Polimer bazlı kompozit üretimi

Polymer based composite production

  1. Tez No: 614635
  2. Yazar: GÖRKEM DEĞİRMEN BİRİCİK
  3. Danışmanlar: PROF. DR. FUNDA ATEŞ, DOÇ. DR. HANDE ÇELEBİ
  4. Tez Türü: Doktora
  5. Konular: Kimya Mühendisliği, Chemical Engineering
  6. Anahtar Kelimeler: Biyokütle, Piroliz, Karbon Fiber, Polimer, Karakterizasyon, Biomass, Pyrolysis, Carbon Fiber, Polymer, Characterization
  7. Yıl: 2019
  8. Dil: Türkçe
  9. Üniversite: Anadolu Üniversitesi
  10. Enstitü: Fen Bilimleri Enstitüsü
  11. Ana Bilim Dalı: Kimya Mühendisliği Ana Bilim Dalı
  12. Bilim Dalı: Belirtilmemiş.
  13. Sayfa Sayısı: 196

Özet

Bu çalışmada; hammadde olarak keten lifi, matris malzemesi olarak da PA66 seçilmiştir. Keten lifinin farklı sıcaklık (400°C, 500°C, 700°C), farklı alıkonma zamanı (1 saat ve 3 saat) parametreleri ile sabit yataklı reaktörde pirolizi gerçekleştirilmiştir. Elde edilen keten lifi piroliz katı ürünü ve PA66 eriyik karıştırma yöntemi ile ekstrüderden geçirilmiş, enjeksiyon kalıpta şekillendirilmiştir. Karbon fiber ve keten lifi piroliz katı ürünü karışımı PA66 matris malzemesine kompozit malzeme üretmek üzere katkılanmıştır. HNO3 modifikasyonunun karbon fiber, piroliz katı ürünü üzerine etkisi araştırılmıştır. Modifiye edilen karbon fiber ve piroliz katı ürünü ile PA66 kompozit örnekleri hazırlanmıştır. Hazırlanan kompozit örneklerinde çekme testi, su absorpsiyon testi, termal iletkenlik testi gerçekleştirilmiştir. Örneklerin ısıl davranışını incelemek için termogravimetrik analiz (TGA) ve morfolojik yapısını gözleyebilmek için taramalı elektron mikroskobu (SEM) karakterizasyon yöntemleri uygulanmıştır. Ayrıca keten lifi piroliz katı ürünü ve karbon fiber için elementel analiz, FT-IR ve BET analizi yapılarak özellikleri belirlenmiştir. Modifikasyon kompozit malzemelerin mekanik özelliklerinde gelişme sağlamıştır. Toplamda %10 katkı ile karbon fiber içeren kompozit malzemelerde çekme dayanımı 90,5 MPa bulunurken, %50 karbon fiber ve %50 piroliz katı ürünü içeren kompozit malzemelerde çekme dayanımı 89 MPa olarak bulunmuştur. 70,6 MPa çekme dayanımına sahip saf PA66'ya kıyasla iyileşme elde edilmiştir.

Özet (Çeviri)

In this study flax fiber has been used as a raw material while PA66 has been chosen as matrix. The flax fiber has been pyrolyzed in a fixed bed reactor with different process parameters with temperature (400°C, 500°C, 700°C) and retention time (1 and 3 hours). The flax fiber pyrolysis char product and PA66 has been processed at the extruder by melt compounding and shaped at injection moulding. Carbon fiber and flax fiber pyrolysis char product has been mixed to produce composite material. The effect of HNO3 modification has been investigated upon carbon fiber and flax fiber pyrolysis char product. PA66 composite material products have been prepared with modified carbon fiber and flax fiber pyrolysis char product. Tensile test, water absorption test and thermal conductivity test has been conducted on prepared composite material products. To examine the thermal behavior of composite material products thermogravimetric analysis (TGA) has been used and the morphological properties of products has been observed with scanning electron microscopy characterization method. Furthermore the properties of carbon fiber and flax fiber pyrolysis char product has been determined with elemental analysis, FT-IR and BET analysis. Modification has provided development on mechanical properties of composite materials. The tensile strength has been found as 90.5 MPa for composite materials including carbon fiber while it has been found as 89 MPa for composite materials including 50% carbon fiber, 50% pyrolysis solid product with 10% reinforcement. The improvement has been achieved compared to pure PA66 with a tensile strength of 70.6 MPa.

Benzer Tezler

  1. Processing and characterization of polymer composites with superior impact resistance

    Üstün darbe dayanımlı polimer bazlı kompozit malzemelerin üretimi ve karakterizasyonu

    ABDULLAH TUĞRUL SEYHAN

    Yüksek Lisans

    İngilizce

    İngilizce

    2003

    Metalurji Mühendisliğiİzmir Yüksek Teknoloji Enstitüsü

    Malzeme Bilimi ve Mühendisliği Ana Bilim Dalı

    YRD. DOÇ. DR. METİN TANOĞLU

  2. Doku mühendisliği uygulamaları için polimer matrisli kompozit malzeme üretimi

    Production of polymer matrix composite material for tissue engineering applications

    AYŞE KAPLAN

    Yüksek Lisans

    Türkçe

    Türkçe

    2021

    BiyomühendislikYıldız Teknik Üniversitesi

    Biyomühendislik Ana Bilim Dalı

    DOÇ. DR. CEM BÜLENT ÜSTÜNDAĞ

  3. Çeşitli katkı malzemelerinin sinerjitik etkisi ile epoksi esaslı polimer kompozit kaplamanın üretimi ve tribolojik özelliklerinin incelenmesi

    Production of epoxy based polymer composite coating with synergistic effect of various additives and investigation of its tribological properties

    MERVE YILMAZ

    Yüksek Lisans

    Türkçe

    Türkçe

    2023

    Metalurji MühendisliğiSakarya Üniversitesi

    Metalurji ve Malzeme Mühendisliği Ana Bilim Dalı

    PROF. DR. ŞADUMAN ŞEN

  4. Dogal fiber takviyeli kompozit üretimi ve mekanik özelliklerinin tespiti

    Natural fiber based composites; production and mechanical properties

    ENGİN SARIKAYA

    Doktora

    Türkçe

    Türkçe

    2019

    Makine MühendisliğiPamukkale Üniversitesi

    Makine Mühendisliği Ana Bilim Dalı

    PROF. DR. HASAN ÇALLIOĞLU

  5. Development of biocompatible and flexible polymers for DLP processing and improvement of mechanical properties

    DLP prosesi için biyouyumlu ve esnek polimerlerin geliştirilmesi ve mekanik özelliklerinin iyileştirilmesi

    EMRAH UYSAL

    Doktora

    İngilizce

    İngilizce

    2021

    Makine MühendisliğiMarmara Üniversitesi

    Makine Mühendisliği Ana Bilim Dalı

    PROF. DR. BÜLENT EKİCİ

    DOÇ. DR. MUSTAFA ÇAKIR