Zirkonyum, metal ve alümina destekli üç ve dört üyeli posterior köprülerde porselen bağlantı direncinin ısı ve yük analizleriyle incelenmesi.
Evaluating the porcelain bonding resistance of zirconia, gold and alumina cored posterior fixed partial dentures by finite element analysis
- Tez No: 329117
- Danışmanlar: PROF. DR. ATİLLA SERTGÖZ, DOÇ. DR. BÜLENT EKİCİ
- Tez Türü: Doktora
- Konular: Diş Hekimliği, Dentistry
- Anahtar Kelimeler: Belirtilmemiş.
- Yıl: 2012
- Dil: Türkçe
- Üniversite: Marmara Üniversitesi
- Enstitü: Sağlık Bilimleri Enstitüsü
- Ana Bilim Dalı: Protetik Diş Tedavisi Ana Bilim Dalı
- Bilim Dalı: Belirtilmemiş.
- Sayfa Sayısı: 198
Özet
Bu çalışmanın amacı, farklı termal genleşme katsayılı üstyapı porselenleri ile venerlenen, farklı uzunluktaki posterior köprülerin porselen fırınlaması sonrası ve çiğneme kuvvetleri karşısındaki mekanik davranışlarının sonlu elemanlar analiz yöntemi ile incelenmesidir. Kartezyen koordinat sisteminde çizilen 3 ve 4 üyeli posterior köprü modelleri üç boyutlu sonlu elemanlar analiz programına aktarıldı. Zirkonyum, altın alaşım ve alümina alt yapılarla vener porselenlerinden oluşan modellerden zirkonyum ve alümina alt yapılar ayrıca 2'şer farklı TGK' ya sahip porselenlerle venerlendi. Termal streslerle beraber, çiğneme kuvvetleri ve kontak tipi ile oluşan birleşik stres dağılımları incelendi. Bu amaç ile çalışmanın ilk bölümünde zirkonyum ve alüminyum oksit destekli 3 ve 4 üyeli köprü restorasyonlarında, her alt yapıya uygun 3'er farklı TGK' ya sahip porselenlerle fırınlanması sonucu oluşacak termal stresler 3 boyutlu sonlu elemanlar stres analiz yöntemi ile hesaplandı. Altın alaşım destekli 3 ve 4 üyeli köprü restorasyonları da uygun TGK' ya sahip porseleni ile kontrol grubu olarak değerlendirildi. Çalışmanın ikinci bölümünde ise; ilk bölümde stres analizi yapılmış modellere, 3 farklı okluzal kontak tipinde; 3 farklı yük uygulandı ve oluşan stresler 3 boyutlu sonlu elemanlar stres analiz yöntemi ile hesaplandı. Modellere 14 termal stres analizi ve 126 okluzal kuvvet analizi uygulandı. Sonuçlar maksimum asal stres değeri olarak değerlendirildi. Çalışmanın sonucunda tam seramik restorasyonlarda iki yapı arasındaki bağlantının, materyallerin TGK' ları arasındaki uyumluluktan etkilendiği gözlenmiştir. Maksimum asal stres değerleri materyallerin TGK' ları arasındaki fark azaldıkça düşmektedir. Tam seramik materyallerin dirençleri aynı zamanda okluzal kuvvet miktarı ve kontak tipinden de etkilenmektedir. Maksimum gerilim stres değerleri antagonist kontakların artmasıyla azalmaktadır.
Özet (Çeviri)
The objective of this study was to evaluate the influence of three different core materials veneered with porcelains with different thermal expansion of coefficients (CTE), on the residual stresses in posterior fixed patial dentures and the stress distribution due to the combined influences of different loading conditions by finite element analysis (FEA). The model of a multi-layer three and four unit fixed partial denture for posterior region has drawn at cartesian coordinat system was translated into a three-dimensional FEA program. These fixed partial denture models was made with gold alloy, zirconia, and alumina-based core and veneering ceramics. For the zirconia and alumina cores also two different porcelains with different CTE were used for veneering. Fourteen thermal stress analysis and 126 occlusal loading stress analysis were performed. Results were evaluated in two groups. One of them is thermal residual stresses as bonding strength and the other is combined stress values as the flexural strength of the multi-layer fixed partial denture. Results showed that bond strength of all-ceramic materials depends on the compatibility between CTE of ceramic systems. Residual tensile stresses decreases as the difference of CTE of the materials decreases. The strength of all ceramic materials also effected by the level of load and loading conditions. Stresses decreases as the number of antagonist contacts increases.
Benzer Tezler
- Copy-milling sistemiyle hazırlanmış üç üniteli iki farklı materyaldeki tam seramik köprülerin marjinal uyumlarının fırınlama aşamalarında karşılaştırılması
Comparison of marginal adaptation of two different three unit all-ceramic bridges fabricated with copy-milling system during the firing cycles
GÜRKAN USANMAZ
Doktora
Türkçe
2005
Diş HekimliğiHacettepe ÜniversitesiProtetik Diş Tedavisi Ana Bilim Dalı
PROF.DR. ERDAL ŞAHİN
- Tam ve metal destekli porselenlerde marjin seramiğinin yapımında kullanılan iki farklı yöntemin seramik homojenitesine etkisinin incelenmesi
The examination of the effect of two different methods which are used in the construction of margin ceramics in the all and metal reinforced porcelain on the ceramic homogeneity
UMUT GÜLER
- Biyokütleden sulu faz reformlama ile hidrojen üretimi için nano karbon/metal katalizörler geliştirilmesi
Developing nano carbon/metal catalysts for hydrogen production from biomass by using aqueous phase reforming technique
BURÇAK KAYA
- Krom ve molibden içerikli mezogözenekli alümina destekli katalizörlerin etan dehidrojenasyonunda mikrodalga reaktörde incelenmesi
Investigation of mesoporous alumina supported chromium and molybdenum catalysts in dehydrogenation of ethane in microwave reactor
PINAR ÇİTLİ
Yüksek Lisans
Türkçe
2019
Kimya MühendisliğiGazi ÜniversitesiKimya Mühendisliği Ana Bilim Dalı
PROF. DR. NURAY OKTAR
- Non-oxidative dehydrogenation of propane to propene over precious-metal free anatase titania
Değerli metal içermeyen anataz titanya üzerinde propanın propene oksidatif olmayan dehidrojenasyonu
IQTIDAR ALI KHAN
Yüksek Lisans
İngilizce
2022
Kimya MühendisliğiOrta Doğu Teknik ÜniversitesiKimya Mühendisliği Ana Bilim Dalı
DR. ÖĞR. ÜYESİ GÖKHAN ÇELİK