Yüzey ve ısıl işlemlerinin zirkonya alt yapı sistemlerinin mekanik özelliklerine etkisinin araştırılması ve X-ray difraktometre yüzey analizleri ile değerlendirilmesi

Investigating the effect of surface and heat treatment on mechanical properties of zirconia based ceramicsand evaluating by X-ray difractometer surface analyses

  1. Tez No: 341975
  2. Yazar: İPEK ÇAĞLAR
  3. Danışmanlar: PROF. DR. NURAN YANIKOĞLU
  4. Tez Türü: Doktora
  5. Konular: Diş Hekimliği, Dentistry
  6. Anahtar Kelimeler: Belirtilmemiş.
  7. Yıl: 2012
  8. Dil: Türkçe
  9. Üniversite: Karadeniz Teknik Üniversitesi
  10. Enstitü: Sağlık Bilimleri Enstitüsü
  11. Ana Bilim Dalı: Protetik Diş Tedavisi Ana Bilim Dalı
  12. Bilim Dalı: Belirtilmemiş.
  13. Sayfa Sayısı: 112

Özet

Zirkonya alt yapılı seramikleryüksek mekanik özellikleri nedeniyle diş hekimliğinde sıklıkla kullanılmaktadır. Ancak uygulanan yüzey ve ısıl işlemlerininalt yapı materyallerinin mekanik özelliklerini etkilediği düşünülmektedir. Bu in vitro çalışmada; iki zirkonya esaslı alt yapı sistemine uygulanan yüzey ve ısıl işlemleri sonrasında, materyallerin ortalama yüzey pürüzlülüğü, faz değişim analizleri ve bükülme dayanımları araştırıldı. Çalışmada her materyal için 15 mm çapında ve 1.2±0.2 mm kalınlığında 40'ar adet disk şeklinde örnek hazırlandı. Örnekler kendi içinde 4 gruba (kontrol, kumlama, lazerle pürüzlendirme ve fırınlama) ayrıldı. Tüm örneklerin, profilometre ile yüzey pürüzlülüğü ölçümü,tarama elektron mikroskobu (SEM) analizi ve X-Ray difraksiyon (XRD) analizi yapıldı. Materyallerin bükülme dayanımları iki eksenli bükülme dayanımı testi (üç top üzerinde piston) ile incelendi.Veriler Bonferroni düzeltmeli Kruskal Wallis H Testi (p0.05). XRD analizinde;her iki materyalde göreceli monoklinik faz oranlarının ısıl işlemler ile ciddi bir şekilde azaldığı saptandı. Fırınlanan örneklerinin bükülme dayanımları azalırken, kumlama ve lazer uygulanan örneklerin bükülme dayanımlarının arttığı tespit edildi (p

Özet (Çeviri)

In dentistry zirconia based ceramics are frequently used because of their high mechanical properties. However, different surface and heat treatment methods are believed effect their mechanical properties . In this in-vitro study, the effect of surface and heat treatment on mean surface roughness, phase transformation analysis and biaxial flexural strength of two zirconia based core materials were investigated.In this study 40 discs specimens of the materials were fabricated with a diameter of 15 mm and 1.2±0.2 mm. Fourty discs from each material were randomly divided into four groups (control, sandblasting, etching with laser energy, firing process).Surface roughness was measured by using profilometer. Surface topographic analysis was examined by scanning electron microscopy (SEM). X-ray diffraction analysis was performed to characterize the crystalline phases for all specimens.All spicemen?s flexural strength were examined by biaxial flexural strength test (piston on 3 balls).The data were analyzed by using the Kruskal Wallis H Test and Mann Whitney U Test for multiple comparison. Spearman?s rho (?) coefficient was usedto investigate relationshipbetween surface roughness roughness and biaxial flexural strength, relative amount of monoclinic zirconia and biaxial flexural strength, surface roughness and relative amount of monoclinic zirconia. Heat and surface treatments effect the surface roughness of two zirconia based core materials but the diffrences are not significantly important. X-ray diffraction analysis revealed that in all materials, transformation from tetragonal to monoclinic phases was decreased by heat treatments. Firing significantly decreased the strength values of two materials. The mean biaxial flexural strength of laser and sandblasted group were significantly different. A liner correlation was found between the roughness of the surface and strength for all groups. However, significant correlation was found only in firing DC-Zirkon specimens.

Benzer Tezler

  1. Yüzey uygulamaları ve yapay yaşlandırma işleminin Y-TZP dental seramiklerinin biaksiyel bükme dayanımı ve faz değişimi üzerine etkilerinin in-vitro olarak incelenmesi

    Influence of surface treatments and accelerated aging on flexural strength and phase transformation of bilayered Y-TZP ceramics

    EVRİM ÖZER BULTAN

    Doktora

    Türkçe

    Türkçe

    2013

    Diş Hekimliğiİstanbul Üniversitesi

    Protetik Diş Tedavisi Ana Bilim Dalı

    PROF. DR. DENİZ ŞEN

  2. Farklı üstyapı seramiklerinin zirkonya altyapıya makaslama bağ dayanımlarının araştırılması

    Evaluation of shear bond strength of different veneering ceramics to Y-TZP framework

    GÖKHAN UZEL

    Doktora

    Türkçe

    Türkçe

    2010

    Diş HekimliğiEge Üniversitesi

    Protetik Diş Tedavisi Ana Bilim Dalı

    PROF. DR. BİRGÜL ÖZPINAR

  3. Zirkonyanın farklı yüzey işlemleri sonrası rezin siman ile bağlantısının değerlendirilmesi

    Effects of surface treatments on the shear bond strenght of luting cements to zirconia

    IŞIL KEÇİK BÜYÜKHATİPOĞLU

    Doktora

    Türkçe

    Türkçe

    2015

    Diş HekimliğiGaziantep Üniversitesi

    Protetik Diş Tedavisi Ana Bilim Dalı

    DOÇ. DR. ASLI SEÇİLMİŞ

    PROF. DR. GÜLFEM ERGÜN

  4. Uçak motorlarında kullanılan ınconel 718 süper alaşımının atmosferik plazma yöntemiyle kaplanarak sürünme davranışının incelenmesi

    Investigation of creep behaviour of inconel 718 superalloys used in aircraft engines by coating with atmospheric plasma method

    ERGÜN SUBAŞI

    Doktora

    Türkçe

    Türkçe

    2022

    Metalurji Mühendisliğiİstanbul Teknik Üniversitesi

    Malzeme Bilimi ve Mühendisliği Ana Bilim Dalı

    PROF. DR. EYÜP SABRİ KAYALI

  5. Zirkonya destekli demir katalizörü ile sentez gazından olefin üretimi

    Olefin production from synthesis gas with zirconia supported iron catalyst

    CEMİLE DUT

    Yüksek Lisans

    Türkçe

    Türkçe

    2022

    KimyaYıldız Teknik Üniversitesi

    Kimya Mühendisliği Ana Bilim Dalı

    DOÇ. DR. HALİT EREN FİGEN

    DR. ABDULLAH ZAHİD TURAN