Sürekli döküm tandişinde bindirme yapılan slab dökümler için tonaj, kalite belirleme çalışması

Study of slab quality and tonnage determination for overlapping heats in a continuous casting tundish

PDF İndir

  1. Tez No: 389240
  2. Yazar: AYŞE ORAN
  3. Danışmanlar: DOÇ. DR. CEVAT BORA DERİN
  4. Tez Türü: Yüksek Lisans
  5. Konular: Metalurji Mühendisliği, Metallurgical Engineering
  6. Anahtar Kelimeler: Belirtilmemiş.
  7. Yıl: 2015
  8. Dil: Türkçe
  9. Üniversite: İstanbul Teknik Üniversitesi
  10. Enstitü: Fen Bilimleri Enstitüsü
  11. Ana Bilim Dalı: Metalurji ve Malzeme Mühendisliği Ana Bilim Dalı
  12. Bilim Dalı: Belirtilmemiş.
  13. Sayfa Sayısı: 149

Özet

Çelik, ana metali demir olan ve kütlece %2'den daha az karbon ve ilave alaşım elementleri içeren malzemedir. Çeliğin geniş kullanım alanı, sıcak ve soğuk şekillendirmeye uygunluğu, kaynak edilebilirliği, işlenebilirliği, sert, sünek ve aşınma dayanımlı olması, korozyon dayanımı, yüksek sıcaklıklarda ısıya ve deformasyona dayanımı onu vazgeçilmez kılmaktadır. Dolayısıyla da bugünün ve yarının endüstrisinde sürdürülebilir gelişmenin ana direklerinden biri olarak yerini korumaktadır. Kullanım alanları hemen hemen her mühendislik dalına uzanmaktadır. Günümüzde cevherden çelik üretiminde kullanılan iki ana işlem vardır. Bunlar, demir cevherinin sıcak metale (sıvı) redüklenmesi veya doğrudan demire redüklenmesi (DRI-direct reduced iron), diğer adıyla sünger demir (sponge iron) üretimidir. Günümüzde çeliğin rafinasyonunda ise iki yöntem takip edilmektedir. Bunlar; • Yüksek fırın-konverter yöntemi, • Elektrik ark fırını yöntemidir. Yüksek fırında, demir cevheri ile birlikte redükleyici olarak kok veya kömürün kullanılması ile sıvı ham demir elde edilir ve bu ergiyik, bazik oksijen fırınında işlenir, rafine edilir. Elektrik ark fırınlarında ise ısı ve ergitme için gerekli enerji, elektrik enerjisi ile elde edilir. Genellikle hurda ve sünger demirin birlikte kullanıldığı fırınlar olarak nitelendirilebilir. Ardından ikincil metalurji işlemleri (pota fırınları, vakum vb.) çeliğe uygulanır. Çelik işletmelerindeki ikincil metalurji işlemlerinden gelen sıvı metal belli şekil, ölçü ve ağırlıklara göre dökülür. Döküm prosesleri aşağıdaki şekilde gruplandırılabilir; • Sürekli Döküm, • Şerit Döküm, • İngot Döküm Dünya genelinde en çok kullanılan döküm yöntemi“Sürekli Döküm”yöntemidir ve kullanım oranı %90'a kadar yükselmiştir. Ayrıca sürekli döküm, %95'den fazla verim, üniform katılaşma, hızlı döküm, az sayıda üretim aşaması avantajlarını sağlamaktadır. Çelik üretim proseslerinde rafine edilen sıvı metal, potadan tandiş vasıtasıyla sürekli dökümün ekipmanlarından olan metal kalıplara dökülmektedir. Tandiş ergimiş metalin kalıplara dökülüp katılaşmanın başlamasından hemen önce muhafaza edildiği son metalurjik kanaldır. Tabanında bir veya bir kaç delik bulunan bir konteyner biçimindedir ve ergimiş metalin kalıplara doğru beslenmesi görevini görmekte, ergimiş metal akışının sıçramalar olmadan daha pürüzsüz akışını sağlamaktadır. Birçok fabrikada uygulaması olduğu gibi Çolakoğlu Metalurji A.Ş. fabrikasında da satış siparişlerinin tonaj, kalite, ebat (slab genişliği) özelliklerinin çelikhane üretim koşullarını optimize etmeye uygun olmaması durumlarında farklı kaliteler aynı tandiş için planlanmakta ve dökümü yapılmaktadır. Bu uygulama sonucunda iki farklı döküm kalitesinin tandişte karışması durumu ortaya çıktığından ve bu karışımın başlangıç ve bitiş sınırları ile kimyasal kompozisyonu bilinmediğinden“Sürekli Döküm Tandişinde Bindirme Yapılan Slab Dökümler için Tonaj, Kalite Belirleme Çalışması”adı altında bir modelleme yapılmıştır. Bu çalışma ile bindirme döküm uygulaması sonucunda karışan kalitelerin sınırları belli edilmiş, kimyasal kompozisyonu bulunmuştur. Böylece esas kalitelerden saptırılacak slabların standartlara göre boylarına ve döküm kalitesi isimlerine karar verilmesine imkan sağlanmıştır. Özet olarak, bu çalışmanın amacı iki farklı kalitenin aynı tandişte bindirilmesi neticesinde arada karışan kalitenin başlangıç ve bitiş sınırlarının belirlenmesi ve böylece bindirme slab olarak ayrılması gereken toplam tonajın hesaplanması, bu tonaja göre en uygun slab boylarının bulunması ve ayrılan ilgili slab ya da slabların kalitelerinin belirlenmesidir. Modelleme çalışmasının doğruluğunun kontrolü açısından bazı bindirme işlemleri sonucunda tamamen tahmine ve deneyime dayalı olarak“bindirme ara slabı”adı altında esas kaliteden saptırılan slabların baş-orta-son kısımlarından birer adet numune alınmıştır ve analiz sonuçları modelleme çalışmasında elde edilenler ile kıyaslanmıştır. Neticede elde edilen bulgularda ve grafiklerde gerçek analiz sonuçları ile modelleme programının sonuçlarının analiz cihazından, kompozisyon % aralık hassasiyetinden, dökümde oluşabilen sorunlardan kaynaklı olabilecek bazı sapmalar haricinde birbirlerine oldukça yakın olduğu tespit edilmiştir. Mevcut durumda Çolakoğlu Metalurji A.Ş. fabrikasında bindirme slabların kalite isimlendirmesi, tonaj ve boylarının belirlenmesi tamamen tahminlere ve deneyimlere dayanılarak yapılmaktadır. Bu çalışma ile Çolakoğlu Metalurji A.Ş.'de bindirme dökümler konusunda tahmini veriler ile çalışmak yerine daha gerçekçi sonuçlarla çalışılmasına imkan sağlanmıştır.

