Harçlarda kullanılan bazı puzolanik malzemelerin tane boyutunun alkali-silika reaksiyonuna ve basınç dayanımına etkisinin araştırılması

Investigation of the effect of difference in particle size of some pozzolinic materials used in mortars on alkali-silica reaction and pressure strength

PDF İndir

  1. Tez No: 576634
  2. Yazar: FAHRİ YENTÜRK
  3. Danışmanlar: PROF. DR. BAHRİ ERSOY
  4. Tez Türü: Yüksek Lisans
  5. Konular: Maden Mühendisliği ve Madencilik, Mining Engineering and Mining
  6. Anahtar Kelimeler: Belirtilmemiş.
  7. Yıl: 2017
  8. Dil: Türkçe
  9. Üniversite: Afyon Kocatepe Üniversitesi
  10. Enstitü: Fen Bilimleri Enstitüsü
  11. Ana Bilim Dalı: Maden Mühendisliği Ana Bilim Dalı
  12. Bilim Dalı: Belirtilmemiş.
  13. Sayfa Sayısı: 91

Özet

Bu çalışmada, beton harcının alkali silika reaksiyonuna (ASR) bazı puzolinik madde olarak kullanılan mineral katkıların tane boyutunun etkisi araştırılmıştır. Bu kapsamda Soma termik santrali dip külü (taban külü) ve Gördes zeoliti beş farklı öğütme süresi (0, 30, 60, 180 ve 240 dk) kullanılarak öğütme işlemi gerçekleştirildi ve beş farklı tane boyut grubuna sahip mineral katkı elde edildi. Her bir tane boyutundaki katkılardan sırasıyla %10, 20 ve 30 oranında çimento yerine ikame edilerek beton harçları hazırlandı. Harç hazırlamada agrega olarak Doğancık köyü (Sultandağı/Afyonkarahisar) deresinden alınan doğal ince agrega ve CEM-I 42,5 çimentosu kullanıldı. Hazırlanan harç çubuklarına TS 13517'ye göre hızlandırılmış harç çubuğu yöntemiyle ASR'den kaynaklı genleşme miktarları belirlenmiştir. Çalışmalar sonucunda, alkali silika reaksiyonunu bastırması ve genleşmeyi engellemesi bakımından en iyi sonuçları dip külü için 240 dk. öğütülmüş (d50:16,79 µm) ürünün %30 ikamesi ile elde edilmiştir. Bu ürün katkısız üretilen harca göre genleşme oranını %85,86 oranında azalttığı ve basınç dayanımında ise önemli oranda bir azalmaya (%2,45) neden olmadığı saptanmıştır. Zeolit ile yapılan çalışmalarda ise en iyi sonucun 240 dk. öğütülmüş (d50:10,49 µm) ürünün %10 ikamesi ile elde edilmiştir. Zeolitin %10 ikamesi ile üretilen harçlarda genleşmelerin mineral katkısız harçlarla hazırlananlara göre yaklaşık %98 azaldığı, ancak basınç dayanımında da yaklaşık %29 oranında bir azalma olduğu saptanmıştır.

Özet (Çeviri)

In this research, the effect of the particle size of mineral additive used as some pozzolanic substance on the alkali silica reaction (ASR) of the concrete mortar was investigated. In this context, Soma thermal power plant bottom ash (floor ash) and Gördes zeolite were grinned using five different grinding times (0, 30, 60, 180 and 240 min) and a mineral additive with five different particle size was obtained. Concrete mortars were prepared by substituting respectively 10%, 20 and 30 of cement from each particle size additive. The natural thin aggregate and CEM-I 42.5 cement taken from Doğancık village (Sultandağı / Afyonkarahisar) stream were used as aggregate in the preparation of mortar. Percent expansion values of the mortars resulting from ASR were determined by accelerated mortar bar method according to TS 13517. As a result of the studies, the best results for suppressing alkali silica reaction and preventing expansion for bottom ash, 240 min. (d50:16,79 µm) obtained with a 30% substitution of the product obtained. This product, according to the mortar produced without additive, decreased the rate of expansion by 85,86% and compressive strength did not cause a significant decrease (2.45%). In the studies with zeolite, the best result was obtained with a 10% substitution of the product obtained at the grinding time of 240 min (d50:16,79 µm). The decrease by ~ 98% in the expansion compared to those prepared with mineral additive, but in the pressure strength the decrease by ~29% was determined in the mortars produced with 10% substitution of zeolite.

Benzer Tezler

  1. Tez No

    884115

    Mitigating alkali silica reaction using waste glass powder

    Alkali silika reaksiyonunun azaltılması için atık cam tozu kullanımı

    ABED ALİOGLU

    Yüksek Lisans

    İngilizce

    İngilizce

    2024

    Kimya Mühendisliğiİstanbul Teknik Üniversitesi

    İnşaat Mühendisliği Ana Bilim Dalı

    DR. ÖĞR. ÜYESİ ÖZGÜR EKİNCİOĞLU

  2. Tez No

    151984

    Investigation of lime mortar characteristics for the conservation of the Ottoman baths in Seferihisar-Urla region

    Seferihisar-Urla bölgesindeki Osmanlı dönemi hamamlarının korunması için kireç harç özelliklerinin incelenmesi

    ÖZLEM ÇİZER

    Yüksek Lisans

    İngilizce

    İngilizce

    2004

    Mimarlıkİzmir Yüksek Teknoloji Enstitüsü

    Mimari Restorasyon Ana Bilim Dalı

    DOÇ. DR. BAŞAK İPEKOĞLU

  3. Tez No

    169152

    Efes Yamaçevler 2'de, 1, 2 ve 4 nolu evler örneğinde Roma dönemi harçları araştırması

    Investigation of Roman mortars obtained from the houses numered 1, 2 and 4 of Ephesus, Terrace House 2

    AYŞE ESİN KULELİ

    Doktora

    Türkçe

    Türkçe

    2005

    MimarlıkDokuz Eylül Üniversitesi

    Mimarlık Ana Bilim Dalı

    PROF. DR. ETİ AKYÜZ LEVİ

    PROF. DR. EMİNE CANER SALTIK

  4. Tez No

    100966

    Kireç harç ve sıvaların fiziksel ve mekanik özelliklerinin iyileştirilmesi

    Improving physical and mechanical properties of lime mortars and plasters

    ÖZLEM MAVİ

    Yüksek Lisans

    Türkçe

    Türkçe

    2000

    Mimarlıkİstanbul Teknik Üniversitesi

    DOÇ.DR. MUSTAFA KARAGÜLER

  5. Tez No

    68380

    Some properties of sement mortors containing blast furnace slag and silica fume

    Yüksek fırın cürufu ve silis dumanlı harç karışımlarının bazı özellikleri

    BURAK KIYICI

    Yüksek Lisans

    İngilizce

    İngilizce

    1997

    İnşaat MühendisliğiOrta Doğu Teknik Üniversitesi

    İnşaat Mühendisliği Ana Bilim Dalı

    PROF. DR. ASIM YEĞİNOBALI

Geri Dön