Investigation of poly(Dimethylsiloxane) additives on polyethylene blend based nanocomposites
Poli(dimetilsiloksan) katkısının polietilen harman matrisli nanokompozitlere etkisinin araştırılması
- Tez No: 363606
- Danışmanlar: PROF. DR. NURSELİ UYANIK
- Tez Türü: Yüksek Lisans
- Konular: Polimer Bilim ve Teknolojisi, Polymer Science and Technology
- Anahtar Kelimeler: Belirtilmemiş.
- Yıl: 2014
- Dil: İngilizce
- Üniversite: İstanbul Teknik Üniversitesi
- Enstitü: Fen Bilimleri Enstitüsü
- Ana Bilim Dalı: Polimer Bilim ve Teknolojisi Ana Bilim Dalı
- Bilim Dalı: Belirtilmemiş.
- Sayfa Sayısı: 114
Özet
Bu çalışmada poli(dimetilsiloksan) (PDMS) katkısının polietilen (PE) harman nanokompozitlerinin morfolojik, termal, yapısal ve mekanik özelliklerine olan etkisi incelenmiştir. Değişik oranlarda alçak yoğunluklu polietilen/metalosen polietilen (AYPE/m-PE) harman matrisli örnekler 27 mm çapında, L/D'si 48 olan çift vidalı ekstrüder ile eriyik karıştırma yöntemiyle hazırlanmıştır. Çalışma sıcaklığı 70-205°C aralığında belirlenmiştir. Onyum iyonlarıyla modifiye edilmiş organokil (Nanomer® I.44P) harmanlara yüzde 5 oranında ilave edilmiştir. Polietilen harmanları ile nanokil arasındaki uyumu sağlamak amacıyla yüzde 15 maleik anhidrit aşılanmış polietilen eklenmiştir. Bunlara ilaveten nanokompozit özelliklerine etkisini araştırmak amacıyla örneklere yüzde 5 ve 10 PDMS katılmıştır. Örneklerin morfolojik, termal, yapısal ve mekanik özellikleri incelenmiştir. Örneklerin gerçek dolgu miktarı kül testi ile belirlenmiştir. XRD sonuçları tabakaları kısmen dağılmış yapılar elde edildiğini göstermiştir. DSC sonuçlarına göre örneklerin kristallenme dereceleri (Xc) artan PDMS miktarı ile azalmaktadır. Bu durum AYPE zengin nanokompozitlerde daha belirgin olarak gözlenmektedir. Tüm örneklerde yüzde 5 ve 10 PDMS ilavesi ile temas açısı değerlerinin sırasıyla %15-20 ile %25-30 arttığı gözlenmiştir. Örneklerin çekme-kopma testleri, Izod darbe dayanımı ve sertlik testlerinin sonuçları PDMS ilavesinin nanokompozitlerin mekanik özelliklerinin önemli ölçüde etkilendiğini ortaya koymuştur.
Özet (Çeviri)
In this study, the effects of the poly(dimethylsiloxane) (PDMS) to the polyethylene (PE) blends nanocomposites were investigated morphologically, thermally, structurally and mechanically. The low density PE/metallocene PE (LDPE/m-PE) blends samples with different compositions were prepared as matrix PE by melt mixing method using co-rotating twin screw extruder with L/D ratio of 48. Processing temperatures were taken between 70-205°C. Onium ions modified organoclay (Nanomer® I.44P) were added as 5 phr to the blends. In order to obtain the compatilibility between polyethylene blends and nanoclay layers, 15 phr maleic anhydride grafted polyethylene was used. In addition to these, 5 and 10 phr PDMS was added to the samples to investigate the effects of PDMS to the properties nanocomposites. Morphological, thermal, structural and mechanical properties of the samples were investigated. Actual filler contents of the samples were determined by ash content tests. XRD results showed that structures between intercalated/exfoliated were obtained. According to DSC analysis, it was observed that degree of crystallinities (Xc) of the samples were decreasing with the increasing amounts of PDMS and this situation is more significant in LDPE rich samples. In all samples, with the addition of 5 and 10 phr PDMS to the clay containing nanocomposites, PDMS increased the contact angle values around 15-20% and 25-30%, respectively. Mechanical characterization results by tensile, Izod impact strength and hardness tests, revealed that the addition of PDMS to the nanocomposites had affected the mechanical properties significantly.
Benzer Tezler
- Polimer esaslı kompozit malzemelere farklı dolgu maddelerinin ilavesinin mekanik ve ısıl özellikleri üzerine etkilerinin incelenmesi
Investigations the effects of different fillers on mechanical and thermal properties of polymer based composite materials
ERKİN AKDOĞAN
Doktora
Türkçe
2019
Makine MühendisliğiPamukkale ÜniversitesiMakine Mühendisliği Ana Bilim Dalı
PROF. DR. NUMAN BEHLÜL BEKTAŞ
- Otomotiv uygulamaları için yüzey özellikleri iyileştirilen polipropilen kompozitlerin hazırlanması ve karakterizasyonu
Preparation of polypropylene composites being cured their surface characteristics for automotive application and it's characterization
NESLİHAN ERGÜN
Yüksek Lisans
Türkçe
2017
Polimer Bilim ve TeknolojisiYalova ÜniversitesiPolimer Mühendisliği Ana Bilim Dalı
PROF. DR. HÜSEYİN YILDIRIM
- The Modification of expandable polystyrene with alpha-methylstyrene and various types of silicones
Köpük polistirenin alfa-metilstiren ve muhtelif tipte silikonlarla modifikasyonu
GÜRKAN SUNAL
Yüksek Lisans
İngilizce
2002
Polimer Bilim ve Teknolojisiİstanbul Teknik ÜniversitesiPolimer Bilim ve Teknolojisi Ana Bilim Dalı
PROF. DR. NURSELİ UYANIK
- Synthesis and characterization of cross-linked poly(Dimethyl Siloxane)nanocomposites
Çapraz bağlı poli(Dimetil Siloksan) nanokompozitlerin sentezi ve karakterizasyonu
YAĞMUR ÇAVUŞOĞLU
Yüksek Lisans
İngilizce
2013
Polimer Bilim ve Teknolojisiİstanbul Teknik ÜniversitesiPolimer Bilim ve Teknolojisi Ana Bilim Dalı
PROF. DR. NURSELİ UYANIK
DOÇ. DR. GÜRALP ÖZKOÇ