Nikel alüminatların sürtünme kaynağı ile birleştirilebilirliklerinin araştırılması

The investigation of weldability of nickel aluminides with friction welding

  1. Tez No: 334786
  2. Yazar: GÖKHAN ARICI
  3. Danışmanlar: YRD. DOÇ. DR. İBRAHİM ÇELİKYÜREK
  4. Tez Türü: Yüksek Lisans
  5. Konular: Metalurji Mühendisliği, Mühendislik Bilimleri, Metallurgical Engineering, Engineering Sciences
  6. Anahtar Kelimeler: Metallerarası bileşikler, sürtünme kaynağı, nikel alüminatlar, 316L paslanmaz çelik, mikroyapı, mikrosertlik, kesme mukavemeti, Intermetallics, friction welding, nickel aluminides, 316L stainless steel, microstructure, microhardness, shear strength
  7. Yıl: 2013
  8. Dil: Türkçe
  9. Üniversite: Eskişehir Osmangazi Üniversitesi
  10. Enstitü: Fen Bilimleri Enstitüsü
  11. Ana Bilim Dalı: Metalurji Mühendisliği Ana Bilim Dalı
  12. Bilim Dalı: Belirtilmemiş.
  13. Sayfa Sayısı: 116

Özet

Bu çalışmada, Ni3Al metallerarası bileşiğin kendisiyle ve 316L paslanmaz çelik ile sürtünme kaynağı yapılmıştır. Farklı sürtünme hızları, sürtünme basınçları ve sürtünme süreleri denenerek optimum kaynak parametreleri belirlenmiştir ve bulunan kaynak parametrelerinin kaynak arayüzeyine, mikroyapıya ve mekanik özelliklere etkisi incelenmiştir. Kaynakların birleşme arayüzeyinde değişen şartlarda meydana gelen değişimleri incelemek için optik mikroskop ve taramalı elektron mikroskobu (SEM) kullanılmıştır. Ayrıca birleşme arayüzeyine dik doğrultuda mikrosertlik ölçümleri yapılmıştır ve ölçülen değerler malzeme arayüzeyinde meydana gelen mikroyapısal değişimlerle ilişkilendirilerek değerlendirilmiştir. Aynı zamanda malzemelerde kaynak kısımlarının kesme mukavemeti ölçülerek mukavemetin şartlara göre nasıl değişiklik gösterdiği incelenmiştir.Ni3Al alaşımının kendisiyle ve 316L paslanmaz çelik ile sürtünme kaynağında değişen işlem parametrelerinin kaynak arayüzeyi mikroyapısını, sertliğini ve mukavemetini etkilediği görülmüştür.Sabit sürtünme hızında, artan süre ve basınç ile doğru orantılı artan sıcaklık sonucu kaynak arayüzeyinin kesme mukavemetinin arttığı görülmüştür. Ancak belli bir değerden sonra aşırı ısınmanın kaynak arayüzeyinde tavlama etkisi yaptığı ve mukavemetin düştüğü görülmüştür.

Özet (Çeviri)

In this study, Ni3Al alloy was bonded with itself and 316L stainless steel by friction welding. Different friction speeds, friction durations and friction pressures were tested to find optimum friction welding parameters and it was investigated how effects the welding parameters to welding interface, microstructure and mechanical properties. SEM and optical microscopy were carried out to examine the microstructural variations on welding interfaces of samples. Also microhardness distribution across the interface was evaluated considering the microstructural variations. In addition, shear strength of welded parts were measured to find out the effects of welding conditions.It was observed that microstructure, microhardness and shear strength of welding interface were affected by welding parameters.For a fixed friction speed, the shear strength of welding interface of materials increased with increase in friction pressure and duration which cause higher temperature. But after a certain time and the pressure value, it was observed that overheating of welding interface causes annealing so shear strengths of welding interface of materials decreased.

Benzer Tezler

  1. AISI 1030 çelik yüzeyine GTA kaynak yöntemiyle Ni3Al intermetalik bileşiğinin kaplanabilirliğinin araştırılması

    Investigation of surface coating Ni3Al intermetalic compound on the AISI 1030 steel by using GTA welding method

    ADİL KÜÇÜKARSLAN

    Yüksek Lisans

    Türkçe

    Türkçe

    2015

    Teknik EğitimFırat Üniversitesi

    Metalurji Eğitimi Ana Bilim Dalı

    DOÇ. DR. UĞUR ÇALIGÜLÜ

  2. Dubleks paslanmaz çeliğin Ni3Al ile kaplanabilirliğinin araştırılması.

    Investigation with Ni3Al coating of dublex stainless stell

    TAYFUN ÇETİN

    Yüksek Lisans

    Türkçe

    Türkçe

    2014

    Metalurji MühendisliğiFırat Üniversitesi

    Metalurji ve Malzeme Mühendisliği Ana Bilim Dalı

    DOÇ. DR. SERMİN OZAN

  3. Östenitik paslanmaz çeliğin bor katkılı Ni3Al ile kaplanabilirliğinin araştırılması

    Investigation of boron doped Ni3Al coating of austenitic stainless stell

    MEHMET AKKAŞ

    Yüksek Lisans

    Türkçe

    Türkçe

    2013

    Metalurji MühendisliğiFırat Üniversitesi

    Metalurji Eğitimi Ana Bilim Dalı

    DOÇ. DR. SERMİN OZAN

  4. The role of boron in phosphorescence persistence of rare-earth co-activated alkalai aluminates

    Nadir toprak elementiyle katkilandirilmis alkali aluminatlarin fosforesans surerliliginde boronun etkisi

    MURAT GÖKHAN ESKİN

    Yüksek Lisans

    İngilizce

    İngilizce

    2011

    Metalurji MühendisliğiSabancı Üniversitesi

    Malzeme Bilimi ve Mühendisliği Ana Bilim Dalı

    YRD. DOÇ. DR. CLEVA OW YANG

  5. Understanding the unusual passive behaviour of high strength hybrid steel in corrosive environments

    Yüksek mukavemetli hibrit çeliğin korozif ortamlarda olağandışı pasif davranışının anlaşılması

    BESTE PAYAM

    Yüksek Lisans

    İngilizce

    İngilizce

    2022

    Metalurji Mühendisliğiİstanbul Teknik Üniversitesi

    Metalurji ve Malzeme Mühendisliği Ana Bilim Dalı

    DR. ÖĞR. ÜYESİ CEM ÖRNEK