR. HALİL KUMBUR
  4. Tez Türü: Yüksek Lisans
  5. Konular: Çevre Mühendisliği, Environmental Engineering
  6. Anahtar Kelimeler: Adsorpsiyon, Atık Su, Kurşun, Hidroksiapatit/Jelatin Kompozit Hidrojelleri, Adsorption, Waste Water, Lead, Hydroxyapatite/Gelatin Composite Hydrogels
  7. Yıl: 2014
  8. Dil: Türkçe
  9. Üniversite: Mersin Üniversitesi
  10. Enstitü: Fen Bilimleri Enstitüsü
  11. Ana Bilim Dalı: Çevre Mühendisliği Ana Bilim Dalı
  12. Bilim Dalı: Belirtilmemiş.
  13. Sayfa Sayısı: 116

Özet

Kurşun; akü imalatı, kablo izolasyonu, radyasyon yalıtımları, benzin katkı maddesi gibi birçok alanda kullanılan oldukça toksik bir ağır metaldir. Hava, su ve toprak yoluyla çevreye yayılan kurşun bileşiklerinin gideriminde iyon değişimi, çöktürme, elektrokimyasal yöntemler ve adsorpsiyon gibi birçok metot uygulanmaktadır. Bu çalışmada adsorpsiyon yöntemi kullanılarak hidroksiapatit/jelatin (HAp/Jel) kompozit hidrojelleri ile kurşun içeren sentetik atık su numunelerinden kurşun (II) giderimi üzerine çalışılmıştır. Gluteraldehitin çapraz bağlayıcı olarak kullanıldığı 1:1, 1:4, 1:9, 0:10 (m/m) oranlarında hidroksiapatit/jelatin kompozit hidrojelleri hazırlanmış ve karakterizasyon çalışmaları yapılmıştır. Elde edilen kompozit hidrojellerin; FTIR spektroskopisi ile bileşimindeki fonksiyonel grupları, BET analizi ile yüzey alanları, SEM analizi ile yüzey mikroyapıları tayin edilmiştir. Yüzey alanı en büyük olan kompozit hidrojeller ile adsorpsiyon çalışmaları yürütülmüştür. Adsorpsiyon çalışmaları sonucunda maksimum kurşun (II) giderimi 80 mg/g olarak bulunmuştur. HAp/Jel kompozit hidrojelleri ile Pb2+ gideriminin gerçekleştirildiği, yapılan SEM-EDS analizi ile doğrulanmıştır. İzoterm çalışmalarının sonucuna göre adsorpsiyon prosesi Langmuir izotermine uyum sağlamaktadır. Termodinamik parametreler (∆G, ∆H and ∆S) kurşun (II)'nin HAp/Jel kompozit hidrojellerine adsorpsiyonunun 25-55 oC'de spontane ve endotermik olduğunu göstermektedir. Yapılan çalışmalar sonucunda atık sulardan kurşun (II) gideriminde kullanılabilecek yeni bir adsorbent olan HAp/Jel kompozit hidrojelleri elde edilmiş ve bu alanda daha önce yapılan çalışmalara katkı sağlayacağı düşünülmüştür.

Özet (Çeviri)

