Farklı yapı ve özelliklere sahip termoplastiklerin kırılma davranışlarında numune boyutu ve deney hızına bağlı değişimlerin incelenmesi
The Investigation of changes depending on specimen size and test speed in the fracture behaviour of thermoplastics which have different structure and properties
- Tez No: 126531
- Danışmanlar: YRD. DOÇ. DR. HALİL DEMİRER
- Tez Türü: Doktora
- Konular: Metalurji Mühendisliği, Metallurgical Engineering
- Anahtar Kelimeler: Hız, Kırılma, Kırılma mekaniği, Plastik malzemeler, Termoplastik, Speed, Fracture, Fracture mechanics, Plastic materials, Thermoplastic
- Yıl: 2002
- Dil: Türkçe
- Üniversite: Marmara Üniversitesi
- Enstitü: Fen Bilimleri Enstitüsü
- Ana Bilim Dalı: Metal Eğitimi Ana Bilim Dalı
- Bilim Dalı: Belirtilmemiş.
- Sayfa Sayısı: Belirtilmemiş.
Özet
ÖZET FARKLI YAPI VE ÖZELLİKLERE SAHİP TERMOPLASTİKLERİN KIRILMA DAVRANIŞLARINDA NUMUNE BOYUTU VE DENEY HIZINA BAĞLI DEĞİŞİMLERİN İNCELENMESİ Kırılma, mekanik bileşenlerin karşılaştığı hasar modlarının başında gelmektedir. Kırılma konusunda en önemli kavram malzemelerin kırılma tokluğudur. Kırılma tokluğunun ölçümü için basit darbe ve ağırlık düşürme testleri gibi bir çok standart test uygulanmaktadır. Çatlak hattından yüklenmiş numuneler veya çift konsollu kiriş şeklindeki numunelerle kırılma tokluğu ölçümü ilk olarak yapıştırmalı bağlantılarda gerçekleştirilmiştir. Daha sonra bazı metal alaşımları üzerinde test edilen bu yöntem polimetilmetakrilat ve polistiren gibi gevrek polimerlere de uygulanarak olumlu sonuçlar alınmıştır. Bu çalışmada esas olarak çift konsollu kiriş şeklindeki numunelerin yüksek ve orta yoğunluklu polietilen ve polipropilen gibi üç farklı polimer için uygulanabilirliğinin incelenmesi hedeflenmiştir. Başlangıçtaki denemelerde numunenin literatürde verilen geometrik şekli ile bunun mümkün olmadığı görüldü ve çözüm için yapılan uzun denemelerden sonra orijinal numune geometrisi üzerinde yapılan modifikasyonlar sonunda bu malzemeler için test edilebilir yeni bir numune geometrisine ulaşıldı. Levha halindeki üç cins polimer için bu yeni geometri esas alınarak üzerinde kırılmaya kılavuzluk edecek kanallar bulunan farklı boyut ve kalınlıkta numuneler hazırlandı. Üzerlerinde değişik uzunlukta çentik açılmış olan bu numuneler farklı hızlarda MOD-I testine tabi tutuldu. Kırılmadaki maksimum yükte oluşan çatlak açılma yer değiştirmesi ölçülerek kompliyans değerleri belirlendi. Elde edilen veriler numune kompliyansının çatlak uzunluğu ile değişimini gösterecek şekilde grafikler halinde sunuldu. Sonuçların deneylerde kullanılan polimerlerin mekanik özellikleri İle uyumlu olması ulaşılan numune geometrisinin bu malzemeler için uygulanabilir olduğunu göstermiştir. Eylül 2002 Kenan BÜYÜKKAYA V
Özet (Çeviri)
ABSTRACT THE INVESTIGATION OF CHANGES DEPENDING ON SPECIMEN SIZE AND TEST SPEED IN THE FRACTURE BEHAVIOUR OF THERMOPLASTICS WHICH HAVE DIFFERENT STRUCTURE AND PROPERTIES Fracture is the main failure mode of mechanical components. Fracture toughness of materials is the most important concept in the fracture subject. Several standard test methods such as simple impact and falling weight tests are utilised for the measurement of fracture toughness. The measurement of this property with crack-line loaded or double cantilever beam specimens were first applied on adhesively bonded joints. Later this method was tested on some metal alloys. It was also applied on brittle polymers such as polymethylmetacrylate and polystyrene and positive results obtained. The main aim of this study is to investigate the applicability of the double cantilever beam specimens for three different polymers namely high and medium density polyethylene and polypropylene. In the earlier trials it was found that it was impossible to test this specimen with the geometry which was given in the literature. After long trials; modifications were made on the original specimen geometry for the solution and finally a new geometry, applicable for these materials, was obtained. By considering the new geometry for the three types of sheet polymers, different size and thickness specimens with guide grooves were prepared. These specimens which have various length notches on them were subjected to MOD-I testing under different test speeds. Compliance values were determined by measuring the crack opening displacement which corresponds to maximum load. The obtained data were presented in the form of graphs which show the change of specimen's compliance with crack lenght. The conformity of results to the mechanical properties of specimen materials showed the applicability of present specimen geometry for these materials. September 2002 Kenan BÜYÜKKAYA VI
Benzer Tezler
- Bazı esterlerin kinetik incelenmesi ve termodinamik parametrelerin belirlenmesi
Kinetic study and detesmination of thermodnamic parameters of some esters
İBRAHİM TAŞ
Yüksek Lisans
Türkçe
1986
Kimya MühendisliğiUludağ ÜniversitesiKimya Ana Bilim Dalı
PROF. DR. MUSTAFA CEBE
- İzmir'de bazı yolların kapatılarak yaya bölgeleri oluşturma da kent peyzajını geliştirme açısından yeniden planlanması üzerinde araştırmalar
Başlık çevirisi yok
BAHAR TÜRKYILMAZ
Yüksek Lisans
Türkçe
1985
Şehircilik ve Bölge PlanlamaEge ÜniversitesiŞehir ve Bölge Planlama Ana Bilim Dalı
- Testosteron dihidrotestosteron ve östrojenin benign prostat hiperplazisindeki etyolojik rolleri
The roles of testosterone, dihydrotestosterone and estradiole on the etiology of benign prostatic hyperplasia
HALUK TOKUÇOĞLU
- Süt formüllerinin tüketim uygulamaları ve süt formüllerinin C vitamini içeriği ile pH değerleri
Başlık çevirisi yok
GÖNÜL VAROL
Yüksek Lisans
Türkçe
1986
Besin Hijyeni ve Teknolojisiİstanbul ÜniversitesiÇocuk Gelişimi Ana Bilim Dalı
DOÇ. DR. TÜRKAN KUTLUAY
- Türkiye'de aile planlaması çalışmalarında erkeklerin önemi, hastane personeli ile fabrika işçilerinin doğum kontrol yöntemlerine karşı tutum ve davranranışlarında farklılığın araştırılması
Başlık çevirisi yok
KAMİL MALKOÇLU
Yüksek Lisans
Türkçe
1987
Demografiİstanbul ÜniversitesiAile Sağlığı Ana Bilim Dalı
DOÇ. DR. DERİN KÖSEBAY