Kitosan-ko-Hyaluronik asit kriyojellerinin hazırlanması ve karakterizasyonu
Prepation and characterization of chitosan-co-Hyaluronic acid cryogels
- Tez No: 441739
- Danışmanlar: PROF. DR. NİLHAN KAYAMAN APOHAN
- Tez Türü: Yüksek Lisans
- Konular: Kimya, Chemistry
- Anahtar Kelimeler: Belirtilmemiş.
- Yıl: 2016
- Dil: Türkçe
- Üniversite: Marmara Üniversitesi
- Enstitü: Fen Bilimleri Enstitüsü
- Ana Bilim Dalı: Kimya Ana Bilim Dalı
- Bilim Dalı: Organik Kimya Bilim Dalı
- Sayfa Sayısı: 112
Özet
Hidrojeller; hidrofilik homopolimerler veya kopolimerlerden oluşan çapraz bağlı polimerik ağ yapılardır ve bu yapıların hidrofilik gruplardan dolayı suya karşı yüksek ilgileri vardır. Suda belli bir denge hacmine kadar şişerler fakat orijinal şekillerini korurlar. Hem doğal hem de sentetik polimerlerden hazırlanabilmektedirler. Hidrojeller, biyolojik sıvılarda biyouyumluluk gösterirler. Biyoteknolojide önemli bir potansiyele sahip polimerik jellerin yeni tiplerinden birisi de 'kriyojeller' dir. Kriyojeller; ozmotik, kimyasal ve mekanik kararlılıkları nedeniyle biyolojik uygulamalarda önem kazanmışlardır. Kriyojellerin oluşumu çözücünün donma noktasının altında gerçekleşir. Böylelikle zamanla çözücünün büyük bir kısmı donup birbirine bağlı buz kristalleri oluştururken, bu buz kristallerinin etrafında donmamış sıvıda bulanan polimer öncülleri polimerleşerek buz kristallerinin etrafında bir ağ yapı oluştururlar. Donmuş çözücü kristalleri gözenek oluşturucu ajan olarak görev yapar. Polimerleşmeden sonra donmuş karışım oda sıcaklığına getirildiğinde buz kristalleri erir ve makrogözeneklere sahip polimer ağ yapı elde edilir. Bu tez çalışmasında kitosan-ko-hyaluronik asit kriyojellerinin doku mühendisliği uygulamasında yapı iskelesi (scaffold) olarak kullanılabilirliği araştırıldı. Bu nedenle çalışmada kitosan-ko-hyaluronik asit kriyojelleri sentezlendi. Çapraz bağlayıcı olarak glutaraldehit kullanıldı. Kopolimerler, hyaluronik asitin farklı konsantrayonları (ağırlıkça %0, %10, %20, %30, %50) kullanılarak elde edildi. Bu çalışma ile saf kitosandan elde edilen kriyojellerin, hyaluronik asitin farklı konsantrayonlarda kopolimerleri yapılmasıyla mekanik ve biyomalzeme özellikleri iyileştirildi ve doku iskelesi olarak kullanılmaları ile hücre uyumluluklari incelendi. Elde edilen kriyojellerin yapı karakterizasyonu Infrared spektroskopisi ile yapıldı. Morfolojik yapısına SEM analizi ile bakıldı. Termal analizleri DSC ve TGA ile incelendi ve şişme davranışı takip edildi. MTT testi ile ekilen 3T3 fibroblast ve SAOS-2 hücrelerinin canlılığı takip edildi.
Özet (Çeviri)
Hydrogels are crosslinked polymer networks which consists of hydrophilic homo or copolymer and they show high affinity to water due to its hydrophilic structure. They swell to a maximum equilibrium swelling value but they don't lose their original form. They can be synthesized with both natural and synthetic polymers. Hydrogels shows biocompability in biological liquids. Cryogels are considered as a new type of polymeric gel which have significant potential in the area of biotechnology. Cryogels gained prominence in biologic applications due to their osmotic properties and chemical-mechanical stability. Cryogel formation is carried out under the tempeture of freezing point of the solvent. Therefore, while a interconnected structure is formed by the crystallization of solvent due to freezing of solvent, a network is formed around these frozen structure by polymerization of precursors. The frozen solvent crystals play role as a pore forming agents. After the polymerization, frozen solvent melts when the frozen mixture is warmed up to room temperature thus an interconnected macroporous polymer network is obtained. In this thesis work, the usability of chitosan-co-hyaluronic acid cryogels as a tissue engineering scaffold was investigated. Firstly, chitosan-co-hyaluronic acid cryogels were synthesized. Glutaraldehyde was used as a crosslinker. Several different composition of this copolymer was synthesized (0 wt %, 10 wt %, 20 wt %, 30 wt %, 50 wt %) In this work the mechanical and biomaterial properties of pure chitosan was improved by making copolymer with hyaluronic acid in different concentration and it was investigated that their application as a scaffold in tissue engineering and cell biocompability . Chemical structure of cryogels analised by Infrared Spectroscopy. Morphology of cryogels was investigated by SEM technique. Thermal properties of cryogels were investigated by DSC and TGA. Also swelling ratio of cryogels were measured. The cell viablity of 3T3 fibroblast and SAOS-2 on cryogels was investigated by MTT tests.
Benzer Tezler
- Dental uygulamalarda yumuşak doku genişletici hidrojellerin sentezi, karakterizasyonu ve şişme kinetiği
Synthesis, characterization and swelling kinetics of soft tissue expander hydrogels in dental applications
ÖMER FARUK GÜDER
Yüksek Lisans
Türkçe
2021
Makine MühendisliğiTekirdağ Namık Kemal ÜniversitesiMakine Mühendisliği Ana Bilim Dalı
DOÇ. DR. UĞUR AKYOL
PROF. DR. BETÜL TAŞDELEN
- Memeli hücrelerinin farklı substrat yüzeyler üzerine adezyonunun kuartz kristal mikrobalans sistemi ile eş-zamanlı belirlenmesi
Real-time determination of the adhesion of mammalian cells on different substrate surfaces by quartz crystal microbalance system
ŞÜKRAN ŞEKER
- Development and characterization of nanofibrous structures for atopic dermatitis treatment
Atopik dermatit tedavisi için nanolifli yapıların geliştirilmesi ve karakterizasyonu
NURSEMA PALA AVCI
Yüksek Lisans
İngilizce
2023
Tekstil ve Tekstil Mühendisliğiİstanbul Teknik ÜniversitesiTekstil Mühendisliği Ana Bilim Dalı
PROF. DR. FATMA BANU NERGİS
DR. ÖĞR. ÜYESİ NEBAHAT ARAL YILMAZ
- Nanocomposite scaffolds containing metal nanoparticles
Metal nanotanecik içeren nanokompozit yapı iskeleleri
AYŞEN AKTÜRK
Doktora
İngilizce
2020
Biyomühendislikİstanbul Teknik ÜniversitesiMetalurji ve Malzeme Mühendisliği Ana Bilim Dalı
PROF. DR. GÜLTEKİN GÖLLER
PROF. DR. MELEK MÜMİNE EROL TAYGUN
- Atıksu ön arıtımı için koimmobilize enzim tasarımı
Coimmobilised enzyme designing for wastewater pretreatment
SİNEM DİKEN GÜR