Lead is a highly toxic heavy metal which is used in many fields as battery manufacturing, cable isolation, insulation of radiation, gasoline additive etc. There are several methods like ion exchange, precipitation, electrochemical methods and adsorption for removal of lead compounds emitted environment via air, water and soil. In this study, adsorption method was used. Removal of lead (II) by hydroxyapatite/gelatin (HAp/Gel) composite hydrogels from synthetic waste water samples that contains lead ions were studied. HAp/Gel composite hydrogels in which glutaraldehyde is used as crosslinker were prepared in 1:1, 1:4, 1:9, 0:10 (w/w) proportions and characterization studies were performed. Functional groups of composite hydrogels were characterized by using Fourier Transform Infrared Spectroscopy, surface areas were characterized by using BET analysis, the surface microstructures of composite hydrogels were analyzed by Scanning Electron Microscope. Adsorption studies were performed with the composite hydrogel which has the largest surface area. At the end of adsorption studies maximum removal of lead (II) was determined 80 mg/g. The removal of lead (II) by HAp/Gel composite hydrogels was confirmed by SEM-EDS analysis. According to the results of isotherm studies adsorpstion process is well described by Langmuir isotherm. The thermodynamic parameters (∆G, ∆H and ∆S) indicated that the adsorption of lead (II) on HAp/Gel composite hydrogels were spontaneous and endothermic at 25-55oC. As a result of this study, HAp/Gel composite hydrogels were obtained as a new adsorbent which can be used for the removal of lead (II) ions from waste waters and it is thought to contribute to the studies which have been made in this field before.

Benzer Tezler

  1. Fenolik bağlayıcı kullanılarak sentezlenen hidroksiapatit-jelatin kompozit malzemesinin karakterizasyonu ve ilaç salım profilinin incelenmesi

    Research on characterization and drug release performance of hydroxyapatite-gelatin composite materials syntheted by using phenolic linker

    IRMAK BAŞER GÜMÜŞ

    Yüksek Lisans

    Türkçe

    Türkçe

    2018

    Kimya Mühendisliğiİstanbul Teknik Üniversitesi

    Kimya Mühendisliği Ana Bilim Dalı

    PROF. DR. GÜLHAYAT SAYGILI

  2. SBF ortamında üretilen hidroksiapatit-jelatin kompozit malzemelerin ilaç salım performansının incelenmesi

    Research on drug release performance of hydroxyapatite-gelatin composites produced in SBF medium

    EBRU KAHRAMAN

    Yüksek Lisans

    Türkçe

    Türkçe

    2016

    Kimya Mühendisliğiİstanbul Teknik Üniversitesi

    Kimya Mühendisliği Ana Bilim Dalı

    PROF. DR. GÜLHAYAT NASÜN SAYGILI

  3. Tavşan tibialarında oluşturulan segmenter kemik defektlerinin vasküler endotelyal büyüme faktörü (VEGF) yüklenmiş hidroksiapatit/jelatin matriks ile tedavisi

    Treatment of segmentary bone defects in rabbit tibiae with vascular endothelial growth factor (VEGF)) enhanced hydroxyapatite/gelatin matrix

    BURAK YAĞMUR ÖZTÜRK

    Tıpta Uzmanlık

    Türkçe

    Türkçe

    2010

    Ortopedi ve TravmatolojiGazi Üniversitesi

    Ortopedi ve Travmatoloji Ana Bilim Dalı

    PROF. DR. HALUK YETKİN

  4. Preparation and characterization of chitosan-gelatin/hydroxyapatite scaffolds for hard tissue engineering approaches

    Kitosan-jelatin/hidroksiapatit destek yapıların sert doku mühendisliği yaklaşımları için hazırlanması ve karakterizasyonu

    CANSEL IŞIKLI

    Yüksek Lisans

    İngilizce

    İngilizce

    2010

    BiyomühendislikOrta Doğu Teknik Üniversitesi

    Biyomedikal Mühendisliği Ana Bilim Dalı

    PROF. DR. NESRİN HASIRCI

    PROF. DR. VASIF HASIRCI

  5. Kalvaryal defektlerin onarımında jelatin/hidroksiapatit esaslı kriyojel doku iskelelerinin etkisi

    Effect of gelatin/hydroxyapatite based cryogel scaffolds for calvarial defect repair

    İLYAS İNCİ

    Doktora

    Türkçe

    Türkçe

    2012

    BiyomühendislikHacettepe Üniversitesi

    Biyomühendislik Ana Bilim Dalı

    DOÇ. DR. İBRAHİM VARGEL

    PROF. DR. ERHAN BİŞKİN