Ultrasonik karıştırmanın ZnO toz özelliklerine etkisi

The Effect of ultrasonic stirring on properties of ZnO powder

  1. Tez No: 106260
  2. Yazar: TUBA KARAHAN
  3. Danışmanlar: PROF. DR. MÜZEYYEN MARŞOĞLU
  4. Tez Türü: Yüksek Lisans
  5. Konular: Metalurji Mühendisliği, Metallurgical Engineering
  6. Anahtar Kelimeler: Ultrasonik karıştırma, çinko okzalat dihidrat, çinko oksit vı, Ultrasonic stirring, zinc oxalate hydrate, zinc oxide Vll
  7. Yıl: 2001
  8. Dil: Türkçe
  9. Üniversite: Yıldız Teknik Üniversitesi
  10. Enstitü: Fen Bilimleri Enstitüsü
  11. Ana Bilim Dalı: Metalurji Mühendisliği Ana Bilim Dalı
  12. Bilim Dalı: Belirtilmemiş.
  13. Sayfa Sayısı: 87

Özet

ÖZET Çinko (Zn), boya endüstrisinden eczacılığa, lastik üretiminden malzemelerin koruyucu kaplamalarına kadar, oldukça geniş kullanım alanına sahip bir malzemedir. Genel olarak, çinko buharının yanmasıyla elde edilen çinko oksit (ZnO), çinko bileşiklerinin en önemlilerindendir. Çinko oksit en çok lastik endüstrisinde, onu takiben de önem sırasına göre boya, seramik, elektronik endüstrileri, tekstil, ilaç, yer döşemeleri, koruyucu ve dekoratif kaplamalarda kullanılır. Metal oksitleri içinde, kullanım alanı bol olmasına rağmen, çevreye ve insan sağlığına negatif etkisi çok az olan ZnO, Fransız Prosesi, Amerikan Prosesi ve Islak proses olarak bilinen 3 ana tip prosesle üretilir. Ultrasonik dalgalar güneşin yüzeyindeki sıcaklıklar kadar yüksek sıcaklıklar ve okyanusun en dibindeki basınç kadar yüksek basınçlar üretebilir. Bazı durumlarda, ultrason aynı zamanda yüksek enerjili kimyasal reaksiyonlara da sebep olabilir. Bu olaylar akustik kavitasyon; kabarcıkların oluşumu, büyümesi. ve içe doğru patlayarak bozunuma uğraması, sayesinde oluşur. Bu araştırmada 0,5 molar çinko nitrat çözeltisi içine 0,5 molar okzalik asit çözeltisi katılıp karıştırılarak çinko okzalat dihidrat çöktürülmüştür. Daha sonra çinko okzalat dihidrat 400°C'de kalsine edilerek ZnO elde edilmiştir. Bu işlemde ultrasonik karıştırma ve mekanik karıştırma ayrı ayrı kullanılarak elde edilen çinko okzalat dihidratların ve kalsinasyon sonucu elde edilen ZnO tozlarının özellikleri (termal bozunma, X-ışını kırınımları, FTIR analizleri, morfolojileri) karşılaştırmalı olarak incelenmiştir. Oluşan farklılıkların nedenleri üretim koşullarına bağlı olarak irdelenmiştir.

Özet (Çeviri)

ABSTRACT Zinc (Zn), has a wide range of application, it is used in paint industry, pharmaceuticals, producing rubber and protective coatings. Generally, the most important compound of zinc, zinc oxide is produced by burning zinc vapour. The rubber industry is the chief consumer of zinc oxide, followed by the paint, ceramic, electronic, textile industries, pharmaceuticals, floor coverings, protective and decorative coatings. Despite its wide market, ZnO is the one of the least harmful compounds on human health and environment, among all metal oxides. ZnO can be produced by using three main prosesses which are; French Prosess, American Prosess and Wet Prosess. Ultrasound can produce temperatures as high as those on the surface of the Sun and pressures as great as those at the bottom of the ocean. In some cases, ultrasound can also cause high-energy chemistry. It does so through the process of acoustic cavitation: the formation, growth and implosive collapse of bubbles in a liquid. In this study, 0,5 molar zinc nitrate solution is mixed with 0,5 molar oxalic acid solution and zinc oxalate hydrate is precipitated. Then zinc oxalate hydrate is calcinated and ZnO is produced. Characterisation of zinc oxalate produced by both ultrasonic and mechanic stirring operations and then calcinated zinc oxide were made by using thermal decomposition, X-ray diffraction, FTIR analysis and morphology to asses and analyse the differences caused by different mixing operations.

Benzer Tezler

  1. Tez No

    251477

    Çinko borat üretimi

    Production of zinc borate

    SİBEL YÜCE

    Yüksek Lisans

    Türkçe

    Türkçe

    2009

    Kimya Mühendisliğiİstanbul Teknik Üniversitesi

    Kimya Mühendisliği Ana Bilim Dalı

    DOÇ. DR. HALE GÜRBÜZ

  2. Tez No

    453394

    Ni-b/hBN kompozit kaplamaların elektrodepolama yoluyla üretilmesi ve özelliklerinin incelenmesi

    Production of ni-b/hBN composite coatings by electrodeposition and investigation of its properties

    ERSİN ÜNAL

    Yüksek Lisans

    Türkçe

    Türkçe

    2016

    Makine Mühendisliğiİskenderun Teknik Üniversitesi

    İleri Metalurji ve Malzeme Teknolojileri Mühendisliği Ana Bilim Dalı

    PROF. DR. İSMAİL HAKKİ KARAHAN

  3. Tez No

    457886

    Atış artıklarında iyon belirleme çalışması

    Ion detection work in shot residue

    ÖZGE ÖZEN EROL

    Yüksek Lisans

    Türkçe

    Türkçe

    2017

    Adli TıpOndokuz Mayıs Üniversitesi

    Kimya Ana Bilim Dalı

    PROF. DR. ATİYE NUR ONAR

  4. Tez No

    364220

    Kalsiyum karbonat kristallerinin kontrollü sentezi

    Controlled synthesis of calcium carbonate crystals

    DUYGU GÜRBÜZ

    Yüksek Lisans

    Türkçe

    Türkçe

    2014

    Kimya MühendisliğiYıldız Teknik Üniversitesi

    Kimya Mühendisliği Ana Bilim Dalı

    PROF. DR. MUALLA ÖNER

    UZMAN SEMRA KIRBOĞA OKUMUŞ

  5. Tez No

    305093

    Experimental investigation of agitation hydrodynamics and mixing-time of non-Newtonian solutions

    Newtonumsu olmayan akışkanların karıştırma hidrodinamiğinin ve karışım zamanının deneysel olarak incelenmesi

    BEGÜM ŞEN

    Yüksek Lisans

    İngilizce

    İngilizce

    2011

    Kimya MühendisliğiOrta Doğu Teknik Üniversitesi

    Kimya Mühendisliği Bölümü

    DOÇ. DR. YUSUF ULUDAĞ

Geri Dön