Farklı sentez koşullarında sıfır değerlikli demir nanopartikül üretimi, optimizasyonu ve tekstil boyar maddelerinin giderimine uygulanması
Production of zero valent iron nanoparticles at different synthesis conditions, optimization and application for the textile dyes removal
- Tez No: 427728
- Danışmanlar: DOÇ. DR. MERAL TURABİK
- Tez Türü: Yüksek Lisans
- Konular: Kimya, Kimya Mühendisliği, Tekstil ve Tekstil Mühendisliği, Chemistry, Chemical Engineering, Textile and Textile Engineering
- Anahtar Kelimeler: Belirtilmemiş.
- Yıl: 2015
- Dil: Türkçe
- Üniversite: Mersin Üniversitesi
- Enstitü: Fen Bilimleri Enstitüsü
- Ana Bilim Dalı: Nanoteknoloji ve İleri Malzemeler Ana Bilim Dalı
- Bilim Dalı: Belirtilmemiş.
- Sayfa Sayısı: 148
Özet
Sıfır değerlikli demir nano partikül(SDDNP) çevresel ve diğer uygulamalarda etkin bir malzeme olarak artan bir şekilde dikkat çekmektedir. Bu çalışmada, SDDNP demir(III)'ün borhidrür ile indirgenmesi yöntemi kullanılarak hazırlanmıştır. SDDNP üretimi farklı demir konsantrasyonu, borhidrür konsantrasyonu, stabilizer konsantrasyonu, borhidrür ilave hızı ve reaksiyon ortamının karıştırma hızı gibi farklı koşullarda gerçekleştirilmiştir. Bu parametrelerin tane boyutuna etkisini değerlendirmek için ANOVA istatistiksel model kullanılmıştır. Partikül boyutu ve boyut dağılımı Zeta sizer cihazı ile belirlenmiştir. SDDNP'nin yüzey bileşimi ve özellikleri SEM, EDX, XRF, XRD ve FTIR ile saptanmıştır. Ayrıca BET yüzey alanı ve izo elektrik nokta ölçümü yapılarak sırasıyla 7,79 m2/g ve pH 8,5 olarak bulunmuştur. Optimum koşullarda sentezlenen SDDNP tane boyutu 10-40 nm aralığında saptanmıştır. İkisi de azo grubu tekstil boyarmadde olan Asit Red 42 (AR42) ve Bazik Red 18'in sulu çözeltilerinden, optimum koşullarda sentezlenmiş SDDNP üzerine adsorpsiyonu kesikli sistemde incelenmiştir. SDDNP'in adsorpsiyon kapasitesi farklı başlangıç boyarmadde konsantrasyonu, SDDNP konsantrasyonu, pH, sıcaklık ve karıştırma hızlarında incelenmiştir. Box Behnken Dizaynı(BBD) ve cevap yüzey yöntemi (RSM) bu koşulların birlikte etkilerini gözlemek amacıyla adsorpsiyon deneylerinin dizaynı için uygulanmıştır. İki izoterm model denge verilerine uygulanmış ve Langmuir izoterm modelinin Freundlich izoterm modelinden daha iyi uyum sağladığı görülmüş ve SDDNP üzerinde tek tabaka tutunum kapasitesi AR42 ve BR18 için sırasıyla 972 ve 633 mg/g olarak saptanmıştır. Ayrıca SDDNP üzerine AB42 ve BR18 adsorpsiyon prosesinin yalancı birinci mertebe kinetik modele oldukça iyi uyduğu belirlenmiştir. Termodinamik sonuçlar iki boyanın SDDNP üzerine adsorpsiyonunun egzotermik ve kendiliğinden olduğunu göstermiştir.
