Saflaştırılmış boraks dekahidrat kristallerinin mikrodalga ısıtma ile kurutularak boraks pentahidrat kristallerinin üretilmesi

Production of borax pentahydrat crystals by drying microwave heating of purified borax decahydrat crystals

  1. Tez No: 600253
  2. Yazar: BİLGE ASLAN TANRIVERDİ
  3. Danışmanlar: PROF. DR. HABİBE CANAN CABBAR
  4. Tez Türü: Yüksek Lisans
  5. Konular: Kimya Mühendisliği, Chemical Engineering
  6. Anahtar Kelimeler: Belirtilmemiş.
  7. Yıl: 2019
  8. Dil: Türkçe
  9. Üniversite: Gazi Üniversitesi
  10. Enstitü: Fen Bilimleri Enstitüsü
  11. Ana Bilim Dalı: Kimya Mühendisliği Ana Bilim Dalı
  12. Bilim Dalı: Belirtilmemiş.
  13. Sayfa Sayısı: 128

Özet

Bu tez çalışması ile, boraks pentahidratın (BPH), Na2B4O7.5H2O, üretimi sırasında proses gereği zorunlu olarak açığa çıkan atık sınıflandırmasındaki düşük B2O3 içerikli çözeltinin mümkün olduğunca ekonomiye kazandırılması, böylelikle hem proses performansının artırılması, hem de atık stok alan hacminin ve çevresel etkilerin minimuma indirilmesi amaçlanmıştır. Bu çalışma ile tüvenan tinkal cevherinden elde edilen boraks çözeltisinin öncelikle saflaştırma işlemi uygulanmadan ve sonrasında iki farklı yöntemle saflaştırılması ile (özellikle suda az çözünen kalsiyum, magnezyum ve sülfatın ayrılması) boraks dekahidrat (BDH), Na2B4O7.10H2O, kristallerinin oluşturulması ve oluşturulan bu kristallerin mikrodalga ile kurutularak BPH kristallerinin üretilmesi incelenmiştir. Dünya bor rezervinin %73'üne sahip Türkiye, Eskişehir – Kırka yatağında bulunan tinkal cevheri, renksiz ve saydam olmasına rağmen, bileşimindeki çeşitli safsızlıklar nedeniyle pembe, sarımsı veya gri renklerde bulunabilir. Tinkal cevheriyle birlikte gelen suda çözünmeyen kil gibi gang minerallerin, flokulant ile çöktürülerek ayrılması ile elde edilen boraks çözeltisine öncelikle hiçbir saflaştırma prosesi uygulamadan, ikinci olarak sönmüş kireç soda ile ve son olarak sadece sönmüş kireç ile saflaştırılarak suda az miktarda çözünen safsızlıkların giderilmesi araştırılmış ve elde edilen çözeltiler kristallendirilerek BDH kristalleri elde edilmiştir. Çalışmada daha sonra BPH eldesi için farklı güçlerde (300, 600 ve 1200 W) ve farklı zaman aralıklarında mikrodalga enerjisi kullanılarak ısıtmaya tâbi tutulmuştur. Böylece, ortalama B2O3 içeriği % 37 olarak üretilmiş BDH kristallerinin, mikrodalga ısıtma sonrası ortalama % 48 B2O3 içeriği olan BPH ürünleri elde edilmiştir. Ayrıca 1200 W kademesinin zaman ve enerji verimliliği açısından daha uygun olduğu görülmüştür.

