PH döngü modeli ve farklı tamir yöntemleri uygulanan zirkonya seramiklerinin bağlanma dayanımlarının değerlendirilmesi
Evaluation of bond strength of zirconia ceramicsapplied with PH-cycling model and different repairmethods
- Tez No: 624897
- Danışmanlar: DR. ÖĞR. ÜYESİ GÜL DİNÇ ATA, DR. ÖĞR. ÜYESİ BAYKAL YILMAZ
- Tez Türü: Diş Hekimliği Uzmanlık
- Konular: Diş Hekimliği, Dentistry
- Anahtar Kelimeler: Dental bonding, Dental materyaller, Dental restorasyon, Dental stres analizi, Hidrojen iyon konsantrasyonu, Lazerler, Zirkonyum, Dental bonding, Dental materials, Dental restoration, Dental stress analysis, Hydrogen-ion concentration, Lasers, Zirconium
- Yıl: 2020
- Dil: Türkçe
- Üniversite: Adnan Menderes Üniversitesi
- Enstitü: Diş Hekimliği Fakültesi
- Ana Bilim Dalı: Restoratif Diş Tedavisi Ana Bilim Dalı
- Bilim Dalı: Belirtilmemiş.
- Sayfa Sayısı: Belirtilmemiş.
Özet
Amaç: Çalışmamızın amacı; üç farklı yüzey işlemi (kontrol grubu, air abrazyon ve Er:YAG lazer) uygulanarak iki farklı tamir kiti (Cimara ve Bisco Intraoral Tamir Kiti) ile tamir edilen ve farklı yaşlandırma yöntemleri (pH döngüsü ve termal döngü) ile yaşlandırılan Yttria Stabilize Zirkonya (Y-TZP) seramiklerinin makaslama bağlanma dayanımlarını değerlendirmektir. Gereç ve Yöntem: Y-TZP seramik bloklar (N=120) (Aidite, Zir Dental, Qinhuangdao, Çin) (6 mm x 8 mm x 8 mm) farklı yüzey işlemi için rastgele üç eşit gruba ayrıldı: (a) kontrol grubu (üretici firmanın önerdiği yüzey işlemleri), (b) air abrazyon ve (c) Er:YAG lazer. Yüzey işlemlerinden sonra, bloklara aşağıdaki tamir kitlerinden biri uygulandı: (1) Cimara (Voco, Cuxhaven, Almanya) ve (2) Bisco İntraoral Onarım Kiti (Bisco, Schaumburg, IL, ABD). Kompozit rezin (Clearfil Majesty Posterior, Kuraray, Japan) işlem gören yüzeylere tabakalanarak uygulandı ve ışıkla polimerize edildi. Tamir edilen örneklerin bir yarısı termal döngüye (n=10) (5.000 döngü), diğer yarısı pH döngüsüne (n=10) (6 ay) tabi tutulduktan sonra tüm örneklere makaslama bağlanma dayanımı testi uygulandı. Başarısızlık tipleri ışık mikroskobu altında incelendi. Veriler, üç yönlü varyans analizi, Kruskal-Wallis, Mann-Whitney U ve Bonferroni düzeltmeli ikili karşılaştırma testleri kullanılarak değerlendirildi (α=0,05). Bulgular: Yaşlandırma yöntemleri, yüzey işlemleri ve tamir kitleri arasında etkileşimin olduğu ve de tamir kiti ile yüzey işlemleri arasında etkileşimin olduğu bulunmuştur (p<0,05). Tüm gruplarda %100 adeziv başarısızlık görüldü. Sonuç: Zirkonya seramiklerin tamirinde yüzey işlemlerinin, tamir kitlerinin ve pH döngüsünün makaslama bağlanma dayanımları üzerine etkisinin olduğu bulunmuştur.
Özet (Çeviri)
Aim: The aim of this study was to evaluate the shear bond strength of Yttria Stabilized Zirconia (Y-TZP) ceramics treated with three different surface treatments (no treatment, air abrasion and Er:YAG laser) and repaired with two different repair kits (Cimara and Bisco) followed by aging with two different aging methods (pH cycling and thermocycling). Materials and methods: Y-TZP ceramic blocks(N=120) (Aidite, Zir Dental, Qinhuangdao, China) (6 mm x 8 mm x 8 mm) were randomly and equally divided into three groups for different surface treatments: (a) control group (surface treatments recommended by the manufacturer) (b) air abrasion, and (c) Er:YAG laser. After surface treatment, one of the following repair kits was applied to the blocks: (1) Cimara (Voco, Cuxhaven, Germany) and (2) Bisco Intraoral Repair Kit (Bisco, Schaumburg, IL, USA). Resin composite (Clearfil Majesty Posterior, Kuraray, Japan) was applied to the treated surfaces incrementally and light cured. Half of the repair samples were subjected to thermocycling (n=10) (5.000 cycles) and the other half to pH cycling (n=10) (6 months), and then shear bond strength test was applied to all specimens. Failure patterns were examined under a stereomicroscope. Data were evaluated by using three-way analysis of variance, Kruskal-Wallis, Mann-Whitney U and Bonferroni corrected paired comparison tests (α=0,05). Results: Interactions were found between aging methods, surface treatments and repair kits, as well as between repair kit and surface treatments (p<0,05). All groups showed 100% adhesive failures. Conclusion: It has been observed that surface treatments, repair kits and pH cycle have an effect on shear bond strength in repair of zirconia ceramics.
Benzer Tezler
- PH döngü modeli ve farklı tamir yöntemleri uygulanan kompozit rezinlerin bağlanma dayanımlarının değerlendirilmesi
Evaluation of bond strength of composite resins applied ph-cycling model and different repair methods
FETİYE AKIN
Diş Hekimliği Uzmanlık
Türkçe
2017
Diş HekimliğiAdnan Menderes ÜniversitesiRestoratif Diş Tedavisi Ana Bilim Dalı
YRD. DOÇ. DR. GÜL DİNÇ ATA
- Derin öğrenme ve büyük veri analitiği yöntemleriKullanarak Covid-19 yayılımının ileriye dönük tahmini
Forecasting the spread of covid-19 using deep learning and big data analytics methods
CYLAS KIGANDA
Yüksek Lisans
İngilizce
2023
Bilgisayar Mühendisliği Bilimleri-Bilgisayar ve KontrolGazi ÜniversitesiBilgisayar Bilimleri Ana Bilim Dalı
PROF. DR. MUHAMMET ALİ AKCAYOL
- Tommaso Campanella ve Thomas More`un ütopyalarının karşılaştırılması
Comparing Thomas More and Tommaso Campanella`s utopias
MAHMUT AVCI
Yüksek Lisans
Türkçe
2006
FelsefeAtatürk ÜniversitesiFelsefe ve Din Bilimleri Ana Bilim Dalı
YRD. DOÇ. DR. OSMAN ELMALI
- Süt formüllerinin tüketim uygulamaları ve süt formüllerinin C vitamini içeriği ile pH değerleri
Başlık çevirisi yok
GÖNÜL VAROL
Yüksek Lisans
Türkçe
1986
Besin Hijyeni ve Teknolojisiİstanbul ÜniversitesiÇocuk Gelişimi Ana Bilim Dalı
DOÇ. DR. TÜRKAN KUTLUAY