TiZr alaşımının toz metalurjisiyle üretimi ve biyouyumluluk özelliğinin incelenmesi

Investigation of biocompatibility property and production of TiZr alloys by powder metallurgy

  1. Tez No: 504339
  2. Yazar: ABDURRAHMAN AKKUŞ
  3. Danışmanlar: DOÇ. DR. MEHMET KAYA
  4. Tez Türü: Yüksek Lisans
  5. Konular: Metalurji Mühendisliği, Ortopedi ve Travmatoloji, Metallurgical Engineering, Orthopedics and Traumatology
  6. Anahtar Kelimeler: Toz metalurjisi, geleneksel sinterleme, biyomalzeme, biyouyumluluk, Powder metallurgy, conventional sintering, biomaterial, biocompatibility
  7. Yıl: 2018
  8. Dil: Türkçe
  9. Üniversite: Adıyaman Üniversitesi
  10. Enstitü: Fen Bilimleri Enstitüsü
  11. Ana Bilim Dalı: Metalurji ve Malzeme Mühendisliği Ana Bilim Dalı
  12. Bilim Dalı: Belirtilmemiş.
  13. Sayfa Sayısı: 101

Özet

Bu çalışmada, TiZr alaşımı toz metalurjisi (TM) yöntemlerinden geleneksel sinterleme ile farklı gözenek oranlarında üretildi. Üretilen numunelerin optik görüntüleri, SEM-EDX görüntü analizleri, XRD desen analizleri, basma dayanımları ve in vivo ortamda biyouyumlulukları incelendi. Üretim yapılırken, atomik olarak Ti-20Zr element tozları dönen bir kap içerisinde toz karışımlarının homojen olması için 12 saat süreyle karıştırıldı ve sonrasında gözenek oluşturmak için amonyum bikarbonat ile karıştırılarak farklı basınçlarda briketlendi. Briketlenen ham numuneler daha sonra farklı sıcaklıklarda iki saat süreyle argon gazı korumalı bir fırın içerisinde sinterlendi. Böylece % 3.17 ile % 40.40 aralığında gözenekliliğe sahip numuneler üretildi. Sinterleme sıcaklığı ve soğuk presleme basıncının artması ile gözenek oranlarının azaldığı görüldü. Üretilen numunelerin SEM-EDX ve XRD analizlerinde yapının α (hcp) fazıdan meydana geldiği, üretilen numunelerden gözenek oranının azalması ile basma dayanımlarının arttığı ve kemiğin basma dayanımından daha fazla olduğu belirlendi. İn vivo ortamda yapılan biyouyumluluk çalışmasında gözenek oranının artması ile yeni kemik ve fibröz doku oluşumunun iyi olduğu, ayrıca herhangi bir doku nekrozunun olmadığı anlaşıldı.

Özet (Çeviri)

In this study, TiZr alloy was produced as different porosities by conventional sintering from powder metallurgy (TM) methods. Optical images, SEM-EDX image analysis, XRD pattern analysis, compression strengths of produced samples and their biocompatibility in vivo were investigated. Ti-at%20Zr element pouders were mixed in a rotating vessel for 12 hours to obtain homogeneous mixtures before production. Later, powder mixture was mixed with ammonium bicorbonate to from pores structure, and then the mixture was briquette at different pressures.Finally the briquetted raw samples were sintered in an argon gas-protected oven at different temperatures for two hours. Thus, porous samples with porosity ranging from 3.17% to 40.40% were obtained. It was observed that the porosity decreases with increasing sintering temperature and cold pressing pressure. In the SEM-EDX and XRD analyzes of the produced samples, α (hcp) phase was seen and it was determined that compressive strength of samples increased with decreasing porosity, and also it was understood that the compressive strengthes of the produced samples were higher than that of bone. In the biocompatibility study performed in the in vivo environment, ıt was understood that the formation of new bone and fibrous tissue were good, and tissue necroses were not occurred.

Benzer Tezler

  1. Development of rare earth-free negative electrode materials for NiMH batteries

    NiMH bataryalar için nadir toprak elementi içermeyen negatif elektrotların geliştirilmesi

    EZGİ ONUR ŞAHİN

    Yüksek Lisans

    İngilizce

    İngilizce

    2016

    EnerjiOrta Doğu Teknik Üniversitesi

    Metalurji ve Malzeme Mühendisliği Ana Bilim Dalı

    PROF. DR. TAYFUR ÖZTÜRK

  2. TiC ve ZrC ilaveli TZM kompozitlerinin spark plazma sinterleme (SPS) yöntemi ile üretimi ve karakterizasyonu

    Production and characterization of TZM based TiC or ZrC reinforced composites prepared by spark plasma sintering (SPS)

    CANSİNEM TÜZEMEN

    Yüksek Lisans

    Türkçe

    Türkçe

    2016

    Metalurji Mühendisliğiİstanbul Teknik Üniversitesi

    Metalurji ve Malzeme Mühendisliği Ana Bilim Dalı

    PROF. DR. GÜLTEKİN GÖLLER

  3. Ti-Zr-Mo alaşımlarının elektrokimyasal korozyon davranışlarının incelenmesi

    Investigation of the electrochemical corrosion behavior in Ti-Zr-Mo alloys

    BADEGÜL TUNÇAY

    Yüksek Lisans

    Türkçe

    Türkçe

    2021

    Makine MühendisliğiKarabük Üniversitesi

    İmalat Mühendisliği Ana Bilim Dalı

    PROF. DURSUN ÖZYÜREK

  4. Investigations on bulk glass forming ability of titanium based multicomponent alloys

    Titanyum bazlı çok bileşenli alaşımların iri ve hacimli cam oluşturma eğiliminin incelenmesi

    SILA SÜER

    Yüksek Lisans

    İngilizce

    İngilizce

    2008

    Metalurji MühendisliğiOrta Doğu Teknik Üniversitesi

    Metalurji ve Malzeme Mühendisliği Bölümü

    PROF. DR. AMDULLA O. MEKHRABOV

    PROF. DR. M. VEDAT AKDENİZ

  5. Farklı materyallerden imal edilerek üst yapısı tamamlanan dar çaplı dental implantların kırılma dayanımlarının karşılaştırılmalı olarak incelenmesi

    Comparative investigation of fracture resistance of narrow diameter dental implants fabricated from different materials with single crown restoration

    YAĞMUR KAHRAMAN BANAZLI

    Diş Hekimliği Uzmanlık

    Türkçe

    Türkçe

    2022

    Diş HekimliğiSivas Cumhuriyet Üniversitesi

    Protetik Diş Tedavisi Ana Bilim Dalı

    DOÇ. DR. OĞUZHAN GÖRLER