Güncel CAD/CAM hibrit seramiklere uygulanan farklı yüzey işlemlerinin makaslama bağlanma dayanımına etkisinin değerlendirilmesi

Evaluation of the effects of different surface treatments on the bonding strength of recent CAD/CAM hybrid ceramics

  1. Tez No: 482954
  2. Yazar: MERVE TOKGÖZ ÇETİNDAĞ
  3. Danışmanlar: DOÇ. DR. AYŞE MEŞE
  4. Tez Türü: Diş Hekimliği Uzmanlık
  5. Konular: Diş Hekimliği, Dentistry
  6. Anahtar Kelimeler: Belirtilmemiş.
  7. Yıl: 2017
  8. Dil: İngilizce
  9. Üniversite: Dicle Üniversitesi
  10. Enstitü: Diş Hekimliği Fakültesi
  11. Ana Bilim Dalı: Protetik Diş Tedavisi Ana Bilim Dalı
  12. Bilim Dalı: Belirtilmemiş.
  13. Sayfa Sayısı: 141

Özet

Bu in vitro tez çalışmasının amacı, farklı yüzey işlemlerinin (kontrol, HF asit, Al2O3 tanecikleri ile kumlama, tribokimyasal silika kaplama ve fiber lazer) farklı hibrit seramiklerin (Lava Ultimate ve Vita Enamic) yüzey yapısı üzerinde yaptığı değişiklikleri ve bağlantı dayanımına etkisini incelemektir. Çalışmamızda 2 farklı seramik materyalinden, 120 adet örnek makaslama bağlanma dayanımı testi için ve 10 adet örnek SEM görüntüsü için olmak üzere toplam 130 adet örnek kullanıldı. Makaslama bağlanma testi için şeffaf akrilik kalıba gömülen seramik örnekler öncelikle seramik tipine göre 2 gruba, daha sonra uygulanan yüzey işlemine göre 5 alt gruba ayrıldı. Yüzey işlemi uygulamasından sonra her gruptan birer örneğin SEM görüntüleri elde edildi. Tüm örneklere simantasyon işlemi öncesi Clearfil Ceramic Primer Plus silan 60 sn süreyle uygulandı. Makaslama bağlanma dayanımı testi için akriliğe gömülü seramik örneklerin üzerine uyumlu bir kalıp sayesinde Panavia V5 adeziv rezin siman uygulandı. Bu işlemden sonra tüm örneklere termal döngü uygulaması (5000 döngü, 5-552 C) yapıldı. Kopma gerçekleşene kadar 0,5 mm/dk hızla universal test cihazı kullanılarak makaslama bağlanma kuvveti değerleri ölçüldü. Makaslama testinden sonra yüzeylerin analizi için stereomikroskop kullanıldı. Makaslama bağlanma kuvveti değerleri arasındaki istatistiksel farklılıkların değerlendirilmesi için Oneway Anova Testi, Tamhane Çoklu Karşılaştırma Testi, Kruskal Wallis H Testi, Mann Whitney U Testi ve Bonferoni Düzeltmeli Mann Whitney U Testi kullanıldı. Yüzey işlemine göre en yüksek bağlanma dayanımı değerleri HF asit uygulaması ve Al2O3 tenecikleri ile kumlama gruplarında görüldü. Vita Enamic seramik materyalinin bağlanma dayanımı değerlerinin Lava Ultimate seramik materyalinden daha yüksek olduğu görüldü. Makaslama testi sonrasında elde edilen kopma yüzeylerinin stereomikroskop incelemesinde en fazla adeziv tip kopma görüldü.