Özet (Çeviri)

Steel is an alloy of iron and carbon that is widely used in construction and other applications because of its high tensile strength and low cost. Carbon, other elements, and inclusions within iron act as hardening agents that prevent the movement of dislocations that naturally exist in the iron atom crystal lattices. The carbon in typical steel alloys may contribute up to 2.1% of its weight. Steel is irrevocable material because of its wider usage area, possibility for hot and cold forming, weld ability, hard, ductile, abrasion resistance features, corrosion resistance, heat and deformation resistance at high temperatures. So that, its usage area could reach variety of engineering subjects. It is common today to talk about“the iron and steel industry”as if it were a single entity, but historically they were separate products. The steel industry is often considered an indicator of economic progress, because of the critical role played by steel in infrastructural and overall economic development. Contemporarily, there are two main methods to produce a steel from iron ore. First one is reduction of iron ore to liquid and warm metal and the other one is reduction to directly iron (DRI-direct reduced iron) in different name sponge iron. In the present day, two common ways are followed to produce and refine the steel as mentioned below. • Blast furnace-converter method, • Electric arc furnace method. In a blast furnace, fuel, ore, and flux (limestone) are continuously supplied through the top of the furnace, while a hot blast of air (sometimes with oxygen enrichment) is blown into the lower section of the furnace through a series of pipes called tuyeres, so that the chemical reactions take place throughout the furnace as the material moves downward. The end products are usually molten metal and slag phases tapped from the bottom, and flue gases exiting from the top of the furnace. The downward flow of the ore and flux in contact with an up flow of hot, carbon monoxide-rich combustion gases is a countercurrent exchange process. Liquid raw iron is gained by using coke and coal as reduction material in a blast furnace and relevant liquid raw iron is refined in a basic oxygen furnace. In an electric arc furnace, the energy and heat to gain molten steel are provided from electric energy. Generally speaking, electric arc furnace is known as it uses both scrap and sponge iron. The electric arc furnace operates as a batch melting process producing batches of molten steel known“heats”. The electric arc furnace operating cycle is called the tap-to-tap cycle and is made up of the following operations: • Furnace charging • Melting • Refining • De-slagging • Tapping • Furnace turn-around After the electric arc furnace process, secondary metallurgy processes begin (ladle furnace, vacuum degasser etc.) for molten steel. The molten steel that was processed in secondary metallurgy is casted through the tundish to the molds considering to sales order requirements for shape, dimension and weight. Casting processes are classified as follows; • Continues casting, • Band casting, • Ingot casting. The most common casting method in the world is“Continues Casting”and its application ratio raised up to approximately %90. Continues casting provides more than %95 efficiency, uniform solidification, faster casting speed etc. In a process of continues casting, tundish is the last metallurgical channel to cover and accommodate the melted steel before pouring to the molds and permitting to begin the solidification. There are one or more than one holes at the bottom of tundish and they let to feed the mold with hot steel. In addition, tundish mechanism provides smooth pouring of hot steel. As a common application for many companies in the world and Çolakoğlu Metalurji A.Ş., slab or billet heats which has different quality names so different chemical compositions are produced in the same tundish during continues casting process in case of the tonnage, quality, dimensions (slab width) unsuitableness to optimize the steel plant's production conditions. At the end of relevant application, two different qualities are mixed, overlapped in the same tundish and the borders of this overlapped slab mixing are unknown. So that, because there is a requirement to know the borders and the new chemical composition of relevant mixing steel,“Study of slab quality and tonnage determination for overlapping heats in a continuous casting tundish”work has been done in this thesis. In addition, this study permits to decide the cast id name (quality name) according to Çolakoğlu Metalurji A.Ş. quality and chemical compositions standards and slab lengths according to Çolakoğlu Metalurji A.Ş. slab dimension standards. In practical case, people in Çolakoğlu Metalurji A.Ş. separate overlapped slabs from original heats with their experience and guess without any measurement, calculation and chemical analysis tests. To wrap up, the main purpose of this study is to clarify the quality borders of overlapped slabs so that to calculate the overlapped slab's tonnage and most suitable slab lengths according to the tonnage though. In addition, the main purpose of this study is to name the overlapped slab quality. In order to control the chemical results of relevant modelling study, 3 pieces from head, middle and tail were taken from the overlapped slab that was separated with experiences by Çolakoğlu Metalurji A.Ş. employees. Then 3 different samples from head, middle and tail of overlapped slabs and 3 different chemical analysis were gained from mass spectrometer of Çolakoğlu Metalurji A.Ş. and viewed the change of chemical compositions step by step from head to tail. Then same conditions were entered (the name of overlapped qualities, dimensions etc.) to the modelling study and viewed the results. At the end, results were compared with each other in tables, graphs. Eventually, relevant results of modelling study that has been already compared with experimental results are quite successful except small and negligible deviations. Basically, this study provides opportunity to work with more reliable result instead of the result based on guess and experiments about overlapped heats in Çolakoğlu Metalurji A.Ş. plant.

