Genleştirilmiş polistiren köpük (EPS) ile atık polistiren köpük granüllerin betona karıştırılmasıyla elde edilen hafif betonun karakteristik özelliklerinin belirlenmesi
Characterization of expanded polystyrene foam (EPS) and waste polystyrene foam granules embedded light concrete
- Tez No: 346579
- Danışmanlar: YRD. DOÇ. DR. HALİL İBRAHİM DEMİRCİ
- Tez Türü: Yüksek Lisans
- Konular: Mühendislik Bilimleri, Teknik Eğitim, Endüstri Ürünleri Tasarımı, Engineering Sciences, Technical Education, Industrial Design
- Anahtar Kelimeler: Beton, Hafif beton, Polistiren köpük, Concrete, Lightweight concrete, Polystyrene foam
- Yıl: 2013
- Dil: Türkçe
- Üniversite: Karabük Üniversitesi
- Enstitü: Fen Bilimleri Enstitüsü
- Ana Bilim Dalı: Makine Eğitimi Ana Bilim Dalı
- Bilim Dalı: Belirtilmemiş.
- Sayfa Sayısı: Belirtilmemiş.
Özet
Bu çalışmada, birçok sektörde (ambalaj, inşaat vb.) kullanılan genleştirilmiş polistiren köpük (EPS) atıkların geri dönüşümü ve granül şeklinde genleştirilmiş polistiren köpüklerin hafif beton üretiminde kullanılabilmesi araştırılmıştır. Hafif beton kum, çimento, su, katkı maddesi ve genleştirilmiş polistiren köpük karıştırıcı ile karıştırılarak üretilmiştir. Hafif betonların üretiminde çimento miktarının (ağırlıkça) % 1, % 1,5 ve % 2 oranında atık EPS polistiren köpük granülleri kullanılmıştır. Elde edilen hafif betonun karakteristik özellikleri basınç, eğilme, su emme ve ısıl iletkenlik testleri ile belirlenmeye çalışılmıştır. Ayrıca, hafif betonların birim hacim ağırlık, rötre dayanımı çalışmaları gerçekleştirilmiştir. Yapılan basınç dayanım testleri sonucunda, en yüksek basınç dayanımı % 1 EPS ilave edilen hafif betonda 6,246 N/mm², en düşük basınç dayanımı % 2 EPS ilave edilen hafif betonda 5,209 N/mm² sağlanmıştır. Eğilme testleri sonuçlarında, en yüksek eğilme dayanımı % 1 EPS oranında üretilen hafif betonda 2,081 N/mm², en düşük eğilme % 2 EPS oranında üretilen hafif betonda dayanımı 1,763 N/mm² değeri ile elde edilmiştir. Su emme testi sonuçlarına göre, % 1 EPS ilave edilen hafif betonların % 2 EPS ilave edilen hafif betonlara göre daha yüksek olduğu belirlenmiştir. Ayrıca yine su emme testlerinde, atık EPS malzemenin betona ilavesi ile elde edilen hafif betonların normal betona göre su emme oranının daha düşük olduğu sonucuna varılmıştır. Isıl iletkenlik deney sonuçlarına göre, en düşük ısıl iletkenlik değeri % 2 atık EPS polistiren ilave edilen hafif betonda 0,3296 W/mK, en yüksek ısıl iletkenlik değeri % 1 atık EPS polistiren katkılı hafif betonda 0,3921 W/mK olarak tespit edilmiştir. EPS polistiren köpük granüllerin katkı oranlarının artması sonucu ısıl iletkenlik değerinin azaldığı, ısı yalıtım değerinin yüksek olduğu tespit edilmiştir. Son olarak, atık EPS polistiren katkılı hafif betonların yalıtımlı ve yarı taşıyıcı olarak kullanılabileceği tespit edilmiştir.
