Çinko borat maddesinin odun plastik kompozitlerde antifungal etkisinin incelenmesi

Investigation of antifungal effect of zinc borat compound on wood plastic composites

  1. Tez No: 423833
  2. Yazar: ESRA YILMAZ
  3. Danışmanlar: YRD. DOÇ. ERTUĞRUL ALTUNTAŞ
  4. Tez Türü: Yüksek Lisans
  5. Konular: Ağaç İşleri, Biyoloji, Mikrobiyoloji, Wood Products, Biology, Microbiology
  6. Anahtar Kelimeler: Belirtilmemiş.
  7. Yıl: 2016
  8. Dil: Türkçe
  9. Üniversite: Kahramanmaraş Sütçü İmam Üniversitesi
  10. Enstitü: Fen Bilimleri Enstitüsü
  11. Ana Bilim Dalı: Orman Endüstri Mühendisliği Ana Bilim Dalı
  12. Bilim Dalı: Belirtilmemiş.
  13. Sayfa Sayısı: 99

Özet

Bu çalışmada, çinko borat katkılı odun plastik kompozit (OPK) malzemenin oduna arız olabilen bazı çürüklük mantarlarına (Trametes versicolor, Coniophora puteana, Postia placenta) karşı dayanımı araştırılmıştır. OPK örnekleri %50, %60 ve %70 oranlarında değişen sarıçam odun unu, HDPE ve katkı maddeleri ile ikiz vidalı ekstruder kullanılarak üretilmiştir. Bazı formülasyonlarda uyumsuzluk gidermek amacıyla MAPE kullanılmıştır. Ekstrüzyondan elde edilen granül malzemeler sıcak preste levha haline getirilerek bu levhalardan standartlara uygun test örnekleri hazırlanmıştır. Üretilen kompozit örneklerinin mekanik (eğilme, çekme ve şok direnci), biyolojik bozunurluk, yüzey sertliği testleri ile termal (TGA/DTA), ATR-FTIR ve SEM analizleri yapılarak özellikleri belirlenmiştir. Sonuçlara göre genel olarak odun unu oranı arttıkça OPK örneklerinin mekanik değerlerinin azaldığı ancak elastikiyet modülünün arttığı saptanmıştır. Ayrıca OPK içine eklenen MAPE takviyesinin malzemenin özelliklerini iyileştirdiği tespit edilmiştir. Biyolojik bozunurluk test sonuçları incelendiğinde odunun unu oranının artması ile malzemenin ağırlık kayıbının önemli ölçüde arttığı gözlemlenmiştir. Ancak OPK örneklerine çinko borat maddesinin eklenmesi ile ağırlık kayıplarının %12'lerden %2'lere düştüğü görülmüştür. Biyolojik bozunmanın etkisiyle örneklerin yüzey sertlik değerlerinde de düşüş olmuştur. Ayrıca farklı sürelerde mantara maruz kalan OPK örneklerinde odun unundan kaynaklı kimyasal değişimlerin meydana geldiği FTIR analizleri ile tespit edilmiştir. Mantar çürüklüğü sonrası malzemedeki odunun termal özelliklerinde de değişimlerin olduğu TGA/DTA analizleri ile de gösterilmiştir. Son olarak SEM görüntüleri çürüklük mantarlarının OPK yüzeyinde değişimlere neden olduğunu göstermiştir.

Özet (Çeviri)

In this study, the resistance of zinc borate reinforced wood plastic composite (WPC) materials against to some wood-rot fungi (Trametes versicolor, Coniophora puteana, Postia placenta) was investigated. WPC samples containing 50%, 60% and 70% wood flour, HDPE and additives were manufactured by using a twin-screw extruder. In some formulations, MAPE was used as coupling agent to prevent the unconformity. Extruded WPC granules were converted into plates via a hot press and test specimens were prepared from these plates according to the standarts. The properties of the WPC specimens were determined by using mechanical (flexural, tensile and shock resistance), biodegradability and surface hardness tests along with thermal (TGA/DTA), ATR-FTIR and SEM analyzes. According to the results in general as the amount of wood flour ratio increased mechanical properties of WPC specimens decreased, however the modulus of elasticity increased. Moreover, it was also found that the addition of MAPE improved the properties of WPC samples. Biodegradability test results showed that when the wood flour ratio increased the weight loss of the WPC samples was significaly increased. However, the addition of zinc borate material into formulations reduced the the weight loss of the samples from around 12% to 2%. The surface hardness values decreased due to biological degradation of samples. Furthermore, in the samples exposed to the fungal attack for various times some chamical changes were determined via FTIR analysis originating from the wood flour. After the fungal decay tests the alterations in the thermal properites of wood flour in the material were also shown through TGA/DTA analyses. Finally, SEM images were showed that the rot fungi caused changes on the surface of WPC.

Benzer Tezler

  1. Çinko borat katkılı polimer kompozit zırh malzemelerin üretilmesi ve özelliklerinin incelenmesi

    Production of zinc borate reinforcement polymer composite shielding materials and determination of their properties

    TOYGAR ÇARDAK

    Yüksek Lisans

    Türkçe

    Türkçe

    2023

    EnerjiBursa Teknik Üniversitesi

    Enerji Sistemleri Mühendisliği Ana Bilim Dalı

    PROF. DR. SONGÜL AKBULUT ÖZEN

  2. Nano boyutlu çinko borat sentezinde reaksiyon koşullarının etkisi

    The effect of reaction conditions in synthesis of zinc borate in nanoscale

    YEŞİM İNAN

    Yüksek Lisans

    Türkçe

    Türkçe

    2012

    Kimya Mühendisliğiİstanbul Teknik Üniversitesi

    Kimyasal Teknolojiler Ana Bilim Dalı

    PROF. DR. HALE GÜRBÜZ

  3. Alev geciktirici polimer kompozitlerin ekstrüzyon yöntemi ile hazırlanması ve karakterizasyonu

    Preparation and characterization of flame retardant polymer composites through extrusion method

    AYKUT YÜCESOY

    Yüksek Lisans

    Türkçe

    Türkçe

    2017

    Mühendislik BilimleriYıldız Teknik Üniversitesi

    Metalurji ve Malzeme Mühendisliği Ana Bilim Dalı

    YRD. DOÇ. DR. HALE BERBER YAMAK

  4. Effect of rare earth elements addition on magnetic properties of nickel-zinc ferrites

    Nadir toprak elementleri ilavesinin nikel-çinko ferritlerin manyetik özelliklerine etkisi

    KADİR BORA DEMİREL

    Yüksek Lisans

    İngilizce

    İngilizce

    2024

    Metalurji Mühendisliğiİstanbul Teknik Üniversitesi

    Metalurji ve Malzeme Mühendisliği Ana Bilim Dalı

    DR. ÖĞR. ÜYESİ NURİ SOLAK

  5. Değişik özelliklerdeki ZnO kristallerinin brillant black boyar maddesinin bozundurulmasına fotokatalitik etkisinin incelenmesi

    Investigation of the photocatalytic effect of ZnO crystals with different properties on the degradation of brillant black dyes

    HANİM ESRA SAĞLAM

    Yüksek Lisans

    Türkçe

    Türkçe

    2021

    Kimya MühendisliğiÇankırı Karatekin Üniversitesi

    Kimya Mühendisliği Ana Bilim Dalı

    DR. ÖĞR. ÜYESİ MUHAMMED BORA AKIN