AISI 316L paslanmaz çelik matrisli, bor karbür ve karbon nanotüp takviyeli nanokompozitlerin toz metalurjisi ile üretimi ve karakterizasyonu
Production and characterization of AISI 316L stainless steel matrix, boron carbide and carbon nanotube reinforced nanocomposites by powder metallurgy
- Tez No: 676125
- Danışmanlar: PROF. DR. HAYRETTİN AHLATCI
- Tez Türü: Yüksek Lisans
- Konular: Metalurji Mühendisliği, Metallurgical Engineering
- Anahtar Kelimeler: Belirtilmemiş.
- Yıl: 2021
- Dil: Türkçe
- Üniversite: Karabük Üniversitesi
- Enstitü: Lisansüstü Eğitim Enstitüsü
- Ana Bilim Dalı: Metalurji ve Malzeme Mühendisliği Ana Bilim Dalı
- Bilim Dalı: Belirtilmemiş.
- Sayfa Sayısı: 93
Özet
Bu çalışmada, AISI 316L paslanmaz çelik matrisli B4C ve KNT partikül takviyeli kompozit malzemeler sıcak pres yöntemi ile üretilmiş ve mikroyapı, mekanik, tribolojik ve korozyon özellikleri detaylı olarak incelenmiştir. Matris ve takviye malzemeleri toz olarak temin edilmiş ve yüksek enerjili bilyalı öğütme cihazında mekanik olarak karıştırıldıktan sonra sıcak preste sabit basınç ve sıcaklık altında sinterlenmiştir. Takviye elemanı olarak kullanılan B4C ve KNT partikülleri farklı oranlarda hem ayrı ayrı hem de birlikte ilave edilerek sinerjik etkileri incelenmiştir. B4C ve KNT takviye oranlarının artması ile kompozitlerin porozitesinde artış eğilimi görülürken, hesaplanan poroziteler %4,3 - %6,2 aralığında farklılıklar sergilemiştir. Yapılan mikroyapı incelemelerinde, taneler arası bölgelerde hem B4C ve KNT takviye partikülleri, hem de bunların demir ve krom ile reaksiyonları sonucu Fe3C ve Cr23C6 intermetaliklerinin oluştuğu görülmüştür. Sertlik ve basma testleri sonucunda 316L çeliğine farklı oranlardaki B4C ve KNT ilaveleri ile sertlikte artış elde edildiği görülmüştür. 316L çeliğinin dayanımına en büyük katkıyı hacimce %8 KNT takviyesi sağlamıştır (~%110). Artan B4C ve KNT ilaveleri, 316L paslanmaz çeliğin aşınma direncini sürekli olarak iyileştirmiştir. B4C ve KNT içeren kompozitlerin aşınma dirençleri karşılaştırıldığında ise B4C içeren kompozitlerin KNT içerenlerden bir miktar daha iyi aşınma direnci sergilediği görülmüştür. B4C ve KNT ilaveleri ile 316L' nin pasivasyon potansiyel aralığı düşmüş ve pasivasyon kabiliyeti olumsuz yönde etkilenmiştir. B4C ilavesi 316L' nin çukurcuk korozyon direncini KNT ilavesine göre daha az olumsuz etkilemiştir.
Özet (Çeviri)
In this study, AISI 316L stainless steel matrix B4C and KNT particle reinforced composite materials were produced by hot press method and their microstructure, mechanical, tribological and corrosion properties were examined in detail. The matrix and reinforcing materials were supplied as powder and were sintered in hot press under constant pressure and temperature after being mechanically mixed in a high energy ball mill. The synergistic effects of B4C and KNT particles used as reinforcement elements were added separately and together in different proportions. While the amounts of B4C and KNT reinforcements increased, the porosity of composites tended to increase. The calculated porosities varied from 4.3% to 6.2%. In the microstructure studies, it was observed that Fe3C and Cr23C6 intermetallics were formed in the intergranular areas as a result of both B4C and KNT reinforcement particles and their reaction with iron and chromium. As a result of the hardness and compression tests, it was observed that the hardness increased with the addition of B4C and KNT to 316L steel at different amounts. The biggest contribution to the strength of 316L steel was made by 8 vol.% KNT (~110%). Increasing B4C and KNT additions have continuously improved the wear resistance of 316L stainless steel. When the abrasion resistance of composites containing B4C and KNT was compared, it was seen that B4C containing composites displayed slightly better wear resistance than those containing KNT. With the B4C and KNT additions, the passivation potential range of 316L has decreased and the passivation ability has been adversely affected. B4C addition affected pitting corrosion resistance of 316L less negatively than KNT addition.
Benzer Tezler
- Dip coating of metal implants with antibacterialpolymer matrix for the prevention of implantassociated infections
İmlantla ilişkili enfeksiyonların önlenmesi için metalimplantların antibakteriyel polimer matrisli daldırmakaplaması
EMİNE HİLAL ALTINTOP
Yüksek Lisans
İngilizce
2024
Mühendislik Bilimleriİzmir Katip Çelebi ÜniversitesiBiyomedikal Mühendisliği Ana Bilim Dalı
DOÇ. DR. DİDEM ŞEN KARAMAN
- Empirical evaluation of storage materials and conditions for propellant grade white fuming nitric acid
Yakıt sınıfındaki beyaz dumanlı nitrik asit için depolama malzemeleri ve koşullarının deneysel değerlendirmesi
KAAN SAÇ
Yüksek Lisans
İngilizce
2022
Kimya MühendisliğiOrta Doğu Teknik ÜniversitesiKimya Mühendisliği Ana Bilim Dalı
PROF. DR. DENİZ ÜNER
DR. HACI EŞİYOK
- Kaynaklanmış 316L paslanmaz çeliklerin mekanik özelliklerinin ve gerilmeli korozyon davranışının incelenmesi
Investigation of mechanical properties and stress corrosion behavior of welded 316L stainless steels
ULVI AHMADLI
Yüksek Lisans
Türkçe
2023
Makine MühendisliğiManisa Celal Bayar ÜniversitesiMakine ve İmalat Mühendisliği Ana Bilim Dalı
DR. ÖĞR. ÜYESİ SELDA AKGÜN KAYRAL
- Mikrodalga ısıtmanın biyomedikal 316l alaşımının borlama kinetiğine etkisinin incelenmesi ve borür tabakasının karakterizasyonu
Investigation of the effect of microwave heating on boron kinetics of biomedical 316l alloy and characterization of boride layer
SAFİYE İPEK AYVAZ
Doktora
Türkçe
2020
Makine MühendisliğiManisa Celal Bayar ÜniversitesiMakine Mühendisliği Ana Bilim Dalı
DR. ÖĞR. ÜYESİ İBRAHİM AYDIN
- Plazma sprey kaplama yöntemiyle tek ve çift katmanlı kaplanan AISI 316L paslanmaz çeliğinin korozyon davranışlarının incelenmesi
Corrosion behaviour of single and double layer hydroxyapatite coatings on 316L stainless steel by plasma spray
OSMAN ASLAN
Yüksek Lisans
Türkçe
2015
Metalurji MühendisliğiAfyon Kocatepe ÜniversitesiMetalurji ve Malzeme Mühendisliği Ana Bilim Dalı
YRD. DOÇ. DR. YUSUF KAYALI