Sialon kesici takım üretimi ve kesme performansının incelenmesi

Sialon cutting tools and cutting percormance researched

  1. Tez No: 348664
  2. Yazar: SERKAN KILIÇ
  3. Danışmanlar: DOÇ. DR. ZAFER TATLI
  4. Tez Türü: Yüksek Lisans
  5. Konular: Teknik Eğitim, Technical Education
  6. Anahtar Kelimeler: Belirtilmemiş.
  7. Yıl: 2014
  8. Dil: Türkçe
  9. Üniversite: Sakarya Üniversitesi
  10. Enstitü: Fen Bilimleri Enstitüsü
  11. Ana Bilim Dalı: Metal Eğitimi Ana Bilim Dalı
  12. Bilim Dalı: Belirtilmemiş.
  13. Sayfa Sayısı: 126

Özet

Anahtar Kelimeler : Si3N4, α - β -SiAlON, kesici takımlar Silisyum nitrür esaslı silisyum alüminyum oksi-nitrür olarak bilinen SiAlON'lar ileri teknoloji seramik malzemelerinden biridir. Çeşitli olanlarda kullanılabilen teknik olarak önemli seramiklerdendir. Alümina (Al2O3), silisyum nitrür (Si3N4) ve alüminyum nitrürün (AlN) reaksiyon sinterlemesiyle elde edilebilmektedirler. En önemli özellikleri yüksek sıcaklık mukavemeti, yüksek sıcaklıklardaki korozyon direnci, diğer seramiklerle karşılaştırıldığında düşük termal genleşme katsayılarından dolayı çok iyi termal şok direnci, düşük yoğunluğa sahip olması, yüksek sıcaklıklarda sertliğini korumasıdır. Bu yüzden SiAlON yüksek sertlik ve mukavemet istenen yerlerde (işleme teknolojilerinde kesici takım olarak), yüksek sıcaklık korozyonunun görüldüğü yerlerde (türbin elemanları gibi), rulmanların üretiminde kullanılması olarak sıralanabilir. Bu çalışmada Si3N4 tozlarından üretilen β-SiAlON seramiğinin kesici uç olarak kullanılmasının performansı incelenmiştir. β-SiAlON genel formülündeki z=1 değerliliğine göre hesaplanıp hazırlanan sıvı faz sinterlemeyi kolaylaştırıcı oksit katkılar ( Y2O3, MgO ), kullanılarak toz kompozisyonları hazırlanmıştır. Hazırlanan toz kompozisyonları soğuk preste kesici uç formuna getirildikten sonra soğuk izostatik preste 250 MPa basınçta sinterleme öncesi maksimum ham yoğunluğa ulaştırılmıştır. Daha sonra yüksek sıcaklık grafit fırında koruyucu azot gazı ortamında numuneler 1450–1750°C'de, 30-150 dk bekleme sürelerinde sinterleme işlemleri yapılmıştır. Sinterleme sonrası numunelerin Arşimet prensibine göre yoğunluk ölçümleri yapılmıştır. Taramalı elektron mikroskobuyla (SEM) numunelerin mikroyapı analizleri yapılmıştır. XRD analizleri yapılarak Si3N4 faz dönüşümü dönüşümü ve yaklaşık α-β oranları tespit edilmiştir. Malzemelerin mekanik özelliklerini incelemek için serlik ve kırılma tokluğu değerleri incelenmiştir. Sertlik deneyleri 1 kg yük altında Vickers sertlik cihazında gerçekleştirilmiştir. Kırılma tokluğu deneyleri de yine aynı cihazda Indentasyon tekniğiyle oluşturulan çatlak boyları üzerinden ilgili formül kullanılarak hesaplanmıştır. Daha sonra bu çalışmada üretilen β-SiAlON kesici takımları ve endüstride kullanılan WC kesici takımları aynı deney şartlarında sertleştirilmiş AISI 4140 çeliğini kesme işlemine tabi tutulmuştur. Sertleştrilmiş AISI 4140 çeliğini β-SiAlON kesici takımları ile işlenmesinde yüksek ilerleme ve kesme hızlarında pürüzsüz bir yüzey elde edilmiştir.

