Cu ve Co katkılanmış MgB2 süperiletkenlerinin incelenmesi

Investigation of Cu and Co-doped MgB2 superconductors

  1. Tez No: 197064
  2. Yazar: İSMAİL DEMİREL
  3. Danışmanlar: DOÇ.DR. AYHAN GÜLDESTE
  4. Tez Türü: Yüksek Lisans
  5. Konular: Fizik ve Fizik Mühendisliği, Physics and Physics Engineering
  6. Anahtar Kelimeler: MgB2 süperiletkenler, termoelektrik güç, termal iletkenlik, katıhalreaksiyon yöntemi, MgB2 superconductors, thermoelectric power, thermal conductivity, solid-state reaction method
  7. Yıl: 2006
  8. Dil: Türkçe
  9. Üniversite: Erciyes Üniversitesi
  10. Enstitü: Fen Bilimleri Enstitüsü
  11. Ana Bilim Dalı: Fizik Ana Bilim Dalı
  12. Bilim Dalı: Belirtilmemiş.
  13. Sayfa Sayısı: 105

Özet

iiiCu VE Co KATKILANMIŞ MgB2 SÜPERİLETKENLERİN İNCELENMESİİsmail DEMİRELErciyes Üniversitesi, Fen Bilimleri EnstitüsüYüksek Lisans Tezi, Mart 2006Tez Danışmanı: Doç. Dr. Ayhan GÜLDESTEÖZET(MgB2)1-xCux (x=0.0, 0.1 , 0.2 , 0.3 , 0.4 , 0.5) ve (MgB2)1-xCox (x=0.0, 0.1, 0,3, 0,5)süperiletken sistemleri katıhal reaksiyon tekniği ile hazırlanmıştır. Hazırlanannumunelerin yapısal özellikleri X-ışını toz kırınımı (XRD) tekniği ve taramalı elektronmikroskobu (SEM) ile incelenmiştir. Her iki sisteminde XRD analizi, MgB2 sistemineCu ve Co'ın eklenmesinin sırası ile MgCu2, MgB24, MgO ve MgB4, MgCo2O safsızlıkfazları ile çok fazlı bir oluşuma neden olduğunu gösterdi. Cu ve Co konsantrasyonuarttığında bu safsızlık fazlarının pik şiddeti artmaktadır. Ayrıca MgB2 içerisinde Cu veCo'ın herhangi bir kaydedilebilir çözünmesi gözlenmemiştir.Cu ve Co eklenmesiyle elektriksel özellikler büyük ölçüde etkilenmiştir. Numunelerindirencinin sıcaklık bağımlılığı Tc'ye kadar bir metalik davranış gösterdi. MgB2 içindekiCu ve Co konsantrasyonu artırıldığında, Tc ve Tc(0) değerlerinin azaldığı bulundu.Süperiletkenlik faz geçişi x=0.3 yukarısındaki Cu konsantrasyonu ve Co'ın x=0.5numunesi için tamamen kayboldu. MgB2 içerisinde Cu ve Co ilavesi ile geçişin daha dagenişlediği, saf MgB2 (x=0) için süperiletkenlik geçişlerinin keskin olduğu gözlenmiştir.Uygulanan magnetik alanın artışı ile bu geçiş daha da genişler. Termoelektrik güç S(T)değerinin bütün numuneler için pozitif bulunması hole tipi iletimin baskın olduğunugöstermektedir. Termal iletkenliğin (κ) büyüklüğü Cu ve Co konsantrasyonuartırıldığında aşağı doğru bastırıldı ve HTc sistemlerde genellikle gözlenen, Tc'ye yakınsıcaklıklarda κ(T)'nin keskin yükselişi gözlenmedi.

