Bor karbür ve titanyum karbür ilaveli sürtünmeli kaplamanın karakteristik özelliklerinin incelenmesi

Investigation of characteristic properties of boron carbide and titanium carbide additive friction surfacing

  1. Tez No: 649088
  2. Yazar: MEHMET ERBİL ÖZCAN
  3. Danışmanlar: PROF. DR. LATİF ÖZLER
  4. Tez Türü: Doktora
  5. Konular: Makine Mühendisliği, Metalurji Mühendisliği, Mechanical Engineering, Metallurgical Engineering
  6. Anahtar Kelimeler: Belirtilmemiş.
  7. Yıl: 2020
  8. Dil: Türkçe
  9. Üniversite: Fırat Üniversitesi
  10. Enstitü: Fen Bilimleri Enstitüsü
  11. Ana Bilim Dalı: Makine Mühendisliği Ana Bilim Dalı
  12. Bilim Dalı: Belirtilmemiş.
  13. Sayfa Sayısı: 180

Özet

Kaplama işlemleri, malzemenin özelliklerinin belirlenmesinde önemli rol oynar. Malzemelerin sertlik, korozyon ve aşınma direnci gibi yüzey özelliklerini iyileştirmek ya da bu özellikleri bir araya toplamak amacıyla farklı kaplama yöntemleri kullanılmaktadır. Bu kaplama yöntemlerinden biri de sürtünmeli kaplama yöntemidir. Yöntem, altlık malzeme yüzeyine kendi ekseni etrafında belirli bir çevresel hızda dönen kaplama milinin teması sonucunda plastik deformasyon sıcaklığına ulaşarak altlık malzeme üzerine biriktirme esasına dayanır. Bu çalışmada, kaplama işlemleri iki farklı yöntem kullanılarak yapılmıştır. Birinci yöntemde önce altlık malzeme yüzeyine belirli oranda kaplama tozu yapıştırılmış daha sonra kaplama mili vasıtasıyla kaplama malzemesinin altlık malzeme yüzeyine karışması sağlanarak malzeme kaplanmıştır. İkinci yöntemde ise takviye malzemeleri ve alüminyum tozlar çeşitli oranlarda karıştırılıp, kaplama milinin içine preslenerek sinterlenmiş ve gradyanlı olarak altlık malzeme üzeri kaplanmıştır. Deney parametrelerinin kaplamaların mekanik özellikleri üzerine, mikro yapıya, sertliğe ve aşınma direncine etkisi incelenmiş ve elde edilen kaplamaların eğme deneyleri yapılmıştır. Mikro yapı incelemeleri optik, SEM, EDX ve XRD yardımıyla yapılmıştır. Yapılan çalışma sonucunda, bazı toz ilavesiz tek katlı kaplamalarda altlık malzeme ile kaplama ara yüzeyinde kısmi boşluklar olduğu görülmüştür. Toz serme yöntemi ile yapılan kaplamalarda altlık malzemesi ile kaplama arasındaki yapışma yüzeyinin oldukça iyi, fakat homojen bir kaplama yapısının oluşmadığı görülmüştür. Toz takviyeli gradyanlı kaplamalarda ise kaplama ile altlık malzemesinin ara yüzey yapışmasının iyi olduğu, katmanlar arasındaki geçişlerin iyi olduğu görülmüştür.

Özet (Çeviri)

Coating processes play an important role in determining the properties of the material. Different coating methods are used to improve the surface properties of the materials such as hardness, corrosion and wear resistance or to gather these properties together. One of these coating methods is friction surfacing method. The method is based on the principle of accumulation on the substrate material by reaching the plastic deformation temperature as a result of the contact of the consumable rod rotating around the axis to the substrate at a certain rotational speed. In this study, coating processes were made using two different methods. In the first method, a certain amount of coating powder is adhered to the substrate material surface, and then the material is coated by ensuring that the coating material is mixed with the surface of the substrate material by means of the consumable rod. In the second method, reinforcement and aluminum powders are mixed in various proportions, pressed into the consumable rod and sintered and coated gradiently on substrate surface. The effects of the test parameters on the mechanical properties were investigated. Microstructure, micro hardness and wear resistance were examined and bending tests of the obtained coatings were carried out. Microstructures were investigated with the help of optics, SEM, EDX and XRD. As a result of the study, it has been observed that some powder-free single-layer coatings have partial gaps at the interface of substrate and coating. It was observed that the adhesion surface between the substrate material and the coating of the samples made by the powder laying method was quite good, but a homogeneous coating structure was not formed. In powder reinforced gradient coatings, it was observed that the interlayer adhesion of the coating and the substrate was good and the transitions between the layers were good.

Benzer Tezler

  1. Bor karbür ve titanyum tozlarından hareketle spark plazma sinterleme tekniği ile bor karbür esaslı kompozit üretimi ve karakterizasyonu

    Production of boron carbide based composites with boron carbide and titanium powders by spark plazma sintering

    UFUK ŞAHİN

    Yüksek Lisans

    Türkçe

    Türkçe

    2015

    Metalurji Mühendisliğiİstanbul Teknik Üniversitesi

    Metalurji ve Malzeme Mühendisliği Ana Bilim Dalı

    PROF. DR. FİLİZ ÇINAR ŞAHİN

  2. Grafen ve bor nitrür katkılarının titanyum diborür – titanyum karbür kompozitlerinin özellikleri üzerine etkilerinin incelenmesi

    Investigation of the effects of graphene and boron nitride additives on the properties of titanium diboride – titanium carbide composites

    BESTE ECEM KAYAR

    Yüksek Lisans

    Türkçe

    Türkçe

    2023

    Metalurji Mühendisliğiİstanbul Teknik Üniversitesi

    Malzeme Bilimi ve Mühendisliği Ana Bilim Dalı

    DOÇ. DR. İPEK AKIN KARADAYI

  3. Sıcak presleme yöntemi ile Al2Cu ve h-BN katkılı alüminyum ve alüminyum alaşım matrisli kompozitlerin aşınma davranışlarının incelenmesi

    Investigation of abrasion behavior of aluminum and aluminum alloy reinforced with Al2Cu and h-BN produced by hot pressing

    BURAK SAMED DOĞU

    Yüksek Lisans

    Türkçe

    Türkçe

    2020

    Metalurji Mühendisliğiİstanbul Teknik Üniversitesi

    Metalurji ve Malzeme Mühendisliği Ana Bilim Dalı

    PROF. DR. HÜSEYİN ÇİMENOĞLU

  4. Production and characterization of spark plasma sintered boron carbide ceramic composites suitable for ballistic use

    Balistik kullanıma uygun bor karbür seramik kompozitlerinin spark plazma sinterleme yöntemi ile üretimi ve karakterizasyonu

    BURCU APAK GÜLSEVER

    Doktora

    Türkçe

    Türkçe

    2018

    Metalurji Mühendisliğiİstanbul Teknik Üniversitesi

    Metalurji ve Malzeme Mühendisliği Ana Bilim Dalı

    PROF. DR. FİLİZ ŞAHİN

  5. B4c ilaveli tzm alaşımlarının spark plazma sinterleme (SPS) yöntemi ile farklı tasarımlarla üretimi ve karakterizasyonu

    Production and characterization of b4c rei̇nforced tzm alloy with different designs prepared by spark plasma sintering (SPS) method

    BARIŞ YAVAŞ

    Doktora

    Türkçe

    Türkçe

    2020

    Metalurji Mühendisliğiİstanbul Teknik Üniversitesi

    Metalurji ve Malzeme Mühendisliği Ana Bilim Dalı

    PROF. DR. GÜLTEKİN GÖLLER