Mechanical properties of compacted and sintered powder metallurgy blanks
Başlık çevirisi mevcut değil.
- Tez No: 6559
- Danışmanlar: DOÇ.DR. SÜLEYMAN SARITAŞ
- Tez Türü: Yüksek Lisans
- Konular: Makine Mühendisliği, Mechanical Engineering
- Anahtar Kelimeler: Toz metalürji, Gözenek, Yüzey oksitlenmesi, Pişirme atmosferi vı, Powder metallurgy, Porosity, Surface oxidation, Sintering atmosphere IV
- Yıl: 1989
- Dil: İngilizce
- Üniversite: Gaziantep Üniversitesi
- Enstitü: Fen Bilimleri Enstitüsü
- Ana Bilim Dalı: Makine Mühendisliği Ana Bilim Dalı
- Bilim Dalı: Belirtilmemiş.
- Sayfa Sayısı: Belirtilmemiş.
Özet
ÖZET TOZ METALLIC JI YÖNTEMİYLE BRKETLENEREK VE PİŞİRİLEREK ÜRETİLEN PARÇALARIM MEKANİK ÖZELLİKLERİ ÖZAKÇA, Mustafa Yüksek Lisans Tezi, Makina Mühendisliği BöIühiü Tez Yöneticisi: Doç. Dr. Süleyman Saritaş Haziran 1989, 91 Sayfa Bu çalışmada, toz metallurji yöntemiyle briketlenerek ve pişirilerek üretilen parçaların mekanik özellikleri incelenmiştir. Deneysel çalışmalar yüzey oksitlenmesinin ve gözeneklerin mekanik özelliklere etkisini incelemek üzere iki ana grup etrafında yoğunlaştırılmıştır. Yüzey oksitlenmesinin mekanik özelliklere etkisini tesbit etmek için briketlenmiş demir tozları kırılmış amonyak, azot, hava gibi atmosferlerde veya pik talaşı ve kok tozu karışımından oluşan ortam içinde pişirilmiştir, indirgeyici atmosfer özelliği gösteren kırılmış amonyak ortamda pişirilen parçalardan oksitsiz yüzey ve en yüksek mekanik özellikler elde edilmiştir. Bunu koruyucu azot atmosferinde pişirilen parçalar izlemektedir. Ayrıca metalografik çalışmalar sonucunda kırılmaların oksitlenmiş tane sınırından başladığı tesbit edilmiştir. Gözeneklerin ve briketleme basıncının mekanik özelliklere etkisini incelemek için yoğunluğu */? 79 ile "/. 94 arasında değişen pişirilmiş parçalar çekme testine tabi tutulmuşlardır. Pişirilmiş malzemelerinçekme mukavemetleri basma yüküne göre maksimum nokta göstermiştir. Bu nokta '/. 98 yoğunluğa karsı gelmektedir. Yoğunluk daha da artırıldığında çekme mukavemeti azalmıştır. Bu durum havanın izole gözeneklerde hapsedilmesiyle izah edilmiştir. Bu hava pişirme esnasında genişleyerek daha önce oluşan soğuk kaynakları yırtmış ve böylece pekme mukavemetini düşürmüştür. Soğuk kaynakların yırtılması ile oluşan çatlaklar ve briketlemedeki yoğunluk dağılımı metalografik metotlarla tesbit edilmiştir.
Özet (Çeviri)
ATTRACT MECHANICAL PROPERTIES OF COMPACTED AND SINTERED POWDER METALLURGY BLANKS ÖZAKÇA Mustafa M.S. in Mechanical Engineering Supervisor : Assoc. Prof. Dr. Süleyman Sari t as June 1989, 91 Pages In this study mechanical properties of compacted and sintered powder metallurgy parts were investigated. The experimental works were focused on observing the influence of powder surface oxidation and residual porosity on mechanical properties. To assess the influence of surface oxidation on the mechanical properties, the amount of surface oxidation was modified by subjecting the powder compacts to different sintering atmospheres. These sintering atmosphere were: Dissociated ammonia, nitrogen, air and mixtures of cast iron chips-coke powders media. Reducing type dissociated ammonia atmosphere produced the oxide-free surface boundary, and gave the highest mechanical properties. Protecting type inert nitrogen atmosphere also produced acceptable level of mechanical properties. Metallographic examination showed that tensile crack initiations were generally started from oxidized surface boundaries. mSintered samples, with densities varying from 79 '/. to 94 "/. of theoretical density, were tested in tension to study the effects of residual porosity and compacting pressure on mechanical properties. Tensile strengths of sintered blanks showed a peak with respect to compacting force. This peak corresponded to BQ */. compacted density. As density was further increased it resulted with lower tensile strengths. This is enpiamed with trapping of air in isolated pores at higher compacting forces, entrapped air is compressed. Later, during sintering, it is expanding and shearing the cold welds produced during compaction, and thus reducing the tensile strength.
Benzer Tezler
- Toz metalurjisi yöntemiyle üretilen mikroalaşım çeliklerinin mikroyapı mekanik özellik ilişkisinin araştırılması
An investigation on the relation sheep between microstructure and mechanical properties of microalloyed steels produced by powder metallurgy
MEHMET AKİF ERDEN
Doktora
Türkçe
2015
Metalurji MühendisliğiKarabük Üniversitesiİmalat Mühendisliği Ana Bilim Dalı
PROF. DR. SÜLEYMAN GÜNDÜZ
- Niyobyum (NB) ile güçlendirilmiş demir (FE) matrisli alaşımların toz metalurjisi yöntemiyle üretimi ve mekanik özelliklerinin araştırılması
An investigation on mechanical properties of nb added fe – matrix alloy produced by powder metallurgy method
DOĞAN ÖZDEMİRLER
Yüksek Lisans
Türkçe
2017
Metalurji MühendisliğiKarabük Üniversitesiİmalat Mühendisliği Ana Bilim Dalı
PROF. DR. SÜLEYMAN GÜNDÜZ
- Mekanik alaşımlama yöntemiyle üretilmiş volfram esaslı kompozitlerin karakterizasyon çalışmaları ve gama radyasyon davranışlarının incelenmesi
Characterization investigations of mechanically alloyed tungsten based composites and their behaviours via gamma radiation
OZAN YILMAZ
Doktora
Türkçe
2017
Metalurji Mühendisliğiİstanbul Teknik ÜniversitesiMetalurji ve Malzeme Mühendisliği Ana Bilim Dalı
PROF. DR. MUSTAFA LÜTFİ ÖVEÇOĞLU
- Difüzyon kaynağı ile birleştirilmiş TM bakır esaslı kompozit malzemelerin mikroyapı ve mekanik özelliklerinin incelenmesi
Investigation of microstructure and mechanical properties of powder metallurgy (PM) copper-based composites welded by diffusion technique
MARWAN ABDUSSALAM MOHAMMED ELHEMSHERI
Doktora
Türkçe
2022
Mühendislik BilimleriKastamonu ÜniversitesiMalzeme Mühendisliği Ana Bilim Dalı
DR. ÖĞR. ÜYESİ ÖZKAN ESKİ
- Toz metalurjisi yöntemiyle elde edilen demir esaslı köpüksü metallerin mikroyapısı ve mekanik özellikleri
Microstructural and mechanical properties of iron based foamed metals obtained by powder metallurgy method
NURAY BEKÖZ
Doktora
Türkçe
2011
Metalurji Mühendisliğiİstanbul ÜniversitesiMetalurji ve Malzeme Mühendisliği Ana Bilim Dalı
PROF. DR. ENVER OKTAY