Grafen takviyeli alüminyum ve titanyum kompozitlerin elektrokimyasal empedans spektroskopisi ile korozyon davranışlarının incelenmesi
Investigation of the corrosion behavior of graphenereinforced aluminum and titanium composites byelectrochemical impedance spectroscopy
- Tez No: 695338
- Danışmanlar: DOÇ. DR. MEVLÜT GÜRBÜZ
- Tez Türü: Doktora
- Konular: Makine Mühendisliği, Mechanical Engineering
- Anahtar Kelimeler: Belirtilmemiş.
- Yıl: 2021
- Dil: Türkçe
- Üniversite: Ondokuz Mayıs Üniversitesi
- Enstitü: Lisansüstü Eğitim Enstitüsü
- Ana Bilim Dalı: Makine Mühendisliği Ana Bilim Dalı
- Bilim Dalı: Belirtilmemiş.
- Sayfa Sayısı: 145
Özet
Alüminyum ve titanyum alaşımları günümüzde en çok kullanılan metalik malzemelerdendir. Bu metaller özellikle savunma sanayi ve biyomedikal gibi alanlarda yaygın kullanılmaktadır. Uygulanacakları alanlarda minimum hasarla maksimum direnç göstermeleri bu metallere değer katmaktadır. Ancak, korozyon metal parçalarda çok yaygın görülen hasarlardan biridir. Metal parçaların kompozit formunda üretimi korozyon davranışını iyileştirmek için bir metot olup, takviye malzemesine bağlı olarak korozyon direncini ölçmek ve optimize etmek büyük değer taşımaktadır. Bu tez çalışmasında saf Al, Ti ve grafen takviyeli Al, Ti ve Ti64 (Ti6Al4V) numuneleri toz metalürjisi yöntemiyle üretilmiş ve korozyon davranışları incelenmiştir. Hazırlanan numunelere oda sıcaklığında NaCl, Ringer ve Saliva (yapay ağız suyu) çözeltilerinde elektrokimyasal korozyon EIS ölçüm denemeleri yapılmıştır. EIS sonuçları SEM görüntüleriyle karşılaştırılarak minimum hasarla maksimum korozyon direnç ve takviye malzemenin optimize değeri belirlenmiştir. Çalışmada saf Al ve grafen takviyeli Al kompozitlerin elektrokimyasal EIS korozyon direnç ölçüm denemeleri 3,5 ağ%. NaCl çözeltide yapılarak en iyi korozyon dayanımı (2,985 (Ω.cm2 )) 0,5 ağ%. grafen içeren AlGr05 numunesinde elde edilmiştir. SEM görüntülerinden grafen takviyesinin korozyon dayanımını iyileştirdiği görülmüştür. Ayrıca saf Ti ve grafen takviyeli örnekler için 3,5 %ağ. NaCl, Ringer ve Saliva çözeltileri için en iyi korozyon dayanımı ağırlıkça 0,15 %ağ. grafen içeren kompozitte (TiGr15) elde edilmiştir. NaCl, Ringer ve Saliva çözeltilerinde maksimum korozyon dayanımı sırasıyla 6.6939E05 (Ω.cm2 ), 8,0897E05 (Ω.cm2 ) ve 5,1791E05 (Ω.cm2 ) olarak bulunmuştur. Son olarak 1200 °C ve 1300 °C'de grafen takviyeli Ti64 kompozitler üretilmiştir. 1200°C'de üretilen kompozitler için yukarıda verilen çözeltiler için en iyi korozyon dayanıma ağırlıkça 0,45% grafen içeren örnek için elde edilmiş, en iyi korozyon dayanımı NaCl, Ringer ve Saliva çözeltilerinde sırasıyla 8,89 (k.Ω.cm2 ), 218,7 (k.Ω.cm2 ) ve 118,8 (k.Ω.cm2 ) olarak belirlenmiştir. 1300 °C'de üretilen kompozitler için ise ağırlıkça 0,60 %ağ. grafen içeren örnekte elde edilmiş, verilen çözeltiler için maksimum korozyon dayanımı NaCl'de 5,34E05 (Ω.cm2 ), Ringer'de 4,3276E05 (Ω.cm2 ) ve Saliva'da 3,5108E05 (Ω.cm2 ) olarak elde edilmiştir.
