Termal oksidasyon ve kimyasal modifikasyon uygulanmış titanyum yüzeylerde karakterizasyon ve osseointegrasyon
Thermal oxidation and hydrofluoric acid treatment on the sandblasted implant surface: A histologic histomorphometric and biomechanical study on sheep pelvis
- Tez No: 493299
- Danışmanlar: PROF. DR. VOLKAN ARISAN
- Tez Türü: Doktora
- Konular: Diş Hekimliği, Dentistry
- Anahtar Kelimeler: Dental implantasyon, Dental implantlar, Hidroflorik asit, Kumlama, Morfometri, Oksidasyon, Osseointegrasyon, Titanyum, Yüzey pürüzlülüğü, Dental implantation, Dental implants, Hydrofluoric acid, Sanding, Morphometry, Oxidation, Osseointegration, Titanium, Surface roughness
- Yıl: 2018
- Dil: Türkçe
- Üniversite: İstanbul Üniversitesi
- Enstitü: Sağlık Bilimleri Enstitüsü
- Ana Bilim Dalı: Oral İmplantoloji Ana Bilim Dalı
- Bilim Dalı: Belirtilmemiş.
- Sayfa Sayısı: Belirtilmemiş.
Özet
Bu çalışmanın amacı; kumlanmış ve termal olarak oksitlenmiş (SO) implant yüzey ile kumlanmış ve termal oksitlenmiş yüzeye ek olarak hidroflorik asitle kimyasal modifikasyonu gerçekleştirilmiş (SOC) implant yüzeyinin topografik, kimyasal ve osseointegrasyon özellikleri açısından standart kumlanmış ve asitlenmiş (SLA) yüzeyle karşılaştırılmasıdır. Gereç ve Yöntem: İlgili yüzeylerin hazırlanmasından ve karakterize edilmesinden sonra altı koyunun pelvik kemiğine her grup için 30 adet olmak üzere, toplam 90 implant yerleştirilmiştir. Üç ve sekiz haftalık iyileşme sonrasında biyomekanik stabilite testleri [rezonans frekans analizi (RFA), yerleştirme (ITV) ve geri çevirme torku değeri (RTV)] ve histomorfometrik analizler (BIC%) yapılmış ve sonuçlar parametrik olmayan metodlarla incelenmiştir (p <0.05). Bulgular: SOC grubundaki pürüzlülük değeri (Ra) SLA ve SO grubundan anlamlı derecede düşük bulunmuştur (p = 0.136, p <0.001 sırasıyla). Bu durum SOC grubunun, SLA ve SO gruplarında elde edilen değerlerden (19.50, SD: 6.07 ve 20.17, SD: 8.95 N/cm, sırasıyla p = 0.001) önemli derecede daha düşük bir ITV (14.83 SD: 4.04 N/cm) göstermesiyle sonuçlanmıştır. Başlangıçtan 3. haftaya kadar olan RFA değerindeki artış sadece SOC grubunda (47.36 SD: 6.93 ISQ) istatistiksel anlamlı fark (62.56 SD: 5.29 ISQ; p = 0.008) göstermiştir. Yerleşim sonrası en yüksek RFA ve RTV değeri SLA grubunda ölçülmüştür (61.11 SD: 7.51 ISQ ve 78.22 SD: 28.73 N/cm). Erken dönem (3. hafta) BIC% oranı ise SO grubunda en yüksek bulunmuştur (39.93 SD: 16.14). Sonuçlar: SOC yüzeyde, kumlanmış ve termal olarak oksitlenmiş yüzeye ilave olarak HF asit uygulanması, standart asitlenmiş ve kumlanmış SLA grubu ile karşılaştırıldığında ek bir avantaj sağlamamıştır.
