Eklemeli üretim yönteminde kullanılan lazer cihazı gücünün, metal porselen bağlantı dayanımı ve metalin mikro yapısına etkisinin değerlendirilmesi
Evaluation of the effect of laser power used in the additive manufacturing method on metal porcelain bond strength and micro structure of metal
- Tez No: 666706
- Danışmanlar: DR. ÖĞR. ÜYESİ HAYDAR ALBAYRAK
- Tez Türü: Diş Hekimliği Uzmanlık
- Konular: Diş Hekimliği, Dentistry
- Anahtar Kelimeler: Belirtilmemiş.
- Yıl: 2021
- Dil: Türkçe
- Üniversite: Erciyes Üniversitesi
- Enstitü: Diş Hekimliği Fakültesi
- Ana Bilim Dalı: Protetik Diş Tedavisi Ana Bilim Dalı
- Bilim Dalı: Belirtilmemiş.
- Sayfa Sayısı: 161
Özet
Son yıllarda Cr-Co altyapılı metal seramik (MS) restorasyonların üretiminde geleneksel döküm yönteminin alternatifi olarak Seçici Lazer Ergitme (SLE) yöntemi sıklıkla tercih edilmektedir. Bu çalışmanın amacı SLE tekniğinde kullanılan farklı üreticilere ait metal tozları ile iki farklı güce sahip lazer ergitme cihazından (100 W, 200 W) üretilen metal altyapıların; mikro yapı ve MS bağlantı dayanımlarını karşılaştırmaktır. Toplam 80 adet metal altyapı numunesi ISO 9693 standartlarına göre döküm yöntemi (Grup D, n=16) ve iki farklı metal tozundan (Remanium Star Cl Grup R, n=32; Castco Grup C, n=32) SLE yöntemiyle üretilmiştir. SLE gruplarındaki numunelerin yarısı 100 Watt (n=16; C-100 ve R-100) diğer yarısı ise 200 Watt (n=16; C-200 ve R-200) gücündeki eklemeli üretim cihazında üretilmiştir. Üretilen metal altyapılar 110 µm' lik Al2O3 tozu ile kumlanmış ve oksidasyon işlemi uygulanmıştır. Oksidasyon uygulanan tüm gruplardan 2'şer adet numunenin mikro yapısı X ışını Difraktometresi (XRD) ile incelenmiştir. Geri kalan numunelere porselen yığma işlemi yapılmıştır. Tüm gruplardan porselen işlenmiş 10'ar adet numune rastgele seçilmiş ve MS bağlantı dayanımı 3-nokta bükme testi ile belirlenmiştir. Kalan numunelerin yarısının MS ara yüzü Enerji Dağılım Spektrometresi (EDS) çizgi ve alan analizi ile karakterize edilmiştir. Numunelerin diğer yarısının faz haritası ve tane boyutu analizi EBSD cihazında belirlenmiştir. Faz haritasından baskın olan faz ve ortalama tane boyutu değerleri ölçülmüştür. Faz haritası incelenen numunelere nano sertlik testi yapılmış ve mikro yapısal özelliklerin nano sertlikle ilişkisi incelenmiştir. MS bağlantı dayanımı verileri, bir istatistik programında varyans analizleri ile değerlendirilmiştir (α=0,05). Yapılan tek yönlü analiz sonucu D grubunun (46,20 MPa), C (40,49 MPa) ve R (40,99 MPa) grubundan daha yüksek MS bağlantı dayanımına sahip olduğu görülmüştür (p
Özet (Çeviri)
In recent years, the Selective Laser Melting (SLM) method is frequently preferred as an alternative to the traditional casting method in the production of metal-ceramic (MC) restorations with Co-Cr substructure. The aim of this study is to compare the microstructure and MC bond strengths of the metal substructure produced from different manufacturers' metal powders, used in SLM technique, by using two laser melting devices of different power levels (100 W, 200 W). A total of 80 metal substructure samples were produced according to ISO 9693 standards. Control group was produced by using the casting method (Group D, n = 16) while the other groups were produced from two different metal powders, using the SLM method (Remanium Star Cl Group R, n = 