Yüzey işlemlerinin veneer materyalleri ile yüksek dayanıklı termoplastik altyapı materyalleri bağlantısına etkisi
Effect of surface treatments on the bonding strength of veneer materials and high-performance thermoplastic framework materials
- Tez No: 669160
- Danışmanlar: DOÇ. DR. DOĞU ÖMÜR DEDE
- Tez Türü: Diş Hekimliği Uzmanlık
- Konular: Diş Hekimliği, Dentistry
- Anahtar Kelimeler: Yüksek performanslı polimer, PEEK, PEKK, yüzey işlemi, veneerleme tekniği, makaslama bağlantı dayanımı testi, Dental bonding, Dental materyaller, Dental stres analizi, Diş kaplamaları, Polimerler, Takma diş tabanları, Yüzey işleme tekniği, High-performance polymer, PEEK, PEKK, surface treatment, veneering technique, shear bond strength test, Dental bonding, Dental materials, Dental stress analysis, Dental veneers, Polymers, Denture bases, Surface handling technique
- Yıl: 2021
- Dil: Türkçe
- Üniversite: Ordu Üniversitesi
- Enstitü: Diş Hekimliği Fakültesi
- Ana Bilim Dalı: Protetik Diş Tedavisi Ana Bilim Dalı
- Bilim Dalı: Belirtilmemiş.
- Sayfa Sayısı: Belirtilmemiş.
Özet
Amaç: Bu tez çalışmasının amacı; farklı yüzey işlemlerinin ve veneerleme tekniklerinin, PEEK ve PEKK polimerleri ile indirekt laboratuvar kompoziti (ILK) ve seramik veneer (SV) materyalleri arasındaki makaslama bağlantı dayanımına (MBD) etkisinin değerlendirilmesidir. Gereç ve Yöntem: PEEK ve PEKK polimer gruplarının her birinden MBD testi için 140'ar, toplamda 280 adet, taramalı elektron mikroskobu (SEM) analizleri için ise 7'şer, toplamda 14 adet polimer örnek hazırlanmıştır (7x7x2 mm). Her iki polimer grubuna ait örnekler, MBD ve SEM analizleri için; herhangi bir işlem uygulanmamış kontrol (Cnt), atmosferik soğuk plazma (Pls), sülfürik asit (Sa), kumlama (Sb), tribokimyasal silika kaplama (Rocatec Plus) (Tbc), kumlama + sülfürik asit (Sb+Sa), Rocatec Plus + sülfürik asit (Tbc+Sa) yüzey işlemleri için, alt gruplara ayrılmıştır (MBD, n=10; SEM, n=1). Yüzey işlemleri uygulanan polimer örneklerin SEM analizleri yapılmış (x1200), ILK ve SV bağlandıktan sonra üniversal test cihazı ile 0,5 mm / dk kafa hızında MBD testi uygulanmıştır. Elde edilen Newton cinsinden değerler megapaskal değerlerine dönüştürülmüştür (MPa = N/mm²). MBD test verileri üç yönlü varyans analizi (ANOVA), bağımsız örneklem t-testi ve Tukey HSD testi ile istatistiksel olarak analiz edilmiştir (α=,05). Test gruplarına ait kırık tiplerinin analiz edilmesinde Pearson chi-kare testi, MBD ve kırık tipleri arasındaki korelasyonun değerlendirmesinde ise Pearson Korelasyon testi kullanılmıştır. Bulgular: Üç yönlü varyans analizi (ANOVA) testi sonuçlarına göre yüzey işlemleri, polimer tipi ve veneer materyali bağımsız değişkenlerin etkileşimlerinden, polimer tipi * yüzey işlemi etkileşimi haricindeki (P=,653) tüm değişkenler ve bunların etkileşimlerinin MBD sonuçları üzerinde anlamlı derecede etkili olduğu görülmüştür (P<,001). En yüksek MBD değerleri, her iki polimer için, Sa yüzey işlemi uygulanan ILK veneer ile bağlanan gruplarda (PEEK; 21,55 ± 1,45 MPa, PEKK; 17,04 ± 1,99 MPa) görülmüştür (P<,05). Sonuç: Uygulanan yüzey işlemlerinin MBD değerleri üzerinde ve PAEK polimerlerin yüzey topoğrafisinde farklı etkilerinin olduğu görülmektedir. Daha yüksek bağlantı dayanımı ve uzun süreli klinik başarının sağlanabilmesi için uygulanacak yüzey işlemi, kullanılan polimer tipi ve veneer materyaline göre daha spesifik hale getirilmelidir.