Özet (Çeviri)

ivINVESTIGATION OF Cu AND Co-DOPED MgB2 SUPERCONDUCTORSİsmail DEMİRELErciyes University, Graduate School of Natural and Applied SciencesM. Sc. Thesis, March 2006Thesis Supervisor: Assoc. Prof. Ayhan GÜLDESTEABSTRACTThe (MgB2)1-xCux (x=0.0, 0.1 , 0.2 , 0.3 , 0.4 , 0.5) and (MgB2)1-xCox (x=0.0, 0.1, 0,3,0,5) superconducting system were prepared by a solid-state reaction technique. Thestructural properties of prepared samples were investigated by X-Ray powderdiffraction (XRD) technique and Scanning Electron Microscopy (SEM). The XRDanalysis of both systems showed that the addition of Cu and Co into the MgB2 systemcaused a multiphase formation with impurity phases mainly MgCu2, MgB24, MgO andMgB4, MgCo2O respectively. The peak intensity of these impurity phases increasedwhen Cu and Co concentration increased. It was also not observed any detectablesolution of Cu and Co in MgB2.The electrical properties were considerably effected by addition of Cu and Co. Thetemperature dependence of resistivity of the samples showed a metallic behavior downto Tc. It was found that the Tc and Tc(0) values decreased when Cu and Co concentrationwas increased in MgB2. The superconducting phase transition completely disappearedfor the Cu concentration above x=0.3 and for the x=0.5 sample of Co. Thesuperconducting transition was obtained to be sharp for pure MgB2 (x=0) where on thetransition become broader with increasing Cu and Co addition into the MgB2. Thetransition becomes also broader with increasing the applied magnetic field. Thethermoelectric power, S(T), value was obtained to be positive for all the samples,indicating that the hole-type conducting is dominant. The magnitude of Thermalconductivity, κ, was suppressed when the Cu and Co concentration was increased andsharp rising of κ(T) at temperatures close to Tc which is often appeared in the HTcsystems was not observed.

Benzer Tezler

  1. ZnO nano sistemlerinin sentezlenmesi ve manyetik özelliklerinin elektron paramanyetik rezonans (EPR) spektroskopisi ile incelenmesi

    Synthesize of ZnO nano systems and investigation of their magnetic properties by using electron paramagnetic resonance (EPR) spectroscopy

    CANGÜL AKTÜRK

    Yüksek Lisans

    Türkçe

    Türkçe

    2013

    Fizik ve Fizik MühendisliğiHacettepe Üniversitesi

    Fizik Mühendisliği Ana Bilim Dalı

    DOÇ. DR. ŞEYDA ÇOLAK

  2. Bazı manyetik malzemelerde (Cu-Co, Ti1-xCoxO2 ince filmler ve mikroteller) dev manyeto empedans incelemeleri

    Giant magneto impedance investigations of some magnetic materials (Cu-Co, Ti1-xCoxO2 thin films and microwires)

    FİKRET YILDIZ

    Doktora

    Türkçe

    Türkçe

    2004

    Fizik ve Fizik MühendisliğiGebze Yüksek Teknoloji Enstitüsü

    Fizik Ana Bilim Dalı

    Y.DOÇ.DR. BULAT RAMEEV

  3. Değişik metal katkılanmış lityum içerme bileşiklerinin sentezi karakterizasyonu ve doldurulabilir lityum piller

    Synthesis and characterization of various metal doped lithium insertion compounds and rechargeable lithium batteries

    ELMAS ÖZKAN

    Yüksek Lisans

    Türkçe

    Türkçe

    2003

    KimyaErciyes Üniversitesi

    Kimya Ana Bilim Dalı

    PROF. DR. ŞABAN PATAT

  4. Lityum iyon pillerde katot aktif madde olarak kullanılan LiMn2O4 bileşiğinin elektrokimyasal performansının artırılması

    Enhancement of electrochemical performance of LiMn2O4 as a cathode active material for lithium-ion batteries

    HALİL ŞAHAN

    Doktora

    Türkçe

    Türkçe

    2009

    KimyaErciyes Üniversitesi

    Kimya Bölümü

    PROF. DR. ŞABAN PATAT

  5. Bazı lityum metal vanadat içerme bileşiklerinin sentezi, karakterizasyonu ve elektrokimyasal özelliklerinin incelenmesi

    Synthesis, characterization and research of some lithium metal oxide insertion compounds

    FATMA KILIÇ

    Yüksek Lisans

    Türkçe

    Türkçe

    2008

    KimyaKahramanmaraş Sütçü İmam Üniversitesi

    Kimya Bölümü

    PROF. DR. ŞABAN PATAT