Özet (Çeviri)
Aluminum, titanium and their alloys are the widely used materials. These metals are widely used in fields such as aviation industry and biomedical applications. The fact that they show maximum resistance with minimum damage in the areas where they will be applied adds value to these metals. However, the corrosion is one of the most common damage to metal parts. The production of metal parts in composite form is a method to improve corrosion behavior, and it is of great value to measure and optimize corrosion resistance depending on the reinforcement material. In this thesis, pure Al, Ti and graphene reinforced Al, Ti and Ti64 (Ti6Al4V) samples were produced by powder metallurgy method and their corrosion behavior was investigated. Electrochemical corrosion EIS measurements were performed on the prepared samples in NaCl, Ringer and Saliva (artificial mouth water) solutions at room temperature. By comparing EIS results with SEM images, maximum corrosion resistance with minimum damage and optimized value of reinforcement material were determined. In the study, electrochemical EIS corrosion resistance measurement trials of pure Al and graphene reinforced Al composites were 3.5 wt%. Best corrosion resistance (2,985 (Ω.cm2)) 0.5 wt% made in NaCl solution. It was obtained in AlGr05 sample containing graphene. From the SEM images, it was seen that the graphene reinforcement improved the corrosion resistance. In addition, the best corrosion resistance with pure Ti and graphene reinforcement was obtained in the composite (TiGr15) containing 0.15% by weight graphene for NaCl, Ringer and Saliva solutions. The maximum corrosion resistance in NaCl, Ringer and Saliva solutions was found as 6.6939E05 (Ω.cm2), 8.0897E05 (Ω.cm2) and 5.1791E05 (Ω.cm2), respectively. Finally, graphene reinforced Ti64 composites were produced at 1200 and 1300 °C. For the composites produced at 1200°C, the best corrosion resistance was obtained for the sample containing 0.45% by weight graphene, the best corrosion resistance was 8,89 (k.Ω cm2), 218,7 (k.Ω cm2) ve 118,8 (k.Ω cm2) in NaCl, Ringer and Saliva solutions, respectively. For the composites produced at 1300 °C, the maximum corrosion resistance was obtained in the sample containing 0.60% graphene by weight, the maximum corrosion resistance was obtained 5.34E05 (Ω.cm2) in NaCl, 4.3276E05 (Ω.cm2) in Ringer and in Saliva as 3,5108E05 (Ω.cm2).
Benzer Tezler
- Grafen takviyeli alüminyum matrisli kompozit malzemelerin üretimi ve eşit kanallı açısal preslemenin (EKAP) malzeme özelliklerine etkisi
Production of composite materials with grafen reinforced aluminum matrix and the effect of equal channel angular pressing (ECAP) on material properties
NİHAL BAĞCI
Yüksek Lisans
Türkçe
2019
Metalurji MühendisliğiMersin ÜniversitesiMetalurji ve Malzeme Mühendisliği Ana Bilim Dalı
DOÇ. DR. ÖMER GÜLER
- Grafen takviyeli bakır matrisli kompozitlerin üretimi ve özelliklerinin incelenmesi
Manufacturing and examining the characteristics of graphen reinforced copper matrix composites
ÖNER KAĞAN ÖZER
Yüksek Lisans
Türkçe
2021
Metalurji MühendisliğiMersin ÜniversitesiMetalurji ve Malzeme Mühendisliği Ana Bilim Dalı
DOÇ. DR. ÖMER GÜLER
- Alüminyum matrisli farklı seramik takviyeli kompozitlere grafen ilavesinin termal ve mekanik özelliklere etkisinin incelenmesi
Investigation of the effect of grafen addition on thermal and mechanical properties of different ceramic reinforced aluminum matrix composites
SAFA POLAT
Doktora
Türkçe
2020
Metalurji MühendisliğiKarabük ÜniversitesiMetalurji ve Malzeme Mühendisliği Ana Bilim Dalı
PROF. DR. YAVUZ SUN
- Toz metalurjisi yöntemiyle üretilen Al2024 ve Al6061 matrisli, grafen – karbon nanotüp ve titanyum dioksik takviyeli kompozit malzemelerin mikroyapı ve mekanik özelliklerinin incelenmesi
Investigation of microstructure and mechanical properties of Al2024 and Al6061 matrix, graphene - carbon nanotube and titanium dioxide rei̇nforced composite materials produced by powder metallurgy method
ALİ ANTEPLİ
Yüksek Lisans
Türkçe
2021
Metalurji MühendisliğiUşak ÜniversitesiMalzeme Bilimi ve Nanoteknoloji Mühendisliği Ana Bilim Dalı
DR. ÖĞR. ÜYESİ KADİR GÜNDOĞAN
- Mikro ark oksidasyon işleminde elektrolite karbon nanotüp ilavesinin titanyum ve alaşımlarının yüzey özelliklerine etkisi
Effect of incorporationing carbon nanotube in to electrolyte in the micro arc oxidation process on the surface characteristics of titanium and its alloys
KAAN SELİM YAZICI
Yüksek Lisans
Türkçe
2013
Metalurji Mühendisliğiİstanbul Teknik ÜniversitesiMetalurji ve Malzeme Mühendisliği Ana Bilim Dalı
DOÇ. DR. MURAT BAYDOĞAN