Ni-Al ve Nano Al2O3 partiküllerinin plazma transfer ark yöntemi ile Ti6Al4V malzeme yüzeyine uygulanmasının araştırılması

Investigation of plasma transferred arc surface modified Ti6Al4V materials by using Ni-Al and Nano Al2O3 powders

  1. Tez No: 496610
  2. Yazar: KORAY AYDIN
  3. Danışmanlar: DOÇ. DR. OSMAN NURİ ÇELİK
  4. Tez Türü: Doktora
  5. Konular: Makine Mühendisliği, Mechanical Engineering
  6. Anahtar Kelimeler: Belirtilmemiş.
  7. Yıl: 2017
  8. Dil: Türkçe
  9. Üniversite: Eskişehir Osmangazi Üniversitesi
  10. Enstitü: Fen Bilimleri Enstitüsü
  11. Ana Bilim Dalı: Makine Mühendisliği Ana Bilim Dalı
  12. Bilim Dalı: Belirtilmemiş.
  13. Sayfa Sayısı: 1167

Özet

Bu çalışmada Ti6Al4V malzeme yüzeyi Plazma Transfer Ark (PTA) yöntemi kullanılarak Ni-Al ve nano Al2O3 partikülleri ile alaşımlandırılmıştır. Ni-Al metal tozuna %0,8 ağırlık oranında nano Al2O3 partikülleri karıştırılarak veya saf Ni-Al tozları ile yapılan PTA prosesinde 90A, 100A, 110A ve 120A akım değerleri kullanılmıştır. PTA sonrası numunelerin havada ve yağda olmak üzere iki şekilde soğumaları sağlanmıştır. Kaplamanın mikroyapısı; optik mikroskop (OM), taramalı elektron mikroskobu (SEM), enerji saçınımlı X-ışını spektroskopisi (EDX) ve X-ışını difraktogramı (XRD) ile analiz edilmiştir. CSM aşınma (tribometer) cihazı ile lineer harekette levha üzeri bilye (küre-disk) yöntemi kullanılarak numunelere aşınma testi yapılmıştır. Aşınma test verileri incelenerek, kayma mesafesine bağlı olarak ortalama sürtünme katsayıları, sürtünme kuvvetleri ve özgül aşınma oranları hesaplanmıştır. Sonuç olarak; PTA yöntemi Ni-Al metal tozu ile Ti6Al4V malzeme üzerine başarılı bir şekilde uygulanmıştır. Tüm PTA kaplanan numunelerde mikrosertlik ve aşınma dayanımlarında ana malzemeye göre iyileşme görülmüştür. Yapılan yüzey modifikasyonu işlemi sonrasında yapıda Ti, NiTi2 ve Ti3Al fazları tespit edilmiştir. NiTi2 kompozit yapının oluşturduğu fazların sertliği ve aşınma dayanımını arttırdığı gözlenmiştir. Kaplama alanındaki sertlik nano Al2O3 ilavesi ile artmıştır. Ti6Al4V üzerine Ni-Al tozu kullanılarak yapılan PTA numunelerinde ana malzemeye göre aşınma oranında 2,05 kat iyileştirme sağlanmıştır.

Özet (Çeviri)

In this study, Ti6Al4V material surface were alloyed with Ni-Al and nano Al2O3 powders by using plasma transferred arc (PTA) welding process. During PTA process, 0.8w.t.% ratio nano Al2O3 powders mixed with Ni-Al or pure Ni-Al were used at arc current values of 90A, 100A, 110A and 120A. Two types of cooling conditions which were air or oil were performed after PTA. The microstructure of the coating layer was characterized by optical microscope (OM), scanning electron microscope (SEM), energy-dispersive X-ray spectroscopy (EDX) and X-ray diffraction analysis (XRD). Wear was evaluated by ball-on-disc abrasive wear test conditions by using CSM instrument tribometer. While preparing wear surface cross-sectional area, coefficients of friction versus sliding distance, friction forces and friction coefficient, and also specific wear rate were analyzed. Ni-Al reinforced composite coatings were successively produced on Ti6Al4V alloys by the PTA process. The microhardness and wear resistances of all of the composite layers produced by the PTA process were enhanced relative to those of the Ti6Al4V substrate. The results indicate that Ti, NiTi2 and Ti3Al phases formed in the composite layers produced by PTA on the surface of the Ti6Al4V alloy. NiTi2 phases in the composite layers were responsible for the improvement in the wear resistance of the alloy and microhardness. Microhardness of composite layer increased by adding nano Al2O3 to Ni-Al particles. The wear rate of Ni-Al reinforced composite coatings on Ti6Al4V improved 2.05-fold relative to that of the unprocessed sample.

Benzer Tezler

  1. NiO/ZnO ve NiO/ZnO/Al2O3 nanokompozit partiküllerinin ultrasonik sprey piroliz (USP) yöntemiyle üretimi

    Production of NiO/ZnO and NiO/ZnO/Al2O3 nanocomposite particles by ultrasonic spray pyrolysis (USP) technique

    DUYGU YEŞİLTEPE

    Yüksek Lisans

    Türkçe

    Türkçe

    2017

    Metalurji Mühendisliğiİstanbul Teknik Üniversitesi

    Metalurji ve Malzeme Mühendisliği Ana Bilim Dalı

    PROF. DR. SEBAHATTİN GÜRMEN

  2. Nikelalüminat (NiO/Al2O3) nanopartiküllerinin üretimi

    Production of NiO/Al2O3 nanocomposite particles

    TUNÇAĞ CİHANGİR ŞEN

    Yüksek Lisans

    Türkçe

    Türkçe

    2014

    Metalurji Mühendisliğiİstanbul Teknik Üniversitesi

    Metalurji ve Malzeme Mühendisliği Ana Bilim Dalı

    PROF. DR. SEBAHATTİN GÜRMEN

  3. Mekanik alaşımlama yöntemi ile FeCrC takviyeli Ni esaslı kompozit üretimi

    Production of FeCrC reinforced and Ni based composites by mechanical alloying

    FATİH DEMİR

    Yüksek Lisans

    Türkçe

    Türkçe

    2014

    Metalurji MühendisliğiFırat Üniversitesi

    Metalurji ve Malzeme Mühendisliği Ana Bilim Dalı

    PROF. DR. SERDAR OSMAN YILMAZ

  4. Magnetic monitoring approach to kinetics of phase transformations in multicomponent alloy systems

    Çok bileşenli alaşım sistemlerinde faz dönüşüm kinetiğine manyetik izleme yaklaşımı

    NAGEHAN DUMAN

    Doktora

    İngilizce

    İngilizce

    2012

    Metalurji MühendisliğiOrta Doğu Teknik Üniversitesi

    Metalurji ve Malzeme Mühendisliği Ana Bilim Dalı

    PROF. DR. AMDULLA O. MEKHRABOV

    PROF. DR. M. VEDAT AKDENİZ

  5. Bazı metallerin RF magnetron sıçratma yöntemiyle TiN ve TiAlN ile kaplanması

    TiN and TiAlN coated some metals by RF magnetron sputtering method

    MİNE ÖZET

    Yüksek Lisans

    Türkçe

    Türkçe

    2008

    Fizik ve Fizik MühendisliğiErciyes Üniversitesi

    Fizik Ana Bilim Dalı

    PROF. DR. AYHAN GÜLDESTE