Benzer Tezler

  1. Tez No

    910475

    Kord teli uygulamalarına yönelik çeliklerin üretim ve sürekli döküm proses parametrelerinin optimizasyonu

    Optimization of production and continuous casting process parameters of steels for cord wire applications

    İLKER AYÇİÇEK

    Doktora

    Türkçe

    Türkçe

    2024

    Metalurji Mühendisliğiİstanbul Teknik Üniversitesi

    Metalurji ve Malzeme Mühendisliği Ana Bilim Dalı

    DR. ÖĞR. ÜYESİ NURİ SOLAK

  2. Tez No

    481433

    Cumhuriyet Dönemi Türk romanında Osmanlıya bakış (1920-1970)

    The overview to Ottoman in Republican period Turkish novel (1920-1970)

    TAYFUN BARIŞ

    Doktora

    Türkçe

    Türkçe

    2017

    Türk Dili ve EdebiyatıUludağ Üniversitesi

    Türk Dili ve Edebiyatı Ana Bilim Dalı

    PROF. DR. ALEV SINAR UĞURLU

  3. Tez No

    426686

    Mezenkimal tümörlerin tanı ve ayırıcı tanısında yeni immünohistokimyasal belirleyicilerin öneminin değerlendirilmesi

    The evaluation of importance of new immunohistochemical markers for the diagnosis and differantial diagnosis of mesenchymal tumors

    SEVİL KARABAĞ

    Tıpta Uzmanlık

    Türkçe

    Türkçe

    2016

    PatolojiÇukurova Üniversitesi

    Tıbbi Patoloji Ana Bilim Dalı

    PROF. DR. GÜLFİLİZ GÖNLÜŞEN

  4. Tez No

    138601

    Kronik pelvik ağrı tanısında renkli doppler ultrasonografinin yeri ve tedavide flavinoidlerin etkinliğinin değerlendirilmesi

    Başlık çevirisi yok

    NURTEN GÜRSOY

    Tıpta Uzmanlık

    Türkçe

    Türkçe

    2001

    Kadın Hastalıkları ve Doğumİnönü Üniversitesi

    Kadın Hastalıkları ve Doğum Ana Bilim Dalı

    DOÇ. DR. AYŞE KAFKASLI

  5. Tez No

    838459

    Ektopik gebelik ve rüptüre ektopik gebelik tanısında bir belirteç olarak DNI'nin yeri var mı?

    Does DNI have a place as a marker in the diagnosis of ectopic pregnancy and ruptured ectopic pregnancy?

    MEHMET CAN YAŞAR

    Tıpta Uzmanlık

    Türkçe

    Türkçe

    2023

    Kadın Hastalıkları ve DoğumSağlık Bilimleri Üniversitesi

    Kadın Hastalıkları ve Doğum Ana Bilim Dalı

    DOÇ. DR. RAHİME BEDİR FINDIK

Geri Dön