Özet (Çeviri)

Keywods : Si3N4, α - β –SiAlON, cutting tools. SiAlON's which is known as silicium aluminium oxy nitride based silicium nitride, is one of the high-tech ceramic materials. This, which can be used in different places, is one of the important ceramics technically. It's made of sintering reaction with alumina (Al2O3), silicium nitride (Si3N4) and aluminium nitride (AlN). The most important features of that are high temperature resistance, corosion resistance at high temperatures, because of their low thermal expansion coefficients comparing to the other ceramics, very good thermal shock resistance, having low density and protecting hardness at high temperatures. Because of this, SiAlON's can be used at places required high hardness and resistance (as cutting components at processing technoogies), at places that high temperature corosion is occured (like turbine components), in producing ball bearing. In this study, it's researched that the performance of using β-SiAlON ceramics that is produced from Si3N4 powders, as a cutting point. With using liquid phase sintering facilitative oxide additives which is made with calculating as for the equality of z=1 at general formul of β-SiAlON, powder compositions had been made. This powder compositions had been conveyed to maximum pure density after being made to the form of cutting point before sintering at 250 MPa pressure at pressing cold isostatic. After that, sintering process of samples at 1450-1750 C, at 30-150 min. waiting moments in high temperature graphite oven in protecting nitrogen atmosphere, had been made. After sintering, density results of samples had been obtained as for Archimed principle. Micro-structure analyses of samples had been got with scanning electron microscope (SEM). With making XRD analyses, Si3N4 phase transformations and approximate α- β rates had been determined. For researching mechanical features of materials, hardness and breaking density rates had been studied. Strength tests had been made under the load of 1 kg at Vickers strength machine. Breaking density tests had been calculated at the same machine with using the formul on crack lengths with technique of Indentation. After that, β-SiAlON cutting tools which is made at this work and WC cutting tools which is used in industry had been subjected to cutting process of AISI 4140 steel which is hardened in the same experiment conditions. High improvement on processing hardened AISI 4140 steel with β-SiAlON cutting tools and a smooth surface had been obtained at cutting forces.

Benzer Tezler

  1. The performance of surface textured SiAlON ceramic cutting tools on turning operation of Inconel 718

    Inconel 718'ı̇n tornalama operasyonunda yüzey dokulu SiAlON seramik kesı̇cı̇ uçların performansı

    KÜBRA GÜRCAN BAYRAK

    Doktora

    İngilizce

    İngilizce

    2023

    Mühendislik BilimleriEskişehir Teknik Üniversitesi

    Malzeme Bilimi ve Mühendisliği Ana Bilim Dalı

    DOÇ. DR. ERHAN AYAS

  2. Cutting tool selection and cutting data optimization for nickel-based superalloys

    Nikel bazlı süperalaşımlar için kesici takım seçimi ve kesme parametrelerinin en iyilemesi

    SEMİH PLATİN

    Yüksek Lisans

    İngilizce

    İngilizce

    1998

    Makine MühendisliğiOrta Doğu Teknik Üniversitesi

    Makine Mühendisliği Ana Bilim Dalı

    PROF. DR. S. ENGİN KILIÇ

  3. Waspaloy süper alaşımının farklı soğutma teknikleri kullanarak frezeleme yöntemi ile işlenebilirliğinin incelenmesi

    Investigation of machinability of Waspaloy super alloy with milling method using different cooling techniques

    ÇAĞRI VAKKAS YILDIRIM

    Doktora

    Türkçe

    Türkçe

    2017

    Makine MühendisliğiDüzce Üniversitesi

    Makine Mühendisliği Ana Bilim Dalı

    PROF. DR. FEHMİ ERZİNCANLI

  4. Trabzon ilinde sporun gelişmesinde etkili olan etnografik faktörlerin ortaya konması

    Başlık çevirisi yok

    HAŞİM ALBAYRAK

    Yüksek Lisans

    Türkçe

    Türkçe

    1994

    SporMarmara Üniversitesi

    Beden Eğitimi ve Spor Ana Bilim Dalı

    YRD. DOÇ. DR. MÜSLÜM BAKIR

  5. Yeni Cami'nin akustik açıdan performans değerlendirmesi

    Evaluation of the acoustical performance of the New Mosque

    EVREN YILDIRIM

    Yüksek Lisans

    Türkçe

    Türkçe

    2003

    Mimarlıkİstanbul Teknik Üniversitesi

    Mimarlık Ana Bilim Dalı

    PROF. DR. SEVTAP YILMAZ DEMİRKALE