Özet (Çeviri)
Zero valent iron nano particle (nZVI) is increasingly gaining attention as an efficient material for environmental and other applications. In this study, nZVI was prepared using the ferric iron reduction method by borohydride. The production of nZVI were carried out different synthesis condition such as ferric iron concentration, borohydride concentration, stabilizer concentration, adding speed of borohydride and stirring speed of reaction medium. The ANOVA statistical modeling was performed to evaluate the effect of these conditions to particle size. Particle size and size distribution were determined by Zeta sizer apparatus. Surface composition of nZVI samples were characterized by SEM, EDX, XRF, XRD and FTIR. BET surface area and iso-electric point (IEP) were also measured and found as 7,79 m2/g and pH 8,5 respectively. The size of nZVI particles synthesized at optimal conditions was predominantly within the range of 10–40 nm. The adsorption of two azo textile dyes aqueous solutions, Acid Red 42(AR42) and Basic Red (BR18), onto nZVI that sythesized at optimal condition were also investigated in a batch mode. Dye adsorption capacity of nZVI was tested under various experimental conditions like initial dye concentration, nZVI concentration, pH, temperature and agitation rate of reaction medium. The Box Behnken Dizaynı(BBD) and response surface methodology(RSM) were applied in designing the adsorption experiments for evaluating the interactive effects of these condition. Two Isotherm models were applied to equilibrium data and the results showed that Langmuir isotherm model more suitable than Freundlich model and maximum monolayer coverage capacities of nZVI for AR42 and BR18 were found as 972 and 633 mg/g, respectively. It was also determined that the processes of AB42 and BR18 adsorption onto nZVI well fitted to pseudo first order kinetic model. Thermodynamic reults showed that the two dyes adsorption onto nZVI were exothermic and spontaneous in nature.
Benzer Tezler
- Design of boron doped (nickel manganese cobalt containing) NMC 811 cathode active materials
Bor katkılanmış (nikel mangan kobalt içeren) NMC811 katot aktif malzemelerinin tasarımı
İBRAHİM CAN TOPAKTAŞ
Yüksek Lisans
İngilizce
2024
Metalurji Mühendisliğiİstanbul Teknik ÜniversitesiMetalurji ve Malzeme Mühendisliği Ana Bilim Dalı
PROF. DR. ÖZGÜL KELEŞ
- Development of nano-alloyed CdTeS quantum dots via two-phase synthesis method
İki faz yöntemiyle nano-alaşım CdTeS kuantum noktacıklarının sentezi
SACİDE MELEK KESTİR
Yüksek Lisans
İngilizce
2022
Bilim ve Teknolojiİstanbul Teknik ÜniversitesiNanobilim ve Nanomühendislik Ana Bilim Dalı
DOÇ. DR. CANER ÜNLÜ
- Bazı nanoparçacıkların sentezi ve manyetik özelliklerinin belirlenmesi
Synthesis of some nanoparticles and determination of their magnetic properties
MUSTAFA COŞKUN
Doktora
Türkçe
2010
Fizik ve Fizik MühendisliğiHacettepe ÜniversitesiFizik Mühendisliği Ana Bilim Dalı
PROF. DR. MUSTAFA KORKMAZ
PROF. DR. TEZER FIRAT
- Grafen oksit katkılı nanokompozitlerin elektrokimyasal ve optik biyosensör platformu olarak kullanılması
Graphene oxide based nanocomposites electrochemical and optical biosensing platforms
BAŞAK BÜYÜK
Yüksek Lisans
Türkçe
2023
Bilim ve Teknolojiİzmir Katip Çelebi ÜniversitesiNanobilim ve Nanoteknoloji Ana Bilim Dalı
DR. ÖĞR. ÜYESİ SEMA DEMİRCİ UZUN
- Multiscale modeling and study on the exfoliation and electronic properties of functionalized graphene analogs
Fonksiyonlaştırılmış grafen analoglarının yapraklanması ve elektronik özellikleri üzerine çok ölçekli modelleme
BERKAY SÜTAY
Doktora
İngilizce
2016
Kimyaİstanbul Teknik ÜniversitesiFizikokimya Ana Bilim Dalı
PROF. DR. MİNE YURTSEVER