Özet (Çeviri)
Aim: The aim of this thesis study was that the evaluate the effect of surface treatments and veneering techniques on the shear bond strength (SBS) of PEEK and PEKK polymers to indirect laboratory composite (ILK) and ceramic veneer (SV) materials. Material and Method: 140 polymer samples (7x7x2 mm) were prepared for each PEEK and PEKK polymer group to perform the SBS test with a total amount of 280; also 7 samples for each polymer to perform scanning electron microscopy (SEM) analysis with a total amount of 14. Each polymer samples were divided into 7 subgroups (n = 10) according to the surface treatments; control (Cnt), atmospheric cold plasma (Pls), sulfuric acid (Sa), sandblasting (Sb), tribochemical silica coating (Tbc), sandblasting + sulfuric acid (Sb+Sa), tribochemical silica coating + sulfuric acid (Tbc+Sa). SEM analyzes of polymer samples with surface treatments were performed. ILK and SV materials were bonded onto the SBS polymer samples. All SBS samples were subjected to SBS test with a universal test machine. The data in Newtons were converted into megapascals (MPa= N/mm²). SBS test data were analyzed statistically by three-way analysis of variance (ANOVA), independent sample t-test, and Tukey HSD test. Pearson chi-square test was used to analyze fracture types of test groups, and Pearson Correlation test was used for correlation between SBS and fracture types. Results: According to the results of the three-way analysis of variance (ANOVA), it was detected that the interaction of surface treatments, polymer type, and veneer material and also the interactions (except polymer type * surface treatment, P = .653) were significant on the SBS results. (P <, 001). The highest SBS values were observed for both polymer in the SA surface treated and ILK veneered (PEEK; 21.55 ± 1.45 MPa, PEKK; 17.04 ± 1.99 MPa) groups (P<,05). Conclusion: The surface treatments had different effects on the SBS values and surface topography of both polymers. Therefore, the surface treatment processes should be more specific for the polymer type and the applied veneering technique.
Benzer Tezler
- Farklı peek materyallerine uygulanan çeşitli yüzey işlemlerinin yaşlandırma prosedürleri altında kompozit ile bağlanma dayanımına etkisinin incelenmesi
Investigation of the effect of various surface treatments applied to different peek materials on the bond strength with composite under aging procedures
ZEYNEP GÖKÇE BAĞLAN
Doktora
Türkçe
2025
Diş HekimliğiSağlık Bilimleri ÜniversitesiProtetik Diş Tedavisi Ana Bilim Dalı
DOÇ. DR. ŞEVKİ ÇINAR
- Farklı yüzey işlemlerinin zirkonya - veneer seramiklerin makaslama bağlanma dayanımına etkisinin incelenmesi
Investigation the effect of different surface treatments on the shear bond stength of zirconia-veneer ceramics
DAİME CENGİZ
Doktora
Türkçe
2013
Diş HekimliğiSelçuk ÜniversitesiProtetik Diş Tedavisi Ana Bilim Dalı
YRD. DOÇ. İSA YÖNDEM
- Polietereterketon materyaline uygulanan farklı yüzey işlemlerinin rezin kompozit ile bağlanma dayanımına etkisinin değerlendirilmesi
Evaluation of the effect of different surface treatments applied on polyetheretherketone material on bonding resistance with resin composite
NATİGA İSRAFİL
Diş Hekimliği Uzmanlık
Türkçe
2020
Diş HekimliğiEskişehir Osmangazi ÜniversitesiProtetik Diş Tedavisi Ana Bilim Dalı
DOÇ. DR. CANAN AKAY
- İndirekt laminate veneer restorasyonlara uygulanan farklı tamir yaklaşımlarının makaslama bağlanma kuvveti ile değerlendirilmesi
Evaluation of shear bond strength of different repair procedures applied to indirect laminate veneers
ABDELRAHMAN WASFI FAYEZ MUSTAFA
Doktora
Türkçe
2019
Diş HekimliğiGazi ÜniversitesiDiş Hastalıkları ve Tedavisi Ana Bilim Dalı
DOÇ. DR. SUAT ÖZCAN
- Porselen lamina venerlerde immediat dentin kaplama prosedürü ve farklı yüzey işlemlerinin bağlanma dayanımına olan etkisinin incelenmesi
Investigation of the immediate dentin sealing procedure in porcelain laminate veneers and the effect of different surface treatments on bond strength
GÜLSÜM TÜRKMEN
Diş Hekimliği Uzmanlık
Türkçe
2022
Diş HekimliğiKocaeli ÜniversitesiProtetik Diş Tedavisi Ana Bilim Dalı
DR. ÖĞR. ÜYESİ SERDAR KILIÇ