Özet (Çeviri)

In this thesis, it is aimed to include the low B2O3 containing solution in the waste classification as required by the process during the production of borax pentahydrate (BPH), Na2B4O7.5H2O, to the economy as much as possible, thus increasing both process performance and minimizing the waste stock area volume and environmental impacts. In this study, borax decahydrate (BDH), Na2B4O7.10H2O crystals were formed without purification and then by two different purification methods. Purification of borax solution obtained from coarse tinkal ore (especially separation of low soluble calcium, magnesium and sulfate) and microwave production of BPH crystals were investigated. Boron reserves of the world have found in Turkey 73 %, Eskişehir - Kırka tincal ore, despite being colorless and transparent, pink due to various impurities in the composition, can be found in yellowish or gray. The removal of small amounts of water-soluble impurities was firstly applied without any purification process, secondly by purifying with slaked lime soda and finally by purifying only with slaked lime, the removal of small amount of impurities dissolved in water was investigated and obtained. The resulting solutions were crystallized to give BDH crystals. In the study, it was then subjected to heating by using microwave energy at different powers (300, 600 and 1200 W) and at different time intervals to obtain BPH. Thus, BDH with an avarege content of B2O3 of 37 %, BPH product with an average content of 48 % B2O3 after microwave heating was obtained. In addition, 1200 W is more suitable for time and energy efficiency.

Benzer Tezler

  1. Antimikrobiyal bor bileşikleri kullanılarak tarihi taş yapılardaki biyodeteriorasyonun önlenmesi üzerine araştırmalar

    Research on the prevention of biodeterioration of historic stone structures by using antimicrobial boron compounds

    ÖZLEM GÜLMEZ

    Doktora

    Türkçe

    Türkçe

    2023

    BiyolojiAtatürk Üniversitesi

    Biyoloji Ana Bilim Dalı

    PROF. DR. ÖZLEM BARIŞ

  2. Sülfürlü ve oksitli bileşiklerden ergimiş tuz elektrolizi ile bakır ve alaşımlarının direkt sentezi

    Direct synthesis of copper and copper alloys from sulfide/oxide compounds via molten salt electrolysis

    LEVENT KARTAL

    Doktora

    Türkçe

    Türkçe

    2019

    Metalurji Mühendisliğiİstanbul Teknik Üniversitesi

    Metalurji ve Malzeme Mühendisliği Ana Bilim Dalı

    PROF. DR. SERVET İBRAHİM TİMUR

  3. Saflaştırılmış sepiyolit ile sulu çözeltilerden mono azo boyar madde bazik mavi 41 (BB41) adsorpsiyon karakteristiklerinin incelenmesi

    Investigation of adsorption characteristics of mono azo dyestuff basic blue 41 (BB41) from aqueous solutions by using purified sepiolite

    HİLAL ASYA KARABULUT

    Yüksek Lisans

    Türkçe

    Türkçe

    2023

    Kimya MühendisliğiYıldız Teknik Üniversitesi

    Kimya Mühendisliği Ana Bilim Dalı

    DOÇ. DR. YASEMEN KALPAKLI

  4. Saflaştırılmış çörekotu (Nigella sativa) yağının oksidatif stabilitesi üzerine tokoferol izomerlerinin ve timokinonun etkisinin belirlenmesi

    Determination of the effect of tocopherol isomers and thymoquinone on the oxidative stability of purified black cumin (Nigella sativa) oil

    ŞEYMA DİLMEN

    Yüksek Lisans

    Türkçe

    Türkçe

    2018

    Gıda MühendisliğiBolu Abant İzzet Baysal Üniversitesi

    Gıda Mühendisliği Ana Bilim Dalı

    DOÇ. DR. SEMRA TURAN

  5. Adsorptive characteristics of aflatoxin B1 in the presence of purified clinoptilolite rich mineral and Lactobacillus plantarum S2

    Saflaştırılmış klinoptilolitçe zengin mineral ve Lactobacillus plantarum S2 varlığında aflatoksin B1?in adsorptif özellikleri

    ÇİSEM BULUT ALBAYRAK

    Doktora

    İngilizce

    İngilizce

    2012

    Kimya Mühendisliğiİzmir Yüksek Teknoloji Enstitüsü

    Kimya Mühendisliği Ana Bilim Dalı

    PROF. DR. SEMRA ÜLKÜ

    PROF. DR. H.ŞEBNEM HARSA