Özet (Çeviri)
In this study, wastes which are used expanded polystyrene foam (EPS) in many industries (packaging, construction, etc.) is thought recycle and so expanded polystyrene foams, which is forms granule, is investigated using in lightweight concrete. Lightweight concretes are produced by mixing with a mixer stone, cement, water, additives and expanded polystyrene foam. Lightweight concrete production used of 1%, 1,5% and 2% (by weight concrete) EPS. Lightweight concrete properties were determined by compression, bending, water absorption and thermal conductivity tests. In addition, lightweight concrete were performed unit weight, shrinkage resistance. As a result of the compressive strength tests, the maximum compressive strength of the lightweight concrete in addition to 1% EPS 6,246 N/mm² and the lowest compressive strength of lightweight concrete in addition to 2% EPS 5,209 N/mm² is provided. Bending test results, the highest flexural strength lightweight concrete produced by 1% EPS 2,081 N/mm², the lowest flexural strength lightweight concrete produced by 2% EPS 1,763 N/mm² value was obtained. According to the results of the water absorption test, 1% EPS added lightweight concretes is higher than 2% EPS added lightweight concretes. Also, in the water absorption test, the rate of water absorption was concluded that the lightweight concretes which are added waste EPS in concrete is lower than the normal. According to the experimental results of thermal conductivity, low thermal conductivity value of the additional 2% of waste polystyrene EPS lightweight concrete is determinated 0,3296 W/mK, the highest thermal conductivity of 1% of the value added lightweight concrete waste polystyrene EPS is determinated 0,3921 W/mK. When EPS foam polystyrene granules amount increasing in lightweight concrete, thermal conductivity decreasing and so the thermal insulation value is higher. Finally, lightweight concrete, is added EPS, can be used as semi-carrier.
Benzer Tezler
- EPS ve atık lastik içeren hafif dolgunun performansının araştırılması
Investigation of the performance of lightweight fill containing EPS and waste tire
ÖZCAN DİKER
Yüksek Lisans
Türkçe
2022
Mühendislik BilimleriKonya Teknik Üniversitesiİnşaat Mühendisliği Ana Bilim Dalı
DR. ÖĞR. ÜYESİ ATİLA DEMİRÖZ
- Yapı kimyasallarının çevresel etkilerinin yaşam döngüsü değerlendirme kapsamında irdelenmesi
Examination of environmental impacts of construction chemicals in the scope of life cycle assessment
CANER ÖZERCAN
Yüksek Lisans
Türkçe
2020
Çevre MühendisliğiTekirdağ Namık Kemal ÜniversitesiÇevre Mühendisliği Ana Bilim Dalı
DOÇ. DR. FÜSUN EKMEKYAPAR
- Genleştirilmiş polistiren köpük (EPS) yalıtım levhalarının özelliklerini etkileyen üretim parametrelerinin irdelenmesi
Evaluation of the production parameters affecting characteristics of expanded polystyrene foam (EPS) insulation boards
ESMA MIHLAYANLAR
- Genleştirilmiş polistiren (EPS) köpüğün geoteknikte kullanılması
Use of expanded polystyrene (EPS) foam in geotechnical engineering
HULUSİ HAKAN KİRİŞ
Yüksek Lisans
Türkçe
2019
İnşaat Mühendisliğiİstanbul Teknik Üniversitesiİnşaat Mühendisliği Ana Bilim Dalı
DOÇ. DR. İSMAİL HAKKI AKSOY
- Alüminyum ve EPS dolgulu sentetik köpükten oluşan tabakalı hibrit köpüklerin mekanik ve dinamik davranışlarının deneysel ve nümerik olarak incelenmesi
Experimental and numerical investigation of mechanical and dynamic behaviors of layered hybrid foams formed by aluminum and EPS filled syntactic foam
KÜBRA ÇAĞLA ÇIBIKÇI
Doktora
Türkçe
2024
Makine MühendisliğiAtatürk ÜniversitesiMakine Mühendisliği Ana Bilim Dalı
PROF. DR. MUSTAFA YAMAN