Ferritik paslanmaz çeliğin kendi kendine ilerleyen yüksek sıcaklık sentezlenmesi yöntemiyle (SHS-KKIYSS) Ni3Al metallerarası bileşiğin kaplanması
Coating of ferritic stainless steel with Ni3Al intermetallic by self propagating high temperature synthesis (SHS)
- Tez No: 355505
- Danışmanlar: PROF. DR. NİYAZİ ÖZDEMİR
- Tez Türü: Yüksek Lisans
- Konular: Metalurji Mühendisliği, Metallurgical Engineering
- Anahtar Kelimeler: SHS, Ni3Al, kaplama, intermetalik, SHS, Ni3Al, coating, intermetallic
- Yıl: 2014
- Dil: Türkçe
- Üniversite: Fırat Üniversitesi
- Enstitü: Fen Bilimleri Enstitüsü
- Ana Bilim Dalı: Metalurji Eğitimi Ana Bilim Dalı
- Bilim Dalı: Kaynak Eğitimi Bilim Dalı
- Sayfa Sayısı: 97
Özet
Bu çalışmada, AISI 430 Ferritik Paslanmaz Çelik numuneler (SHS: Self Propagating High Temperature Synthesis) Kendi kendine İlerleyen Yüksek Sıcaklık Sentezlemesi (KİYSS) yöntemiyle Ni3Al metallerarası bileşiği ile kaplanarak işlem parametrelerinin ara yüzey mikro yapısı üzerindeki etkileri araştırılmıştır. Ni ve Al tozları (ağırlıkça % 87 Ni ve % 13 Al) olacak şekilde tartılmış ve homojen bir karışım elde etmek için, içerisinde 12 mm çapında seramik bilye olan mekanik bir karıştırıcıda, 16 devir/dk ile 24 saat süreyle karıştırılmıştır. Karıştırılan tozlar daha sonra 12 mm çapında 10 mm kalınlığında paslanmaz çelik numuneler üzerine 1 mm kalınlığında 150, 200, 250 ve 300 MPa' lık basınçlar altında soğuk kompaktlanmıştır. Kompaktlanan numuneler, ön tavlama yapılmaksızın argon atmosferli bir odacıkta, üzerlerinde 40 N' luk bir kuvvet uygulanarak ısıtılmış ve ateşlenmişlerdir. Daha önce yapılan çalışmalarda, ateşleme ve yanma ile eş zamanlı olarak oluşan Ni3Al tabakasının paslanmaz çelik yüzeyine tutunamadığı görüldüğünden, ateşlenen numuneler, pozisyonları değiştirilmeksizin 1000 ve 1100 C sıcaklıklarda 45 dakika süreyle difüzyon işlemine tabi tutulmuşlardır. Bu çalışmanın birinci bölümünde konuya giriş yapılmıştır. İkinci bölümde temel bilgiler sunuldu. Üçüncü bölümde deneysel çalışmanın yöntemine yer verildi, dördüncü bölümde ise deney sonuçları verildi. Beşinci ve son bölümde çalışma sonunda elde edilen genel sonuç ve öneriler verildi.
Özet (Çeviri)
In this thesis, specimens from AISI 430 ferritic stainless steel were coated with Ni3Al intermetallic by Self Propagating High Temperature Synthesis (SHS) method and the effects of process parameters on the microstructures of the coated layer and interface were investigated. With this purpose, Al and Ni powders (1/3 atomic ratio) were mixed homogenously in a mechanical mixer with ceramic balls at 16 rpm for 24 hours. Then the mixed powder, 1 mm in thickness was cold compacted on the stainless steel bars of 1 mm diameter and 10 mm height with the pressures of 150, 200, 250 and 300 MPa. The compacted specimens were ignited in a chamber under argon atmosphere by applying a force of 40 kN. Since it was seen that in situ coating was not possible, the specimens were annealed at 1000 and 1100 C for 45 minutes immediately after ignition. It was concluded that the time and temperatures were enough for a sound interface and coating. In the first chapter of the study, the subject is introduced. In the second chapter a literature research was given on the materials and the method (SHS) itself. In the third chapter, the experimental studies, materials and method were presented. In the fourth chapter the results and in the fifth and last chapter conclusion and recommendations are given.
Benzer Tezler
- Design of a stainless steel composite bridge according to the eurocodes and cost analysis
Paslanmaz çelik ile kompozit bir köprünün eurocode'a göre tasarımı ve maliyet analizi
TİJEN BAYER
Yüksek Lisans
İngilizce
2014
İnşaat Mühendisliğiİstanbul Teknik Üniversitesiİnşaat Mühendisliği Ana Bilim Dalı
YRD. DOÇ. DR. BARLAS ÖZDEN ÇAĞLAYAN
- Ferritik paslanmaz çeliğin yüzey modifikasyonunda metal karbürlerin etkisinin Taguchi metoduyla analizi
The analysis by Taguchi method of the effect of metal carbires on surface modification of ferritic stainless steel
BÜŞRA İÇEN
Yüksek Lisans
Türkçe
2019
Metalurji MühendisliğiFırat ÜniversitesiMetalurji ve Malzeme Mühendisliği Ana Bilim Dalı
DOÇ. DR. ALİ KAYA GÜR
- Ferritik paslanmaz çeliğin korozyon davranışına karbür yapıcı alaşım elementlerinin etkilerinin incelenmesi
The investigation of effects of carbid forming alloying elements on corrosion behaviour of ferritic stainless steel
HÜLYA EREN
Doktora
Türkçe
2005
Metalurji MühendisliğiFırat ÜniversitesiMetalurji Eğitimi Ana Bilim Dalı
Y.DOÇ.DR. TÜLAY YILDIZ
- Martenzitik paslanmaz çelik ve ferritik paslanmaz çeliğin kendileriyle ve biribirleriyle sürtünme karıştırma yöntemi ile kaynak edilebilirliğinin araştırılması
Investigation of weldability of martensitic and ferritic stainless steels with themselves and each other by friction stir welding
ERTUĞRUL ÇELİK
Yüksek Lisans
Türkçe
2006
Makine MühendisliğiFırat ÜniversitesiMetalurji Eğitimi Ana Bilim Dalı
PROF. DR. NURİ ORHAN
- Yüzeyi modifiye edilmiş ferritik paslanmaz çeliğin aşınma direncinin Taguchi metoduyla optimizasyonu
The optimization with Taguchi methods of wear behavior of ferritic stainles stell in surface
SİNAN KAYA
Yüksek Lisans
Türkçe
2017
Metalurji MühendisliğiFırat ÜniversitesiMetalurji Mühendisliği Ana Bilim Dalı
DOÇ. DR. ALİ KAYA GÜR