Poli(vinilklorür) yüzeyinin UV ışınlarıyla başlatılan aşı kopolimerizasyonu ile hidrofilik modifikasyonu
Hidrophilic surface modification of Poly(vinylchloride) by UV induced graft copolymerization
- Tez No: 296010
- Danışmanlar: PROF. DR. OLGUN GÜVEN
- Tez Türü: Yüksek Lisans
- Konular: Kimya, Chemistry
- Anahtar Kelimeler: Foto aşılama, yüzey modifikasyonu, hidrofilik, tıbbi saflıkta PVC, ATR-FTIR, Photo grafting, surface modification, hydrophilic, medical grade PVC, ATR-FTIR
- Yıl: 2011
- Dil: Türkçe
- Üniversite: Hacettepe Üniversitesi
- Enstitü: Fen Bilimleri Enstitüsü
- Ana Bilim Dalı: Nanoteknoloji ve Nanotıp Ana Bilim Dalı
- Bilim Dalı: Belirtilmemiş.
- Sayfa Sayısı: 118
Özet
UV ışınlarıyla başlatılan aşı polimerizasyonu, polimer yüzeylerini hidrofilik olarak modifiye etmek için kullanılan başlıca tekniklerden birisidir. Bu çalışmada tıbbi saflıktaki poli(vinilklorür) (PVC) filmlerinin yüzeylerini hidrofilik ve kaygan bir şekilde modifiye etmek amacıyla, N-vinilpirolidon monomeri film yüzeylerine foto-aşılandı. Aşı polimerizasyonu fotobaşlatıcı olarak benzofenon içeren monomer çözeltisi içerisine tıbbi saflıktaki PVC filmleri yerleştirilerek, hava ortamında ve oda sıcaklığında gerçekleştirildi. En etkili yüzey modifikasyonu için aşılama verimini etkileyen monomer derişimi (% 20-80), benzofenon miktarı (0.01-0.05 M), UV lambası ile örnek arasındaki uzaklık (5-15 cm) ve ışınlama süresi (1-15 dk) gibi parametreler incelendi. İstenilen hidrofilik yüzey özelliğini elde edebilmek için % 20 monomer derişimi, 0.04 M benzofenon, 10 dakika ışınlama süresi ve 10 cm uzaklık optimum koşullar olarak belirlendi.Aşılama verimleri gravimetrik ve spektroskopik yöntemlerle bulundu ve aşılanan filmlerin kimyasal karakterizasyonları FTIR, XPS ve Raman Spektrometresi ile yapıldı. Modifiye edilen yüzeylerin hidrofilik özelliği temas açısı gonyometresi ile ölçüldü ve yüzey serbest enerjileri hesaplandı. Aşılamayla birlikte tıbbi saflıktaki PVC'nin molekül ağırlığı dağılımındaki değişikliği gözlemlemek için büyüklükçe ayırma kromatografisi (SEC) analizleri yapıldı. Optimum koşullarda gravimetrik aşılama verimi % 4.0 olarak belirlendi ve bu verimde modifiye edilen filmin yüzey temas açısının 81.8º den, poli(vinilpirolidon) (PVP)'un temas açısı olan 66.4º ye kadar düştüğü gözlemlendi. Bu sonuç aşılamanın ve yüzey modifikasyonunun başarılı bir şekilde gerçekleştiğini göstermektedir.
Özet (Çeviri)
UV induced graft polymerization used for surface modification of polymers is one of the major techniques to improve surface hydrophilicity. In this study, N- vinylpyrrolidone monomer was photo-grafted on the PVC film surfaces in order to modify the films as hydrofilic and lubrious. Graft polymerization was performed in air at room temperature by placing medical-grade PVC films into monomer solution which contains benzophenon as photoinitiator. For the most effective surface modification, parameters as monomer concentration (% 20-80), photoinitiator amount (0.01-0.05 M), UV exposure time (1-15 min), the distance between UV lamp and sample (5-15 cm) that effect the graft yield were investigated. In order to obtain desired hydrophilic surface property, % 20 monomer concentration, 0.04 M benzophenon, 10 minutes irradiation time and 10 cm distance were determined as the optimum conditions.Graft yield was found by gravimetric and spectroscopic methods and chemical characterization of grafted films were made by FTIR, XPS and Raman Spectroscopy techniques. Contact angle of modified surfaces were measured by contact angle goniometer and surface free energies were calculated. Size exclusion chromatography analysis were made in order to observe the changes in molecular weight distribution of PVC with grafting. In optimized conditions, the gravimetric graft yield was calculated as % 4.0 and It was observed that the contact angle of PVC was decreased from 81.8º to 66.4º which is equal to the contact angle of poly(vinylpyrrolidone) (PVP) film. This result indicates that the surface modification and grafting was performed successfully.
Benzer Tezler
- Preparation of pol (vinly chloride) blends: spect ruscopic, thermal, viscosimetric, mechanical and surface characterizations
Poli (Vinil klorür) karışımlarının hazırlanması: Spektroskopik, ısıl, viskonimetrik, mekanik ve yüzey karakterizasyonları
OKŞAN KARAL
Doktora
İngilizce
1998
Kimyaİstanbul Teknik ÜniversitesiKimya Ana Bilim Dalı
PROF. DR. BAHATTİN M. BAYSAL
- Bazı palladyum komplekslerinin iyonofor olarak kullanıldığı iyodür-seçici elektrotların yapımında yeni yaklaşımlar
New approaches for the preparation of iodide-selective electrodes based on some palladium complexes used as ionophore
SEMRA MURATOĞLU
- The Effect of aging on physical and mechanical properties of poly (vinyl chloride) compounts
Yaşlandırma testlerinin poli (vinilklörür) kompoundu üzerindeki fiziksel ve mekanik özelliklerindeki değişimi
DİDEM KALE (EKER)
Yüksek Lisans
İngilizce
2000
KimyaEge ÜniversitesiKimya Mühendisliği Ana Bilim Dalı
PROF. DR. MESUT YENİGÜL
- Isıl püskürtme teknikleriyle plastik ve plastik esaslı kompozit tozlarla kaplanmış yüzeylerin mekanik ve kimyasal özelliklerinin incelenmesi
An Investigation ot mechanicals and chemicals properties ot the plastic and plastic based compozite powder coated surtaces by flama and plasma techniques
MUSTAFA ÖKSÜZ
Doktora
Türkçe
1999
Eğitim ve ÖğretimMarmara ÜniversitesiMetal Eğitimi Ana Bilim Dalı
DOÇ.DR. HÜSEYİN YILDIRIM
- Polyelctrolyte membrane design via click chemistry
Klik kimyası ile polielektrolit membran dizaynı
MEHMET BAŞDAL
Yüksek Lisans
İngilizce
2013
Polimer Bilim ve Teknolojisiİstanbul Teknik ÜniversitesiPolimer Bilim ve Teknolojisi Ana Bilim Dalı
PROF. DR. METİN H. ACAR