Geri Dön

Laboratuvar ölçekli haddeleme ünitesinde haddelenen alaşımlı çeliklerin mikroyapı ve mekanik özellik ilişkisinin araştırılması

Investigation of the relationship betweenmicrostructural and mechanical properties of alloyedsteels after rolling process on laboratory scalarolling mill

  1. Tez No: 744575
  2. Yazar: FURKAN YILMAZ KÜÇÜKAKARSU
  3. Danışmanlar: PROF. DR. SÜLEYMAN GÜNDÜZ
  4. Tez Türü: Yüksek Lisans
  5. Konular: Metalurji Mühendisliği, Metallurgical Engineering
  6. Anahtar Kelimeler: Belirtilmemiş.
  7. Yıl: 2022
  8. Dil: Türkçe
  9. Üniversite: Karabük Üniversitesi
  10. Enstitü: Lisansüstü Eğitim Enstitüsü
  11. Ana Bilim Dalı: İmalat Mühendisliği Ana Bilim Dalı
  12. Bilim Dalı: Belirtilmemiş.
  13. Sayfa Sayısı: 120

Özet

Bu çalışmada, ağırlıkça % 0,22 karbonlu yüksek mukavemetli düşük alaşımlı çelik ve ağırlıkça % 0,4 orta karbon içeren düşük alaşımlı çelik laboratuvar ölçeğinde üretilmiş olup toplam deformasyon % 42 olacak şekilde 4, 5 ve 6 pasoda sıcak haddelenmiştir. Çok pasolu sıcak haddeleme işleminden sonra numuneler iki gruba ayrılmıştır. Bu gruplardan birisi haddelenmiş şekliyle diğeri ise haddeleme sonrası ısıl işlem görmüş haliyle incelenmiştir. Sonuçlar, yüksek mukavemetli düşük alaşımlı çelik ve orta karbonlu düşük alaşımlı çeliğin mikroyapı ve mekanik özelliklerinin her iki durum içinde sıcak haddeleme koşullarından etkilendiğini göstermiştir. Yüksek mukavemetli düşük alaşımlı çelikten haddelenmiş numunelerdeki mukavemet değerlerinin paso sayısı arttıkça artma eğiliminde olduğu tespit edilmiştir. Yüksek mukavemetli ve düşük alaşımlı çelikten haddelenmiş numunelerin aksine, 1150 °C'de 45 dakika östenitlendikten sonra havada soğutulan yüksek mukavemetli düşük alaşımlı haddelenmiş ve ısıl işlem görmüş çelik numunelerde mekanik özelliklerin biraz düştüğü tespit edilmiştir. Mikroyapısal incelemeler haddelenmiş yüksek dayanımlı düşük alaşımlı çeliklerin haddelenmiş ve ısıl işlem uygulanmış çeliklere göre yapısında küçük boyutlu çökeltilere sahip olduğunu ve bundan dolayı çökelti sertleşmesi ile dayanımın arttığını göstermiştir. Çökelme sertleştirmesine ek olarak, yüksek mukavemetli düşük alaşımlı çelikten haddelenmiş numunelerdeki ince çıta beynitin ve blok halinde martenzit/östenit fazlarının bulunması mukavemet artışını desteklemektedir. Orta karbonlu düşük alaşımlı çelikten haddelenmiş numunelerdeki mukavemet değerlerinin paso sayısı arttıkça azalma eğiliminde olduğu görülmüştür. Orta karbonlu düşük alaşımlı çelikten haddelenmiş numunelerin aksine, 850 °C'de 30 dakika östenitlendikten sonra yağda soğutulan ve ardından 460 °C'de 60 dakika temperlenen orta karbonlu düşük alaşımlı haddelenmiş ve ısıl işlem görmüş çelik numunelerde mekanik özelliklerin arttığı tespit edilmiştir. Mikroyapısal incelemeler haddelenme sonrası ısıl işlem görmüş orta karbonlu düşük alaşımlı çeliklerin haddelenmiş çeliklere göre daha küçük boyutlu çökeltilere sahip olduğunu ve bundan dolayı çökelti sertleşmesi ile dayanımın arttığını göstermiştir.

