Emaye kaplamaya uygun saclarda üretim proses parametrelerinin şekillendirme performansı ve hidrojen geçirgenlik direnci üzerine etkilerinin incelenmesi

Investigation of effective process parameters on forming performance and hydrogen permeability resistance of enameling steel

  1. Tez No: 744393
  2. Yazar: RAMAZAN UZUN
  3. Danışmanlar: PROF. DR. ADEM BAKKALOĞLU
  4. Tez Türü: Doktora
  5. Konular: Metalurji Mühendisliği, Metallurgical Engineering
  6. Anahtar Kelimeler: Belirtilmemiş.
  7. Yıl: 2022
  8. Dil: Türkçe
  9. Üniversite: Yıldız Teknik Üniversitesi
  10. Enstitü: Fen Bilimleri Enstitüsü
  11. Ana Bilim Dalı: Metalurji ve Malzeme Mühendisliği Ana Bilim Dalı
  12. Bilim Dalı: Belirtilmemiş.
  13. Sayfa Sayısı: 154

Özet

Bu tezin amacı, çelik üretim proses parametrelerinin emaye çeliklerinin şekillendirme özellikleri ve hidrojen geçirgenlik direnci üzerindeki etkilerini araştırmaktır. Emaye kaplama uygulamalarına uygun düşük karbonlu çeliklere emaye çelikleri denir. Emaye çelikleri beyaz eşya sektörü başta olmak üzere çeşitli sektörlerde kullanılmaktadır. Emaye kaplama işleminde, çelik yüzeye emaye hammaddesi frit çeşitli yöntemlerle malzeme yüzeylerine uygulanır ve ardından yüksek sıcaklıklarda pişirme işleminden geçirilir. Pişirme işleminden sonra geçen sürede kaplama yüzeylerinde bazı kusurlar görülebilir. Balık pulu kusuru, emaye kaplama işlemi sonrasında görülen en yaygın ve zararlı yüzey kusurudur. Kusur, pişirme işleminden sonra soğuma sürecinde emaye ve çelik arayüzeyine hidrojen difüzyonu nedeniyle oluşur. Çelik ve kaplama arayüzünde biriken hidrojen gazı lokal olarak yüksek basınç oluşturur ve kaplamanın yüzeyden atmasına sebep olur. Çeliğin hidrojen geçirgenlik direnci artırılarak kusur oluşumu önlenebilir. Hidrojen geçirgenlik direnci, kimyasal analiz, sıcak ve soğuk haddeleme parametrelerinin yanı sıra ısıl işlem parametreleri ile kontrol edilir. Bu parametreler aynı zamanda çeliklerin şekillendirme performansını da etkiler. Bu nedenle, emaye çeliklerinde hem hidrojen geçirgenlik direncini hem de şekillendirme performans gereksinimlerini karşılamak için çelik üretim proses parametrelerinin optimize edilmesi gerekir. Bu tez çalışmasında, üretim parametrelerinin emaye çeliklerin şekillendirme performansı ve hidrojen geçirgenlik direnci üzerindeki etkilerini incelemek için hem laboratuvar hem de endüstriyel ölçekte çalışmalar yapılmıştır. Tavlama parametreleri, çelik kimyasal analizine bağlı olarak termodinamik denge koşulları analiz edilerek belirlendi. Tez kapsamında gerçekleştirilen deneysel simülasyon çalışmaları, soğuk haddeleme miktarının artması, tavlama sıcaklığının düşmesi ve şekillendirme gerinim oranının artmasıyla hidrojen geçirgenlik direncinin iyileştirdiğini göstermiştir. Öte yandan, sıcak haddeleme esnasında uygulanan bobinin sarılma sıcaklığının artması, soğuk haddeleme esnasında uygulanan ezme oranı ve tavlama sıcaklıklarının artması ile şekillendirme özelliklerinde iyileşme gözlemlenmiştir. Son olarak, hidrojen geçirgenlik direnci ve şekillendirme özelliklerini optimum seviyede sağlayacak uygun çelik üretim parametreleri belirlenmiştir.