Özet (Çeviri)

The aim of this in vitro study was to evaluate the effect of different surface treatments (control, HF acid, sandblasting with Al2O3 particles, tribochemical silica coating and fiber laser) on surface structure and shear bond strength of different ceramics. In our study, 130 specimens were used totally including 120 specimens for shear bond strength and 10 specimens for SEM for each ceramic systems. For shear bond strength, ceramic specimens embedded to clear acrylic resin were firstly divided into 2 groups according to be used ceramics type and divided into 5 subgroups according to surface treatments. After applying the surface treatments, SEM images were taken from each group. Clearfil Ceramic Primer Plus silan was applied to all specimens for 60 seconds before cementation. Panavia V5 adhesive resin cement was manipulated by a mold on the specimens which embedded in acrylic. After this procedure, all specimens were subjected to thermal cycling (5000 cycles, 5-552 C). Bond strength was measured by means of a shear test using universal testing machine with 0,5 mm/min. speed until failure. A stereomicroscope was used to analyse the surfaces for type of failure. To determine the statistical significance of the differences between the mean shear bond strength values, Oneway Anova Test, Tamhane Multiple Comparison Test, Kruskal Wallis H Test, Mann Whitney U Test and Bonferoni Correct Mann Whitney U Test were used. Between all groups, the highest bond strengths were obtained the groups which treated with HF acid and sandblasting with Al2O3. It was observed that the bonding strength values of Vita Enamic ceramic material higher than Lava Ultimate ceramic material. After shear bond strength test, under the stereomicroscope the most prevalent type of failure was seen as adhesive failure and the least prevalent type of failure was seen as cohesive failure.

Benzer Tezler

  1. Farklı CAD/CAM materyalleri ile üretilen lamina veneerlerin bağlanma dayanımlarının in vitro koşullarda değerlendirilmesi

    Farkli CAD/CAM materyalleri ile üretilen lamina veneerlerin bağlanma dayanimlarinin in vitro koşullarda değerlendirilmesi

    ASENA KAPTANOĞLU

    Doktora

    Türkçe

    Türkçe

    2024

    Diş Hekimliğiİstanbul Medipol Üniversitesi

    Protetik Diş Tedavisi Ana Bilim Dalı

    PROF. DR. HALUK BARIŞ KARA

  2. Beyazlatma ajanlarının güncel CAD/CAM materyallerinin yüzey pürüzlülüğüne etkisinin değerlendirilmesi

    Evaluation of the effect of bleaching agents on the surface roughness of novel cad/cam materials

    ELİF ECE AYDIN

    Diş Hekimliği Uzmanlık

    Türkçe

    Türkçe

    2021

    Diş HekimliğiOrdu Üniversitesi

    Protetik Diş Tedavisi Ana Bilim Dalı

    DOÇ. DR. ERSAN ÇELİK

  3. CAD/CAM blokların rezin simanlar ile simantasyonunda kavite dezenfektanı kullanılmasının makaslama bağlanma dayanımına etkisinin incelenmesi

    Investigation of the effect of using cavity disinfectant in cementation of CAD/CAM blocks with resin cements on shears bond strength

    TUĞBA ÖZ

    Diş Hekimliği Uzmanlık

    Türkçe

    Türkçe

    2022

    Diş HekimliğiSağlık Bilimleri Üniversitesi

    Restoratif Diş Tedavisi Ana Bilim Dalı

    PROF. DR. FULYA TOKSOY TOPÇU

  4. Rezin simanların güncel estetik restoratif cad/cam materyallerinin rengi üzerine etkisi

    Başlık çevirisi yok

    IŞIL GÜRDAL

    Diş Hekimliği Uzmanlık

    Türkçe

    Türkçe

    2017

    Diş HekimliğiBezm-i Alem Vakıf Üniversitesi

    Protetik Diş Tedavisi Ana Bilim Dalı

    YRD. DOÇ. DR. AYŞE ATAY

  5. Güncel CAD/CAM seramik bloklarında farklı yüzey işlemlerinin makaslama bağlanma dayanımına etkisinin incelenmesi

    Evaluation of different surface treatments to shear bond strength on current CAD/CAM blocks

    ONUR ETÖZ

    Diş Hekimliği Uzmanlık

    Türkçe

    Türkçe

    2015

    Diş HekimliğiOndokuz Mayıs Üniversitesi

    Protetik Diş Tedavisi Ana Bilim Dalı

    DOÇ. DR. MURAT KURT