İnce film kaplanmış takımlar kullanılarak metal matrisli kompozit levhaların sürtünme karıştırma kaynak tekniği ile birleştirilmesi
Friction stir welding of metal matrix composite sheets by using thin film coated tools
- Tez No: 377260
- Danışmanlar: DOÇ. DR. YAHYA BOZKURT
- Tez Türü: Yüksek Lisans
- Konular: Mühendislik Bilimleri, Teknik Eğitim, Engineering Sciences, Technical Education
- Anahtar Kelimeler: Belirtilmemiş.
- Yıl: 2014
- Dil: Türkçe
- Üniversite: Marmara Üniversitesi
- Enstitü: Fen Bilimleri Enstitüsü
- Ana Bilim Dalı: Metal Eğitimi Ana Bilim Dalı
- Bilim Dalı: Belirtilmemiş.
- Sayfa Sayısı: Belirtilmemiş.
Özet
BU ÇALIŞMADA, YÜKSEK HIZ ÇELİĞİNDEN İMAL EDİLEN TAKIMLAR İLE METAL MATRİSLİ KOMPOZİT LEVHALARIN SÜRTÜNME KARIŞTIRMA KAYNAK YÖNTEMİYLE İLE KÜT ALIN BİRLEŞTİRİLMESİ GERÇEKLEŞTİRİLMİŞTİR. BU TAKIMLAR 3 FARKLI KOMPOZİSYON DADIR; BİRİNCİSİ, HERHANGİ BİR KAPLAMA İŞLEMİ UYGULANMAMIŞ TAKIM, DİGERİ İSE PVD TEKNİĞİ İLE CrN VE ALTIN KAPLANMIŞ OLANLARIDIR. BU ÜÇ FARKLI TAKIMIN, AŞINMA DURUMUNA TAKIM İLERLEME HIZININ ETKİSİ ARAŞTIRILMIŞTIR. SÜRTÜNME KARIŞTIRMA KAYNAK TEKNİĞİYLE BİRLEŞTİRİLEN MMK LEVHALARIN, MEKANİK ÖZELLİKLERİNİ BELİRLEMEK AMACIYLA ÇEKME TESTLERİ YAPILMIŞTIR.DENEYSEL ÇALIŞMALAR SONUCUNDA, TAKIM İLERLEME HIZININ ARTMASIYLA ÇEKME MUKAVEMETİNİN AZALDIĞI VE KARIŞTIRICI UCUN AŞINMA MİKTARININ ARTTIĞI BELİRLENMİŞTİR. BU ETKENLERE BAĞLI OLARAK, METAL MATRİSLİ KOMPOZİT LEVHALARIN KAYNAK PERFORMANSI YÜKSEK TAKIM DÖNME HIZLARINDA; KAPLAMASIZ TAKIM İLE YAPILAN BİRLEŞTİRMELERDE %63.5, CrN KAPLI TAKIMDA %72.3 VE ALTIN KAPLI TAKIMDA İSE %74 OLARAK BELİRLENMİŞTİR.
Özet (Çeviri)
In this study, friction stir butt welding of metal matrix composite sheets was performed with tools made of high speed steel. These tools are at 3 different compositions. First of them, a coating process is not applied, the other tools CrN and Altın are coatde by PVD process. Wear condition of these 3 tools were investigated on the effect of tool traverse speed. Ultimate tensile tests were conducted in order to determine the mechanical properties of metal matrix composite sheets joined by friction stir welding technique. In the result of experimental studies, tensile strength was decreased with increasing of the tool traverse speed and the amount of wear the tool pin was increased. Depending on these factors, the joining performance of metal matrix composite sheets was determinated in high tool traverse speed as 63.5%, 72,3% and 74% with uncoated, CrN coated and AlTIN coated tool, respectively.
Benzer Tezler
- Kuyruk modelleri ve analizi üzerine bir uygulama
Başlık çevirisi yok
DİDEM ÖZPULAT
Yüksek Lisans
Türkçe
1985
İstatistikEge ÜniversitesiBilgisayar Bilimleri ve Mühendisliği Ana Bilim Dalı
DOÇ. DR. FİKRET İKİZ
- Dokuma kumaşlarda örgü tipinin ham kumaşın boyutları ve geometrik özellikleri üzerindeki etkilerinin araştırılması
Başlık çevirisi yok
EMEL ÖNDER
Yüksek Lisans
Türkçe
1985
Tekstil ve Tekstil MühendisliğiEge ÜniversitesiTekstil Mühendisliği Ana Bilim Dalı
DOÇ. DR. GÜNGÖR BAŞER
- Ege bölgesi keçi liflerinin bazı önemli fiziksel, kimyasal özellikleri ve değerlendirme imkanları
Başlık çevirisi yok
NİLÜFER ERDEM
Doktora
Türkçe
1985
Tekstil ve Tekstil MühendisliğiEge ÜniversitesiTekstil Mühendisliği Ana Bilim Dalı
PROF. DR. GÜLSEREN YAZICIOĞLU