Perlit esaslı geopolimer betonda endüstriyel atıkların değerlendirilmesi
Evaluation of industrial wastes in perlite based geopolymer concrete
- Tez No: 655325
- Danışmanlar: DR. ÖĞR. ÜYESİ FATMA KARAGÖL
- Tez Türü: Yüksek Lisans
- Konular: İnşaat Mühendisliği, Civil Engineering
- Anahtar Kelimeler: Geopolimer, perlit, yüksek fırın cürufu, uçucu kül, kırmızı çamur, fiziksel, mekanik ve durabilite özellikler, Geopolymer, perlite, blast furnace slag, fly ash, red mud, physical, mechanical and durability properties
- Yıl: 2020
- Dil: Türkçe
- Üniversite: Atatürk Üniversitesi
- Enstitü: Fen Bilimleri Enstitüsü
- Ana Bilim Dalı: İnşaat Mühendisliği Ana Bilim Dalı
- Bilim Dalı: Belirtilmemiş.
- Sayfa Sayısı: 94
Özet
Amaç: Türkiye'de zengin rezerve sahip perlitin, belirli oranlarda endüstriyel atık ürünlerle ikame edilerek yeni nesil yapı malzemesi olan geopolimer beton üretiminde kullanılmasıdır. Yöntem: : Perlit esaslı geopolimer kompozitte uçucu kül, yüksek fırın cürufu ve kırmızı çamurun ağırlıkça %10, %20 ve %30 oranlarında ikame edilmesiyle 10 farklı karışım grubu hazırlanmıştır. Gruplarda alkali aktivatör olarak NaOH ve Na2SiO3 kombinasyonu kullanılmıştır. Üretilen numunelere, 90°C sıcaklıkta 72 saat boyunca etüvde termal kür uygulanmıştır. Üretilen numunelerin mekanik özeliklerindeki değişimleri belirlemek için birim ağırlıkları, su emme oranları ve 3, 7, 28 ve 90 günlük basınç dayanımları tespit edilmiştir. Ayrıca, yüksek sıcaklık (300°C, 500°C ve 700°C), donma-çözülme, asit (%5 HCl) ve sülfat (%5 MgSO4) etkisi sonrası basınç dayanımları ve ağırlık değişimleri incelenmiştir. Bulgular: Yalnızca perlit içeren grupta 25,1 MPa, uçucu kül, yüksek fırın cürufu ve kırmızı çamur kullanılan gruplarda ise sırasıyla 34,9 MPa, 50,1 MPa ve 28,7 MPa basınç dayanımları elde edilmiştir. Yüksek fırın cürufu içeren gruplar, diğer gruplara nazaran durabilite deneyleri sonucunda daha iyi performans göstermiştir. Sonuç: NaOH ve Na2SiO3 kombinasyonu ile perlit aktive edilerek geopolimer beton üretilmiştir. Ayrıca, endüstriyel atıkların perlit esaslı geopolimer betonlarda ikame edilmesinin, geopolimer kompozitlerin mekanik ve durabilite özelliklerini olumlu yönde etkilediği gözlemlenmiştir. 2020, 94s
Özet (Çeviri)
Purpose: This study aims to use perlite with rich reserves in Turkey, in the production of geopolymer concrete, which is a new generation building material, by replacing it with industrial waste products in certain proportions. Method: 10 different mixture groups were prepared by replacing fly ash, blast furnace slag and red mud at 10%, 20% and 30% by weight in the perlite based geopolymer composite. The combination of NaOH and Na2SiO3 was used as alkaline activator in the groups. The samples were thermally cured in the oven at 90°C for 72 hours. In order to determine the changes in the mechanical properties of the samples produced, the unit weights, water absorption rates and 3, 7, 28 and 90-day compressive strengths were determined. In addition, compressive strengths and weight changes after the effects of high temperature (300°C, 500°C and 700°C), freeze-thaw, acid (5% HCl) and sulphate (5% MgSO4) were investigated. Findings: Compressive strengths of 25,1 MPa were obtained in the group containing only perlite, and 34,9 MPa, 50,1 MPa and 28,7 MPa in the groups using fly ash, blast furnace slag and red mud, respectively. Groups containing blast furnace slag showed better performance as a result of durability tests compared to other groups. Results: Geopolymer concrete was produced by activating perlite with the combination of NaOH and Na2SiO3. In addition, it has been observed that the substitution of industrial wastes in perlite-based geopolymer concretes positively affects the mechanical and durability properties of geopolymer composites. 2020, 94 p
Benzer Tezler
- Kırmızı çamur ve yüksek fırın cürufunun perlit esaslı geopolimer beton özelliklerine etkisi
The effect of red mud and blast furnace slag on perlite based geopolymer concrete properties
FATİH AKBULUT
Yüksek Lisans
Türkçe
2020
İnşaat MühendisliğiAtatürk Üniversitesiİnşaat Mühendisliği Ana Bilim Dalı
DOÇ. DR. RIZA POLAT
- Yapay hafif agrega üretimi ve geopolimer betonda kullanımının araştırılması
Production of artificial lightweight aggregate and investigation of its use in geopolymer concrete
AHMET ÖZCAN
Doktora
Türkçe
2024
İnşaat Mühendisliğiİnönü Üniversitesiİnşaat Mühendisliği Ana Bilim Dalı
PROF. DR. MEHMET BURHAN KARAKOÇ
- Geri dönüştürülmüş geopolimer agregalardan üretilen normal betonların mekanik ve fiziksel özelliklerini araştırılması
Investigation of the properties of normal concretes produced from recycled geopolymer aggregates
SAYED AHMAD ANIS
Yüksek Lisans
Türkçe
2023
İnşaat MühendisliğiAtatürk ÜniversitesiYapı Malzemesi Ana Bilim Dalı
DOÇ. DR. RIZA POLAT
- Isı yalıtım kabiliyetine sahip perlit esaslı geopolimer bağlayıcılı harçların geliştirilmesi
Development of perlite-based geopolymeric mortars with thermal insulation capability
SELAHATTİN GÜZELKÜÇÜK
Doktora
Türkçe
2020
İnşaat MühendisliğiKırıkkale Üniversitesiİnşaat Mühendisliği Ana Bilim Dalı
PROF. DR. İLHAMİ DEMİR
- Tek parçalı karışım yöntemiyle üretilen perlit esaslı geopolimer betonlarda nano katkıların ve kür koşullarının etkilerinin incelenmesi
Investigation of the effects of nano additives and curing conditions on perlite based geopolymer concrete produced by the one-part mixing method
ELİF DİŞÇİ
Yüksek Lisans
Türkçe
2021
İnşaat MühendisliğiAtatürk Üniversitesiİnşaat Mühendisliği Ana Bilim Dalı
DOÇ. DR. RIZA POLAT