Thermal loading effects on CFRP composites

Termal yüklemenin karbon elyaf ile güçlendirilmiş kompozit malzemelere etkileri

  1. Tez No: 116548
  2. Yazar: BESİM GÖKÇE DARA
  3. Danışmanlar: PROF.DR. ALPAY ANKARA
  4. Tez Türü: Doktora
  5. Konular: Metalurji Mühendisliği, Metallurgical Engineering
  6. Anahtar Kelimeler: Polymer matrix composite, thermal loading, moisture absorption, service life IV
  7. Yıl: 2001
  8. Dil: İngilizce
  9. Üniversite: Orta Doğu Teknik Üniversitesi
  10. Enstitü: Fen Bilimleri Enstitüsü
  11. Ana Bilim Dalı: Belirtilmemiş.
  12. Bilim Dalı: Belirtilmemiş.
  13. Sayfa Sayısı: 116

Özet

öz TERMAL YÜKLEMENİN KARBON ELYAF İLE GÜÇLENDİRİLMİŞ KOMPOZİT MALZEMELERE ETKİLERİ DARA, Besim Gökçe Doktora, Metalürji ve Malzeme Mühendisliği Bölümü Tez Yöneticisi : Prof. Dr. Alpay ANKARA Ocak 2001, 116 sayfa Bu tez havacılık ve uzay sanayiinde kullanılan sürekli elyaf ile güçlendirilmiş epoksi matrisli kompozit malzemeler üzerinde termal yüklemelerin etkilerini araştırmaktadır. Termal yüklemelerin malzemenin nem soğurma davranımına olan etkileri de araştırılmıştır. Neme doyurulmuş numuneler 200 ile 350C aralığında sıcaklıklara 5 ile 30 dakika zaman aralığında maruz bırakıldıktan sonra basma ve katlar arası kayma direnci testleri; yapıştırıcılı bağlantılı numunelere ise tek taraflı kesme direnci testleri gerçekleştirilmiştir. Termal yükleme sonrası malzemenin matris etken özelliklerinde ve nem soğurma özelliklerinde büyük değişiklikler gözlemlenmiştir. Termal yükleme sonrası oluşan yaygın katlar arası ayrılma bu davranım değişikliklerinin ana nedeni olarak belirlenmiştir. Termal yükleme sonrası malzemenin nem soğurma davranımının tahminine yönelik yan ampirik bir yöntem önerilmektedir. Bunun yanında ısı etkisi ile kimyasalbozunmaya uğrayan, neme doymuş, polimer matrisli bir kompozit malzeme için enerji dengesine dayalı sıcaklık dağılımı hesap yöntemi de çalışmada yer almaktadır. Çalışmanın en belirgin çıkarımı havacılık endüstrisinde kullanılan karbon elyaf ile güçlendirilmiş polimer matrisli kompozit malzemelerin servis ömrünü belirlemede çok önem taşıyacak termal yüklemeye bağlı olarak malzemenin nem soğurma davranımındaki değişikliğin belirlenmesidir. Anahtar kelimeler : Polimer matrisli kompozit, termal yükleme, nem soğurma vı

Özet (Çeviri)

ABSTRACT THERMAL LOADING EFFECTS ON CFRP COMPOSITES DARA, Besim Gökçe Ph.D. Department of Metallurgical and Materials Engineering Supervisor: Prof. Dr. Alpay ANKARA January 2001, 116 pages This thesis investigates the effects of thermal loading on epoxy matrix continuous fiber reinforced laminated composites used in aerospace industry. The effect of thermal loading to moisture absorption behavior of the material was also investigated. Moisture saturated specimens exposed to temperatures in the range of 200 to 350°C for exposure times of 5 to 30 minutes were tested for compression, interlaminar shear strength and adhesively bonded specimens for single lap shear strength. The matrix dominated mechanical properties and moisture absorption behavior of the material were found to change extensively after thermal loading. Excessive delamination after thermal loading was identified as the main cause for this behavior change. A semi-empirical model for the estimation of the moisture take up behavior after thermal loading is proposed together with a thermal energy balance calculation for the chemically decomposing, moisture saturated polymer matrix composite. The theoretical calculations supported by experimental results affirm the behaviour change due to thermal loading. The most prominent outcome of the investigation is iiithe change in moisture absorption behaviour due to thermal loading which is especially decisive in service life determination of CFRP components and structures utilised in aerospace industry.

Benzer Tezler

  1. Damage progression in composite materials: An experimental and numerical study

    Kompozit malzemelerde hasar ilerlemesi: Deneysel ve sayısal çalışma

    HAFIZ QASIM ALI

    Doktora

    İngilizce

    İngilizce

    2023

    Makine MühendisliğiSabancı Üniversitesi

    Malzeme Bilimi ve Nanomühendislik Ana Bilim Dalı

    PROF. DR. MEHMET YILDIZ

  2. Investigation of CNT smart paint for structural health monitoring in advanced and nano-enhanced carbon fiber composites

    Gelişmiş ve nano takviyeli kompozit malzemeler için karbon nanotüp içerikli akıllı boyanın yapısal sağlık izleme için geliştirilmesi

    YAĞMUR ATEŞCAN

    Yüksek Lisans

    İngilizce

    İngilizce

    2015

    Uçak Mühendisliğiİstanbul Teknik Üniversitesi

    Uçak ve Uzay Mühendisliği Ana Bilim Dalı

    YRD. DOÇ. HÜLYA CEBECİ

  3. Behavior of cfrp confined concrete specimens under temperature cycles and sustained loads

    Karbon lifli polimer ile güçlendirilmiş beton numunelerin ısı çevrimleri ve kalıcı yükler altında davranışı

    BARIŞ ERDİL

    Doktora

    İngilizce

    İngilizce

    2012

    İnşaat MühendisliğiOrta Doğu Teknik Üniversitesi

    İnşaat Mühendisliği Bölümü

    DOÇ. DR. İSMAİL ÖZGÜR YAMAN

    PROF. DR. UĞURHAN AKYÜZ

  4. Kompozit 3U küp uyduların yapısal analiz ve tasarımları

    Structural analysis and design of composite 3U cubesats

    EGEMEN MENTEŞ

    Yüksek Lisans

    Türkçe

    Türkçe

    2015

    Astronomi ve Uzay Bilimleriİstanbul Teknik Üniversitesi

    Uçak ve Uzay Mühendisliği Ana Bilim Dalı

    PROF. DR. ZAHİT MECİTOĞLU