Endüstriyel atık kauçuk katkılı geçirimli jeopolimerin karakteristik özellikleri
Characteristic properties of industrial waste rubber added geopolymer
- Tez No: 715688
- Danışmanlar: PROF. DR. SEVGİ DEMİREL
- Tez Türü: Yüksek Lisans
- Konular: Çevre Mühendisliği, İnşaat Mühendisliği, Environmental Engineering, Civil Engineering
- Anahtar Kelimeler: Atıklar, Endüstriyel simbiyoz, Kauçuk, Sürdürülebilirlik, Yaşam döngüsü, Yeniden kazanma, Wastes, Industrial symbiosis, Rubber, Sustainability, Life cycle, Recycling
- Yıl: 2022
- Dil: Türkçe
- Üniversite: Niğde Ömer Halisdemir Üniversitesi
- Enstitü: Fen Bilimleri Enstitüsü
- Ana Bilim Dalı: Çevre Mühendisliği Ana Bilim Dalı
- Bilim Dalı: Çevre Teknolojisi Bilim Dalı
- Sayfa Sayısı: Belirtilmemiş.
Özet
Bu çalışmada Ditaş Doğan Yedek Parça İmalat ve Teknik Anonim Şirketinin (DİTAŞ) proses atığı olan kauçuğunun ve İSKEN Sugözü Termik Santraline ait atık uçucu külünün jeopolimer harçların üretiminde kullanımının, fiziksel ve mekanik özelliklerine etkisi incelenmiştir. Harç oranları, kontrol numunelerinden itibaren Atık Kauçuk İçeren Geopolimer (AKJ) numunelerinde kauçuk oranı %0, %4, %8 ve %12 olacak şekilde hazırlanmıştır. Kauçuk atığı kırpıntıları 8.00 mm, 3.150 mm ve 1 mm eleklerden geçirilerek, 3 farklı boyutta olacak şekilde elde edilmiştir. Sırasıyla elenmiş atık kauçukların özgül ağırlıkları ise ortalama 1,14, 1,25 ve 1,37 olarak belirlenmiştir. Kauçuk boyutlarının artması ya da kauçuk oranının artması fiziksel ve mekanik deneylerde olumsuz etki olarak gözlemlenmektedir. En yüksek basınç dayanımı kontrol harcında 31.5 MPa olarak elde edilirken atık kauçuk katkılı olan karşımlarda ise %4 oranlı küçük boy kauçuk katkılı jeopolimerden (K4) 30.0 MPa olarak elde edilmektedir. Yapılan yaşam döngüsü analizi sonucunda %4 oranlı orta boy kauçuk (O4), %4 oranlı büyük boy kauçuk (B4), Kontrol ve Normal Harç sırasıyla % 45.06; 45.43; 53.16; 100 küresel ısınma potansiyeli ortaya koymuştur. Çalışma sonuçlarına göre jeopolimer üretiminin karbondioksit salınımını azaltma potansiyeli olduğu görülmektedir.
Özet (Çeviri)
In this study, the effects of the use of rubber, which is the process waste of Ditaş Doğan Yedek Parça Üretim ve Teknik Anonim Şirketi (DITAS), and the waste fly ash of İSKEN Sugözü Thermal Power Plant in the production of geopolymer mortars, on their physical and mechanical properties were investigated. Mortar ratios were prepared as 0%, 4%, 8% and 12% rubber in Waste Rubber Geopolymer (AKJ) samples starting from the control samples. Rubber waste scraps were obtained in 3 different sizes by passing through 8.00 mm, 3.150 mm and 1 mm sieves. The average specific gravity of the sifted waste rubbers was determined as 1.14, 1.25 and 1.37, respectively. An increase in rubber dimensions or an increase in rubber ratio is observed as a negative effect in physical and mechanical experiments. While the highest compressive strength is obtained as 31.5 MPa in the control mortar, it is obtained as 30.0 MPa from 4% small rubber added geopolymer (K4) in waste rubber added mixtures. As a result of the life cycle analysis, 4% medium rubber (O4), 4% large size rubber (B4), Control and Normal Mortar 45.06%; 45.43; 53.16; 100 global warming potential has revealed. It is seen that geopolymer production has the potential to reduce carbon dioxide emissions.
Benzer Tezler
- Kauçuk lif katkılı geopolimer betonların mekanik ve durabilite özelliklerinin araştırılması
Investigation of mechanical and durability properties of geopolymer concrete with rubber fiber
ARİF YILMAZOĞLU
Doktora
Türkçe
2022
İnşaat MühendisliğiKocaeli Üniversitesiİnşaat Mühendisliği Ana Bilim Dalı
DOÇ. DR. SALİH TANER YILDIRIM
- Zeolite filled polmeric gas separation membranes
Zeolit katkılı polimerik gaz ayırma membranları
ÇİĞDEM ATALAY
Yüksek Lisans
İngilizce
1994
Kimya Mühendisliğiİstanbul Teknik ÜniversitesiDOÇ.DR. BİLGÜL TANTEKİN ERSOLMAZ
- Atık tekstillerden ileri dönüşüm nanolifli yağlı aerosol filtre medyalarının üretimi ve karakterizasyonu
Production and characterization of upcycled nanofibrous oily aerosol filter media from waste textiles
MELİKE GÜNGÖR
Doktora
Türkçe
2026
Tekstil ve Tekstil Mühendisliğiİstanbul Teknik ÜniversitesiTekstil Mühendisliği Ana Bilim Dalı
DOÇ. DR. ALİ KILIÇ
- CoSb3 bazlı katkılı skutteruditelerin transport özellikleri
Transport properties of CoSb3 based skutterudities
SEDAT BALLIKAYA
Doktora
Türkçe
2010
Fizik ve Fizik Mühendisliğiİstanbul ÜniversitesiFizik Ana Bilim Dalı
PROF. DR. CTİRAD UHER
PROF. DR. EMİNE RIZAOĞLU
- Atık sulardan organik boyar maddelerin (RhB) gideriminde kullanılacak yeni nesil antimon aşılanmış kalay oksit–esaslı foto katalizör nanoparçacıkların sentezi
Synthesis of next-generation antimony-doped tin oxide-based photocatalyst nanoparticles for the removal of organic dyes (RhB) from wastewater
KÜBRA ÇALIŞKAN
Yüksek Lisans
Türkçe
2024
Metalurji MühendisliğiKonya Teknik ÜniversitesiMetalurji ve Malzeme Mühendisliği Ana Bilim Dalı
DOÇ. DR. ÖZLEM ALTINTAŞ YILDIRIM