Stiren-bütil akrilat-akrilik asit latekslerinin emülsiyon polimerizasyonu ile hazırlanması için proses değişkenlerinin optimizasyonu ve fizikokimyasal özellikleri üzerine divinilbenzen etkisinin incelenmesi
Optimization of process variables for the micro emulsion polimerization of styrene-butyl acrylate-acrylic acid latexes and determination of divinylbenzene effect on their physicaochemical properties
- Tez No: 604952
- Danışmanlar: DOÇ. DR. BİLGE EREN
- Tez Türü: Yüksek Lisans
- Konular: Kimya, Polimer Bilim ve Teknolojisi, Chemistry, Polymer Science and Technology
- Anahtar Kelimeler: Stiren Akrilik Kopolimer, Lateks, Divinilbenzen, Emülsiyon Polimerizasyonu, Su-Bazlı Boya, Styrene Acrylic Copolymer, Latex, Divinylbenzene, Emulsion Polymerization, Water-Born Paint
- Yıl: 2019
- Dil: Türkçe
- Üniversite: Bilecik Şeyh Edebali Üniversitesi
- Enstitü: Fen Bilimleri Enstitüsü
- Ana Bilim Dalı: Kimya Ana Bilim Dalı
- Bilim Dalı: Belirtilmemiş.
- Sayfa Sayısı: 85
Özet
Bu çalışmada öncelikle yarı kesikli çekirdekli emülsiyon polimerizasyonu ile stiren (Sty)/bütil akrilat (BA)/akrilik asit (AAc) kopolimer (SAC) lateks taneciklerinin hazırlanması için proses değişkenlerinin etkisi incelenmiştir. Bu kapsamda, monomer oranları, çekirdek miktarı ve yüzey aktif madde miktarı gibi proses değişkenlerinin SAC latekslerin fizikokimyasal özellikleri üzerindeki etkisi DSC, TG/DTG, SEM, 1H-NMR, FTIR, MFFT ve DLS teknikleri ile açıklanmıştır. Optimizasyon çalışmaları pratik kaplama uygulamaları için akrilik latekslerden beklenen özellikleri sağlayan en ideal lateksin Sty:BA:AAc için 44:54:2 monomer oranları ile elde edildiğini göstermiştir. İkinci bölümde ise belirlenen optimum koşullar uygulanarak divinilbenzen (DVB) çapraz bağlı SAC lateksleri hazırlanmış ve DVB miktarının latekslerin kararlılık, film oluşturma ve tanecik büyüklüğü üzerine etkisi incelenmiştir. SAC lateks partiküllerinde DVB biriminin varlığı, artan termal stabiliteye neden olmuştur. SAC lateksinin camsı geçiş özellikleri, DVB artışından etkilenmiştir. DVB oranı %0'dan %2'ye çıkarıldığında filmlerin Tg değeri 7,5 ºC'den 24,5 ºC'ye çıkmıştır. Minimum film oluşturma sıcaklığı (MFFT) değerleri ise 0-9 ºC arasında değerler almaktadır. Hazırlanan çapraz bağlı latekslerin pratik uygulamalar için uygun olan MFFT ve Tg değerlerine sahip oldukları belirlenmiştir. Böylece uçucu organik bileşik (VOC) değeri artırılmadan daha yüksek mekanik ve kimyasal dirence sahip yeni tip latekslerin eldesi mümkün olmuştur. DVB içeriğinin 0.5%'ten %2'ye çıkarılmasıyla ortalama tanecik boyutu 83.62 nm ile 194.60 nm aralığında değişirken polidispersite indeksi (PDI), sırasıyla 0.015'ten 0.140'a yükselmiştir. Yeterli düzeyde bir kararlılığa ve iyi bir dağılabilirliğe işaret olan PDI değerleri uygulanan yöntemin pratik uygulamalar için çapraz bağlı latekslerin hazırlanmasında kullanılabilecek bir yöntem olduğunu ispatlamıştır.
