Yüzeyi ince film kaplanmış 100Cr6 çeliğinin çeşitli ortamlarda sürtünme ve aşınma davranışlarının incelenmesi
The investigation of friction and wear behavior of thin film coated 100Cr6 in different environments
- Tez No: 244647
- Danışmanlar: YRD. DOÇ. DR. TEVFİK KÜÇÜKÖMEROĞLU
- Tez Türü: Yüksek Lisans
- Konular: Makine Mühendisliği, Metalurji Mühendisliği, Mühendislik Bilimleri, Mechanical Engineering, Metallurgical Engineering, Engineering Sciences
- Anahtar Kelimeler: MoS2-Ti, Fiziksel Buhar Kaplama, Triboloji, Aşınma, Vakum, MoS2-Ti, Phsical Vapor Deposition, Tribology, Wear, Vacuum
- Yıl: 2009
- Dil: Türkçe
- Üniversite: Karadeniz Teknik Üniversitesi
- Enstitü: Fen Bilimleri Enstitüsü
- Ana Bilim Dalı: Metalurji ve Malzeme Mühendisliği Ana Bilim Dalı
- Bilim Dalı: Belirtilmemiş.
- Sayfa Sayısı: 90
Özet
Sürtünme ve aşınma, özellikle havacılık, uzay, elektronik, kimya, kaplama veimalat sanayi gibi alanlarda kullanılmakta olan tüm sistemleri olumsuz etkileyen önemlietkenlerdir. Tribolojik uygulamaların çoğunda sürtünme ve aşınma ile ilgili bu güçlükleriaşmak için çeşitli yağlayıcılar kullanılmaktadır. Ancak, aşırı koşullarda (aşırı sıcaklık,ortam basıncı ve yüzey basıncı vb.) ortaya çıkacak olan sürtünme ve aşınmayı kontroledebilmek için günümüzde temas yüzeylerini katı yağlayıcılar ile kaplanmak en etkiliyöntemlerin başında gelmektedir.MoS2 düşük kayma gerilmesine sahip olması nedeniyle bu alanlarda yaygın olarakkullanılan bir katı yağlayıcıdır. Ancak, MoS2 bu özelliğini her türlü ortamdasürdürememektedir. MoS2'nin düşük kayma gerilmesi değerini söz konusu ortamlarda dasağlayabilmesi kaplamanın yapısına çeşitli elementler katılarak gerçekleştirilebilmektedir.Bu çalışmada darbeli DC kapalı alan manyetik alanda sıçratma yöntemiyle AISI52100 taban malzeme üzerine MoS2-Ti kaplanmıştır. Kaplanan bu filmlerin mekanik,yapısal ve çeşitli ortamlardaki tribolojik özellikleri incelenmiştir. Elde edilen kaplamalardakristolografik yönlenme, kaplama yapısındaki titanyum oranına bağlı olarak değişmekteolduğu belirlenmiştir. Kaplamaların kalınlığını etkileyen en etkin parametrenin magnetronhedef akımının olduğu ortaya çıkarılmıştır. Yapıya eklenen titanyum oranının artmasıylagenel olarak kaplamaların vakum ortamındaki tribolojik davranışlarını olumsuz yöndeetkilediği görülmüştür.
Özet (Çeviri)
Friction and wear are important factors which negatively affect all the systems inaeronautic, space, electronic, chemistry, coating and manufacturing industry. In manytribological applications, various lubricants are used to overcome the difficulties caused byfriction and wear. However, in order to control friction and wear in extreme conditions(high temperatures, high pressure etc.), coating of the contact surface with solid lubricantsis one of the most effective techniques used.MoS2 is a solid lubricant commonly used in this area since it has low shear strength.However MoS2 is not able to show this behavior in any conditions. In order to achieve this,various elements are mixed in coating structure.In this study, AISI 52100 was coated with MoS2-Ti using Pulsed DC Closed-Fieldunbalanced magnetron sputtering. In addition, mechanical, structural and tribologicalproperties of these coated films were investigated. It was observed that the crystallographicorientation was affected by the amount of titanium in the coated films. Furthermore, it wasinvestigated that the most important factor affecting the thickness of the coated films wasthe magneton target current. It was seen that the tribological behavior of the coated films inthe vacuum conditions was negatively affected by increasing the amount of titanium.
Benzer Tezler
- Grafen oksit nanotabakaların plazma yüzey modifikasyonları ve yağ-su ayrımı için ultrafiltrasyon membran üretiminde kullanılması
Plasma surface modification of graphene oxide nanosheets and their usage in the production of ultrafiltration membranes for oil-water separation
FURKAN TURGUT
Yüksek Lisans
Türkçe
2019
Kimya MühendisliğiKonya Teknik ÜniversitesiKimya Mühendisliği Ana Bilim Dalı
PROF. DR. MUSTAFA KARAMAN
- Tek kullanımlık modifiye edilmiş ve edilmemiş grafit elektrotların DNA hibridizasyon sensörü olarak kullanılabilirliğinin araştırılması
Investigation of the usability of modified and unmodified disposable graphite electrodes as DNA hybridization sensor
HAKAN ŞİRANLI
- İnce film kaplama yapılmış nanofiber membranların partikül filtrasyon performanslarının belirlenmesi
Determination of particul filtration performances of thin film composite nanofiber membranes
MÜGE BİÇER
Yüksek Lisans
Türkçe
2016
Çevre Mühendisliğiİstanbul Teknik ÜniversitesiÇevre Mühendisliği Ana Bilim Dalı
PROF. DR. İSMAİL KOYUNCU
- Manufacturing of polystyrene panels with tunable colors
Renkleri değiştirilebilen polistiren levhaların üretilmesi
ECE TÜKENMEZ
Yüksek Lisans
İngilizce
2017
Kimyaİstanbul Teknik ÜniversitesiKimya Ana Bilim Dalı
PROF. DR. OKAN SİRKECİOĞLU
- ALD film kaplı poliamid kumaşların antibakteriyel etkinliklerinin araştırılması
Investigation of antibacterial activitiy of ALD coated polyamide fabrics
SÜMEYYE DİLER
Yüksek Lisans
Türkçe
2021
Tekstil ve Tekstil MühendisliğiBursa Uludağ ÜniversitesiTekstil Mühendisliği Ana Bilim Dalı
DR. ÖĞR. ÜYESİ HALİL İBRAHİM AKYILDIZ