Özet (Çeviri)
This study aimed to analyze and compare the topographical, chemical and osseointegration characteristics of the sandblasted acid-etched (SLA group), sandblasted- thermally oxidized surface (SO group) and its chemical modification by the hydrofluoric (HF) acid (SOC group). Material and Methods: Following the preparation and characterization of the relevant surfaces a total of 90 implants (30 for each group) were placed to the pelvic bone of six sheep. Biomechanical stability tests [resonance frequency analysis (RFA), insertion (ITV) and removal torque value (RTV)] and histomorphometric analyses (BIC%) were performed after three and eight weeks of healing. Results were analyzed by nonparametric tests (p<0.05). Results: The roughness value (Ra) in the SOC group was significantly lower than the SLA and the SO group (p=0.136, p<0.001, respectively). This resulted with a substantially inferior ITV (14.83 SD: 4.04 N/cm) than those achieved in the SLA and SO groups (19.50, SD: 6.07 and 20.17, SD: 8.95 N/cm, respectively; p=0.001). A statistically significant change of the RFA from the baseline (47.36 SD: 6.93 ISQ) to the 3rd week was observed at the SOC group only (62.56 SD:5.29 ISQ; p=0.008). Highest post-placement RFA and RTV values were measured from the SLA group (61.11 SD:7.51 ISQ and 78.22 SD:28.73 N/cm). Early term (3rd week) BIC% was highest in the SO group (39.93 SD:16.14). Conclusions: Adjunct HF acid application on the thermally oxidized did not provide an additional benefit when compared to the sandblasted and acid-etched surface (SLA group).
Benzer Tezler
- Ti6Al4V alaşımına uygulanan farklı yüzey modifikasyonlarının EPD yöntemi ile üretilen hidroksiapatit kaplamalara etkisinin incelenmesi
Investigation of the effect of different surface modifications applied to Ti6Al4V alloy on hydroxyapatite coatings produced by EPD method
ALPEREN KIZILÖZ
Yüksek Lisans
Türkçe
2023
Metalurji MühendisliğiManisa Celal Bayar ÜniversitesiMetalurji ve Malzeme Mühendisliği Ana Bilim Dalı
PROF. DR. AHMET TÜRK
- Combination of cold spray and micro-arc oxidation methods to fabricate a wear resistant multilayer coating on AZ31 alloy
AZ31 alaşımı üzerinde soğuk sprey ve mikro-ark oksidasyon yöntemlerinin kombinasyonuyla aşınmaya dayanıklı çok katmanlı kaplama fabrikasyonu
EFECAN MADAZLI
Yüksek Lisans
İngilizce
2026
Metalurji Mühendisliğiİstanbul Teknik ÜniversitesiMalzeme Bilimi ve Mühendisliği Ana Bilim Dalı
PROF. DR. HÜSEYİN ÇİMENOĞLU
DOÇ. DR. SEZGİN CENGİZ
- Preparation and adsorption behaviour of hydrophilic adsorbents using high internal phase emulsions
Boya adsorpsiyonu için yüksek iç faz emülsiyonlari ile hidrofilik adsorbentlerin hazirlanmasi ve adsorpsiyon özellikleri
BORA IŞILGAN
Yüksek Lisans
İngilizce
2025
Polimer Bilim ve Teknolojisiİstanbul Teknik ÜniversitesiPolimer Bilim ve Teknolojisi Ana Bilim Dalı
DOÇ. DR. ERDEM YAVUZ
- Mikro ark oksidasyon işlemi uygulanmış silisyum karbür takviyeli az91d magnezyum alaşımının korozyon ve aşınma özelliklerinin incelenmesi
Investigation on wear and corrosion properties of micro arc oxidized sic reinforced az91d magnesium alloy
MEHMET RAGIP MUHAFFEL
Yüksek Lisans
Türkçe
2012
Metalurji Mühendisliğiİstanbul Teknik ÜniversitesiMetalurji ve Malzeme Mühendisliği Ana Bilim Dalı
PROF. DR. HÜSEYİN ÇİMENOĞLU
- Effects of oxidative functionalized and aminosilanized carbon nanotubes on the behaviours of polyamide-6 nanocomposites
Oksidatif fonksiyonelleştirilen ve aminosilanlanan karbon nanotüplerin poliamid-6 nanokompozitlerinin davranışlarına etkileri
SEÇİL ŞANKAL
Yüksek Lisans
İngilizce
2013
Polimer Bilim ve TeknolojisiOrta Doğu Teknik ÜniversitesiMikro ve Nanoteknoloji Ana Bilim Dalı (disiplinlerarası)
PROF. DR. CEVDET KAYNAK
DOÇ. DR. BURCU AKATA KURÇ