The effect of the thermomechanical process on microstructure and mechanical properties of (CO25CR15FE20NI40)83AL17 high entropy system
Termomekanik işlemin (CO25CR15FE20NI40)83AL17 sistemindeki yüksek entropili alaşımın mikroyapı ve mekanik özelliklerine etkisi
- Tez No: 683183
- Danışmanlar: DR. ÖĞR. ÜYESİ GÜL İPEK SELİMOĞLU, PROF. DR. HAKAN GAŞAN
- Tez Türü: Yüksek Lisans
- Konular: Metalurji Mühendisliği, Metallurgical Engineering
- Anahtar Kelimeler: Belirtilmemiş.
- Yıl: 2021
- Dil: İngilizce
- Üniversite: Eskişehir Teknik Üniversitesi
- Enstitü: Lisansüstü Eğitim Enstitüsü
- Ana Bilim Dalı: Malzeme Bilimi ve Mühendisliği Ana Bilim Dalı
- Bilim Dalı: Belirtilmemiş.
- Sayfa Sayısı: 67
Özet
AlCoCrFeNi alaşımı çok bileşenli alaşımlardan biridir ve iyi süneklik ve mukavemet kombinasyonu gibi önemli termomekanik özellikleri ile bilinir. Bu yüksek entropi alaşımlı system ayrıca yüksek sıcaklıklarda dayanıklılığa ve iyi basma dayanımına sahiptir. AlCoCrFeNi alaşım sistemi yapısında yüzey merkezli kübik (FCC) ve gövde merkezli kübik (BCC) yapıya sahiptir ve bu çok bileşenlisistem iyi süneklik ve mukavemet kombinasyonu sağlar. Bu çalışma kapsamında, akum ark ergitme ve dökme yöntemi ile üretilen ötektik bileşimdeki (Co25Cr15Fe20Ni40)83Al17 yüksek entropili alaşımının mekanik, termal ve termomekanik işlemlerinin mikroyapı ve sertlik üzerine etkisinin incelenmesi amaçlanmıştır. Plakalara kriyo haddeleme, soğuk haddeleme (oda sıcaklığında haddeleme) ve sıcak haddeleme (500 C, 750 C and 1000 C) ile farklı tavlama sıcaklıkları (750 C, 1000 C and 1100 C) uygulanmıştır. Kriyo haddeleme sonucunda hedeflenen deformasyonun oldukça altında, maksimum %7 deformasyon elde edilebilmektedir. Soğuk ve sıcak haddeleme sonucunda uygulanan deformasyon sırasıyla %50 ve %60 mertebelerine çıkmıştır. Sınırlı deforme edilebilirlik, XRD sonuçlarına göre uygulanan deformasyonla ötektik FCC-BCC faz karışımındaki artan BCC/B2 içeri ile ilişkilendirilmiştir. Ayrıca ötektik faz karışımındaki FCC/ L12 fazının 1000 C üzerinde tavlama ile arttığı gözlemlenmiştir. Maksimum sertlik (412 HV) ise %50 haddelemeden sonra elde edilirken, benzer sertlik değeri (399 HV) 750 C'de %53 deformasyon ile sıcak haddelemede ölçüldü ve bu da 1000 C'ye kadar dinamik yeniden kristalleşmenin belirgin bir etkisinin olmadığını gösteriyor.
Özet (Çeviri)
AlCoCrFeNi alloy is one of the multicomponent alloys and they are known as with their important thermomechanical properties such as good combination of ductility and strength. This high entropy alloy system has also durability at high temperatures and good compressive strength. AlCoCrFeNi alloy system has face centered cubic (FCC) and body centered cubic (BCC) in its structure and this multicomponent system provides good ductility and strength combination. In the scope of this study, it was aimed to analyze the effect of mechanical, thermal and thermomechanical processes on the microstructure and hardness of (Co25Cr15Fe20Ni40)83Al17 eutectic high entropy alloy, which was produced by the vacuum arc melting and casting method. Cryorolling, cold rolling (room temperature rolling) and hot rolling (500 C, 750 C and 1000 C) as well as different annealing temperatures (750 C, 1000 C and 1100 C) were applied to the plates. As the result of the cryorolling, maximum 7% deformation can be attained, which was well below the targeted deformation. The applied deformation has increased to 50% and 60 % as the result of cold and hot rolling, respectively. The limited deformability was attributed to the increased BCC/B2 content in the eutectic FCC-BCC phase mixture with the applied deformation according to XRD results. Moreover, it was observed that the ratio of FCC/L12 phase in the eutectic phase mixture was increased by annealing at or above 1000 C. The maximum hardness (412 HV), on the other hand, was attained after 50% cold-rolling while similar hardness value (399 HV) was measured after 53% hot rolling at 750C indicating the dynamic recrystallization did not have a pronounced affect till 1000C.
Benzer Tezler
- SR katkılı A360 alüminyum alaşımlarında termomekanik işlemin mekanik özelliklere etkisinin incelenmesi
Investıgatıon of the effect of thermomechanıcal process onmechanıcal propertıes of A360 alumınum alloys wıth SR doped
ALPER KARAKOCA
Doktora
Türkçe
2024
Makine MühendisliğiTekirdağ Namık Kemal ÜniversitesiMakine Mühendisliği Ana Bilim Dalı
PROF. DR. SERDAR OSMAN YILMAZ
- Toz metalürjisi yöntemiyle üretilmiş mikroalaşımlı çeliklere uygulanan termomekanik işlemlerin araştırılması
Investigation of thermomechanical processing applied to microalloyed steels produced by powder metallurgy method
DEMET TAŞTEMÜR
Doktora
Türkçe
2023
Metalurji MühendisliğiKarabük Üniversitesiİmalat Mühendisliği Ana Bilim Dalı
PROF. DR. SÜLEYMAN GÜNDÜZ
- Investigation microstructure development in steels using dilatometer
Başlık çevirisi yok
BAHA TEFEKKÜR
- Processing-structure-property relationship in injection molding of PP based compounds and composites for automotive applications
Otomotiv uygulamalarında kullanılan PP esaslı kompound ve kompozitlerin enjeksiyon yöntemi ile şekillendirilmesinde proses-yapı-özellik ilişkisinin incelenmesi
BURCU GİRGİNER ÖZÜNLÜ
Doktora
İngilizce
2022
Polimer Bilim ve Teknolojisiİstanbul Teknik ÜniversitesiMalzeme Bilimi ve Mühendisliği Ana Bilim Dalı
PROF. DR. FATMA SENİHA GÜNER