Özet (Çeviri)

The aim of this dissertation is to investigate the effects of steel production process parameters on forming properties and hydrogen permeability of enameling steels. Low carbon steels that are suitable for enamel coating applications are called enameling steels. Enameling steels are used in various industries, especially in the white goods industry. In enameling process, steel substrates are coated by various enameling techniques and then baked at high temperatures to cure the coating. Some imperfections can be seen on the coating surfaces after the firing process. Fish scale is the most common and detrimental surface defect that is seen after the enameling process. This defect occurs due to hydrogen diffusion to steel surface during cooling step. Hydrogen gas accumulating at the steel-coating interface pressurizes the coating locally and detaches it from the surface. Therefore, defect formation can be prevented by increasing hydrogen permeability resistance of the steel. Hydrogen permeability resistance is controlled by chemical analysis, hot and cold rolling parameters as well as annealing parameters. These parameters also affect the forming performance of steels. Therefore, steel production parameters must be balanced to satisfy both hydrogen permeability resistance and forming performance requirements in enameling steels. In this research, both laboratory and industrial scale studies were performed to examine the effects of production parameters on forming performance and hydrogen permeability resistance of enameling steels. Annealing parameters were determined by analyzing the thermodynamic equilibrium conditions depending on the chemical analysis of the steel. Physical simulation studies showed that hydrogen permeability resistance increases with increase in cold rolling quantity, decrease in annealing temperature and increase in forming strain ratio. On the other hand, improvement in forming properties was observed as coiling temperature, cold rolling ratio and annealing temperatures were increased. Finally, suitable steel production parameters were determined to have hydrogen permeability resistance and forming properties at an optimum level.

Benzer Tezler

  1. Yeni yönetmeliklere göre gıdalarla temasa uygun emaye yüzeylerin geliştirilmesiyeni

    Development of food contact safe enamel surfaces according to the new regulations

    GİZEM KADAKAL

    Yüksek Lisans

    Türkçe

    Türkçe

    2016

    Metalurji Mühendisliğiİstanbul Teknik Üniversitesi

    Malzeme Bilimi ve Mühendisliği Ana Bilim Dalı

    PROF. DR. ONURALP YÜCEL

  2. Taban malzeme ile emaye kaplama arasındaki difüzyon mekanizmasının araştırılması ve düşük metal migrasyonuna sahip emaye geliştirilmesi

    Investigation of diffusion mechanisms at substrate enamel interface and development of new enamel surface with low metal migration

    ÖZGE IŞIKSAÇAN

    Doktora

    Türkçe

    Türkçe

    2020

    Besin Hijyeni ve Teknolojisiİstanbul Teknik Üniversitesi

    Metalurji ve Malzeme Mühendisliği Ana Bilim Dalı

    PROF. DR. ONURALP YÜCEL

  3. Pişirici cihaz üretiminde tesis içi su geri kazanımının değerlendirilmesi

    Evaluation of water recovery at cooking device manufacturing plants

    EFE GÜMÜŞLÜ

    Yüksek Lisans

    Türkçe

    Türkçe

    2016

    Çevre Mühendisliğiİstanbul Teknik Üniversitesi

    Çevre Mühendisliği Ana Bilim Dalı

    DOÇ. DR. HAYRETTİN GÜÇLÜ İNSEL

  4. Development of aqueous-corrosion resistant alkaline borosilicate glass coating for use in hot water storage systems

    Sıcak su depolama sistemlerinde kullanılmak üzere sulu korozyona dayanıklı alkali borosilikat cam kaplamanın geliştirilmesi

    ÖMER FURKAN ÖTKEN

    Yüksek Lisans

    İngilizce

    İngilizce

    2024

    Metalurji MühendisliğiYıldız Teknik Üniversitesi

    Metalurji ve Malzeme Mühendisliği Ana Bilim Dalı

    DOÇ. DR. BUĞRA ÇİÇEK

  5. Alüminyum yüzey üzerindeki emaye kaplamalara titanyum dioksit katkısı ile fotokatalitik özellik kazandırılması

    Giving photocatalytic property to enamel coatingson aluminum by titanium dioxide additive

    ELİF DEMİRHAN

    Yüksek Lisans

    Türkçe

    Türkçe

    2014

    Kimya Mühendisliğiİstanbul Teknik Üniversitesi

    Kimya Mühendisliği Ana Bilim Dalı

    PROF. DR. HALE GÜRBÜZ