32; Castco Group C, n = 32). Half of the samples in the SLM groups were produced in an additive manufacturing device with 100 Watt (n = 16; C-100 and R-100) and the other half with 200 Watt (n = 16; C-200 and R-200) power. The metal substructures produced were sandblasted with 110 µm Al2O3 powder and oxidation process was applied. The microstructures of 2 samples from each of the oxidized groups were examined with X-ray Diffractometer (XRD). Porcelain application process was applied to the remaining samples. 10 pieces of porcelain processed samples were randomly selected from all groups and MC bond strength was determined by putting them through the 3-point bending test. The MC interface of half of the remaining samples was characterized by Energy Dispersive Spectrometry (EDS) line and area analysis. The phase map and particle size analysis of the other half of the samples were determined on the EBSD device. The dominant phase and average grain size values were measured from the phase map. Nano hardness test was performed on samples whose phase maps were examined and the relationship between microstructural properties and nanoshardness was investigated. MC bond strength data were evaluated by analysis of variance in a statistical program (α = 0.05). As a result of the one-way analysis, it was observed that the group D (46.20 MPa) had higher MC bond strength than the group C (40.49 MPa) and group R (40.99 MPa) (p
Benzer Tezler
- Seçici lazer ergitme yöntemi ile değişken üretim parametreleri kullanılarak üretilen 316L paslanmaz çeliğin yapısal ve tribolojik özelliklerinin incelenmesi
Investigation of the structural and tribological properties of 316L stainless steel manufactured using variable production parameters by selective laser melting method
UFUK GENÇOĞLU
Yüksek Lisans
Türkçe
2021
Makine MühendisliğiErzurum Teknik ÜniversitesiMakine Mühendisliği Ana Bilim Dalı
PROF. DR. FATİH YILDIZ
- Manufacturing and characterization of polymer composites by using selective laser sintering 3D printing method
Seçici lazer sinterleme 3D baskı yöntemiyle polimer kompozitlerin üretim ve karakterizasyonu
BURÇİN ÖZBAY
Doktora
İngilizce
2021
Polimer Bilim ve Teknolojisiİstanbul Teknik ÜniversitesiPolimer Bilim ve Teknolojisi Ana Bilim Dalı
PROF. DR. İBRAHİM ERSİN SERHATLI
- Farklı lazer gücü ve tarama hızlarında slm ile üretilen metal altyapıların porselen bağlantı dayanımlarının incelenmesi
Investigation of the porcelain bond strength of metal frameworks manufactured by slm with different laser power and scanning speed
BETÜL KARAHASAN
Diş Hekimliği Uzmanlık
Türkçe
2023
Diş HekimliğiSivas Cumhuriyet ÜniversitesiProtetik Diş Tedavisi Ana Bilim Dalı
PROF. DR. DERYA ÖZDEMİR DOĞAN
- Gaz atomizasyon yönteminde yeni bir nozul tasarımı ve toz üretimi
A new nozzle design and metal powder production by gas atomization
MEHMET AYDIN
Yüksek Lisans
Türkçe
2005
Makine MühendisliğiDumlupınar ÜniversitesiMakine Eğitimi Ana Bilim Dalı
YRD. DOÇ. DR. RAHMİ ÜNAL
- Bir uçak braketinin topoloji yöntemiyle optimizasyonu, seçici lazer ergitme yöntemiyle üretimi ve analizi
Optimization of an aircraft bracket by topology, production and analysis with selective laser melting method
MUSTAFA TOK
Yüksek Lisans
Türkçe
2023
Makine MühendisliğiOsmaniye Korkut Ata ÜniversitesiMakine Mühendisliği Ana Bilim Dalı
DR. ÖĞR. ÜYESİ YUSUF FEDAİ