Özet (Çeviri)
In this study, firstly the effect of process variables for the preparation of styrene (Sty)/butyl acrylate (BA)/acrylic acid (AAc) copolymer (SAC) latex particles via the semi batch seeded emulsion polymerization was investigated. In this context, the effect of process variables such as monomer ratios, seed amount and surfactant amount on the physicochemical properties of SAC latexes were explained by means of DSC, TG/DTG, SEM, 1H-NMR, FTIR, MFFT, and DLS techniques. Optimization studies showed that the most ideal latex that provides the properties expected from acrylic latexes for practical coating applications is obtained with a monomer ratio of 44: 54: 2 for Sty: BA: AAc. In the second part, divinylbenzene (DVB) crosslinked SAC latexes were prepared by applying the determined optimum conditions and the effect of DVB amount on the stability, film formation and particle size of the latexes were examined. The presence of DVB moity in the SAC latex particles caused increased thermal stability The glass transition characteristics of SAC latex was affected by the addition of DVB. When the DVB ratio was increased from 0% to 2%, the Tg value of the films increased from 7.5 ºC to 24.5 ºC. Minimum film formation temperature (MFFT) values are between 0-9 ºC. The prepared cross-linked latexes were found to have MFFT and Tg values suitable for practical applications. Thus, it was possible to obtain new types of latex with higher mechanical and chemical resistance without increasing the voltalite organic compound (VOC) value.When DVB ratio was increased from 0.5% to 2%, the average particle size changed between 83.62-194.60 nm, and polydispersty index (PDI) values increased from 0.015 to 0.140, respectively. PDI values sufficient for practical applications proved that the applied method can be used in the preparation of cross-linked latexes. PDI values indicate sufficient stability and good dispersibility, have proved that the applied method can be used in the preparation of cross-linked latexes for practical applications.
Benzer Tezler
- 2-Hidroksietil metakrilat (HEMA) modifiye edilmiş stiren-bütil akrilat-akrilik asit emülsiyon polimerlerinin sentezi ve karakterizasyonu
Synthesis and characterization of 2-hydroxyethyl methacrylate (HEMA) modified styrene-butyl acrylate-acrylic acid emulsion polymers
HÜLYA ÇINAR
Yüksek Lisans
Türkçe
2022
KimyaBilecik Şeyh Edebali ÜniversitesiKimya Ana Bilim Dalı
PROF. DR. BİLGE EREN
- Alkali dirence sahip akrilik emülsiyon polimerlerinin sentezi ve karakterizasyonu
Synthesis and characterization of alkali resistant acrylic emulsion polymers
BUSE MÜZEYYEN POYRAZ
Yüksek Lisans
Türkçe
2020
KimyaGebze Teknik ÜniversitesiMalzeme Bilimi ve Mühendisliği Ana Bilim Dalı
DR. ÖĞR. ÜYESİ İLKE ANAÇ
- Synthesis of new multifunctional olefin monomers and polymers by reactions of a- hydroxymethyl methyl vinyl ketone
Başlık çevirisi yok
REYHAN İŞERİ
- Çinko tozu ile ATRP (Atom transfer radikal polimerleşme) reaksiyon ortamından bakır katalizin kimyasal indirgeme ile giderilmesi
Removal of the copper catalyst from ATRP mixtures by chemical reduction with zinc powder
FATMA CANTÜRK
Yüksek Lisans
Türkçe
2011
Polimer Bilim ve Teknolojisiİstanbul Teknik ÜniversitesiKimya Ana Bilim Dalı
PROF. DR. NİYAZİ BIÇAK
- The synthesis and characterization of modified resin
Modifiye reçinelerin sentezi ve karakterizasyonu
PELİN DİNÇER
Yüksek Lisans
İngilizce
2012
Polimer Bilim ve Teknolojisiİstanbul Teknik ÜniversitesiPolimer Bilim ve Teknolojisi Ana Bilim Dalı
PROF. DR. NİLGÜN KIZILCAN