Özet (Çeviri)

In this work, high strength low alloy steel with 0,22 wt.% carbon and medium carbon low alloy steel with 0,4 wt. % carbon were produced in laboratory scale and hot rolled with a total deformation of 42% via 4, 5 or 6 passes. After multi-pass hot rolling process, the samples were divided into two groups. One of these groups was examined in as rolled and the other in as heat treated after rolling. The results indicated that microstructural and mechanical properties of high strength low alloy steel and medium carbon low alloy steel are influenced by hot rolling conditions for both cases. It was determined that strength values in as rolled samples of high strength low alloy steel tend to increase with increment in rolling pass number. In contrast to as rolled samples of high strength and low alloy steel, it was seen that mechanical properties were slightly decreased in as rolled and heat-treated samples of high strength low alloy steel that were austenitized at 1150 °C for 45 min. and then cooled in still air. Microstructural investigations showed that finer precipitates in as rolled samples of high strength low alloy steel are obviously more than that of as rolled and heat-treated samples of high strength low alloy steel, as an evidence for higher strength results by precipitation hardening. Additionally, to precipitation strengthening, refinement of lath bainite and amount of blocky martensite/austenite in as rolled samples of high strength low alloy steel favor the increase in strength. However, the strength values in as rolled samples of medium carbon low alloy steel showed a tendency to decrease with increment in rolling pass number. In contrast to as rolled samples of medium carbon low alloy steel, it was seen that mechanical properties were increased in as rolled and heat-treated samples of medium carbon low alloy steel that were austenitized at 850 °C for 30 min., then oil cooled and then tempered at 460 °C for 60 minutes. Microstructural investigations showed that finer precipitates in as rolled and heat-treated samples of medium carbon low alloy steel are obviously more than that of as rolled samples, as an evidence for higher strength results by precipitation hardening.

Benzer Tezler

  1. İkiz merdaneli döküm yönteminde bakır ve çelik shell ile üretilen 5005 alüminyum alaşımlarında üretim parametrelerinin, mekanik özelliklerin ve mikroyapıların incelenmesi

    The investigation of production parameters, mechanical properties and microstructures of 5005 aluminum alloys produced by steel/copper and steel/steel shell pairs in twin roll casting method

    FURKAN BERKAY TAMER

    Yüksek Lisans

    Türkçe

    Türkçe

    2024

    Metalurji MühendisliğiSakarya Üniversitesi

    Metalurji ve Malzeme Mühendisliği Ana Bilim Dalı

    DOÇ. DR. SERDAR ASLAN

  2. Makine imalat sanayi için düşük karbonlu beynitik çelikalaşım ve proses tasarımı

    Alloy & process design of low carbon bainitic steel formachinery industry

    BERTAN PARMAKSIZOĞLU

    Yüksek Lisans

    Türkçe

    Türkçe

    2022

    Metalurji MühendisliğiBursa Teknik Üniversitesi

    İleri Teknolojiler Ana Bilim Dalı

    DOÇ. DR. NAZLI AKÇAMLI

    PROF. DR. ARCAN FEHMİ DERİCİOĞLU

  3. Experimental investigation of discrete to continuous vortex gust encounters

    Tekil sağanak karşilaşmasindan sürekli sağanak karşilaşmasina geçişin deneysel incelenmesi

    KÜBRA SOY

    Yüksek Lisans

    İngilizce

    İngilizce

    2023

    Makine Mühendisliğiİstanbul Teknik Üniversitesi

    Uçak ve Uzay Mühendisliği Ana Bilim Dalı

    PROF. DR. OKŞAN ÇETİNER YILDIRIM

  4. Laboratuvar ölçekli bir biyobenzerin biyofarmasötik sürecinin geliştirilmesi

    Development of the biopharmaceutical process of a lab-scale biosimilar

    TUĞÇE ANAKÖK

    Doktora

    Türkçe

    Türkçe

    2023

    BiyoteknolojiEge Üniversitesi

    Farmasötik Teknoloji Ana Bilim Dalı

    PROF. DR. ERCÜMENT KARASULU

  5. Investigation of microbial communities in laboratory scale anammox reactors using molecular methods

    Laboratuvar ölçekli anammox reaktörlerde mikrobiyal topluluğun moleküler yöntemlerle araştırılması

    ELİF ESEN

    Yüksek Lisans

    İngilizce

    İngilizce

    2013

    Biyoteknolojiİstanbul Teknik Üniversitesi

    İleri Teknolojiler Ana Bilim Dalı

    YRD. DOÇ. DR. ALPER TUNGA AKARSUBAŞI