Aşırı kron harabiyeti olan kanal tedavisi görmüş dişlerde CAD/CAM ile yapılan restorasyonların kırılma dirençlerinin karşılaştırılması
Comparison of fracture resistance of restorations made with CAD/CAM in root canal treated teeth having severe crown damages
- Tez No: 576323
- Danışmanlar: DOÇ. DR. İSMAİL UZUN
- Tez Türü: Diş Hekimliği Uzmanlık
- Konular: Diş Hekimliği, Dentistry
- Anahtar Kelimeler: CAD/CAM, Dental restorasyon, Dental stres analizi, Kök kanal tedavisi, Post kor tekniği, CAD/CAM, Dental restoration, Dental stress analysis, Root canal therapy, Post and core technique
- Yıl: 2019
- Dil: Türkçe
- Üniversite: Ondokuz Mayıs Üniversitesi
- Enstitü: Diş Hekimliği Fakültesi
- Ana Bilim Dalı: Endodonti Ana Bilim Dalı
- Bilim Dalı: Belirtilmemiş.
- Sayfa Sayısı: Belirtilmemiş.
Özet
Amaç: Aşırı kron harabiyeti olan kanal tedavili dişlere yapılan farklı restorasyonların aksiyal kuvvetler altındaki kırılma dayanımlarının incelenmesi. Materyal Metod: Bu çalışmada 80 adet alt daimi 1. büyükazı dişi kullanıldı. Grup I (Post-Kor), Grup II (Kor-Kron), Grup III (Endokron) ve Grup IV (Kontrol) olacak şekilde 20'şerli dört gruba ayrıldı. Kontrol grubu hariç hepsine kök kanal tedavisi yapıldı. Tüm örneklerin kavite preparasyonları yapıldı. Hazırlık aşamaları bittikten sonra her bir dişin restorasyonu CAD/CAM sistemi ile üretildi. Restorasyonların simantasyon işlemi rezin simanla gerçekleştirildi ve örnekler akrilik bloklara gömüldü. Termomekanik yaşlandırma işleminin ardından örnekler kırılma dayanıklılığı testine hazır hale getirildi. Universal test cihazında, örnekler kırılıncaya kadar kuvvet uygulandı. Kırık tipleri incelendi. Verilerin istatistiksel analizi yapıldı. (p<0,05) Bulgular: Aksiyal kuvvetler altında kırılma değerleri açısından istatistiksel olarak anlamlı fark gözlendi (p<0,05). En yüksek kırılma dayanımı değeri kontrol grubunda(1830 ± 277 N) görülürken, en düşük kırılma dayanımı değeri Kor-Kron grubunda (1532 ± 371 N) görüldü. Kırılma dayanıklılığı testi sonucunda görülen başarısızlık tipleri ile deney grupları arasında istatistiksel olarak anlamlı farklılık bulundu (p=0,001). En fazla görülen kırık tipi Tip II (%33,75) kırık olarak belirlendi. Sonuç: Günümüzde CAD/CAM teknolojisindeki gelişmelerle birlikte aşırı kron harabiyeti olan kanal tedavili dişlerin restorasyonunda daha kolay ve başarılı sonuçlar alınmaktadır.
Özet (Çeviri)
Aim: The present study aimed to compare the fracture strenght of different restorations manufactured with CAD/CAM under axial forces. Material and Methods: In this study, 80 permanent mandibular first molar teeth were used. Samples were divided into four groups: Group I (Post-Core), Group II (Core-Crown), Group III (Endocrown) and Group IV (Control). All but the control group, root canal treatment was performed. Cavity preparations of all samples were made. After the preparation stages, the restoration of each tooth was produced with the CAD/CAM system. The cementation of the restorations was carried out with resin cement. Sample teeth are embedded in acrylic blocks. After the thermomechanical aging process, the samples were ready for fracture resistance testing. In the universal testing machine, force was applied to the samples until they break. The fracture types were examined. The data obtained was statistically analyzed. (p<0,05) Results: A statistically significant difference was observed in the fracture values under axial forces (p<0.05). The highest fracture strength was found in the control group (1830 ± 277 N), while the lowest fracture strength was found in the Core-Crown group (1532 ± 371 N). A statistically significant difference was found between the failure types and the experimental groups (p=0.001). The most common type of fracture was Type II fracture (33.75%). Conclusions: Nowadays, with the technological developments in CAD/CAM, the restoration of the endodontically treated teeth with excessive crown destruction is easier and more successful.
Benzer Tezler
- İzmir'de Mustafa Kemal Bulvarı'nın peyzaj mimarlığı açısından etüdü ve peyzaj projesi
Başlık çevirisi yok
ENGİN ALPARSLAN
Yüksek Lisans
Türkçe
1985
Peyzaj MimarlığıEge ÜniversitesiPeyzaj Mimarlığı Ana Bilim Dalı
YRD. DOÇ. DR. ÜMİT ERDEM
- 1,3-difenil-4,5-bis(hidroksiimino)-imidazolidin ve Ni(II), Cu(II), Pd(II), UO2(VI) komplekslerinin sentezi
Başlık çevirisi yok
VEFA AHSEN
Doktora
Türkçe
1984
Kimya MühendisliğiUludağ ÜniversitesiKimya Mühendisliği Ana Bilim Dalı
PROF. DR. ÖZER BEKAROĞLU
- Pastörizasyondan sonra kültür ilavesinin ekşi kremadan yapılan tereyağlarının özelliklerine etkisi üzerine bir araştırma
Başlık çevirisi yok
SERAP TAMER
Yüksek Lisans
Türkçe
1985
Gıda MühendisliğiEge ÜniversitesiSüt Teknolojisi Ana Bilim Dalı
YRD. DOÇ. DR. ERGİN OKTAR
- İzmir pazarlarında satılan taze köy peynirlerinin bazı nitelikleri ve özellikle zehirlenmeye neden olan bakteri içerikleri üzerinde araştırmalar
Başlık çevirisi yok
NURSEL VAPURCU
Yüksek Lisans
Türkçe
1985
Gıda MühendisliğiEge ÜniversitesiSüt Teknolojisi Ana Bilim Dalı
DOÇ. DR. HASAN YAYGIN
- Sera domates üretiminde aşı uygulaması ile elde edilen çift kök sistemine sahip domateslerin verim ve kalite yönünden üstünlükleri üzerine bir araştırma
Başlık çevirisi yok
ALİ DİZDAROĞLU
Yüksek Lisans
Türkçe
1985
ZiraatEge ÜniversitesiBahçe Bitkileri Ana Bilim Dalı
PROF. DR. FAHRETTİN MECİT