Al 5052 alaşımının mikro ark oksidasyon yöntemiyle farklı katkı maddeleri ilave edilerek kaplanması ve yüksek sıcaklıkta tribolojik özelliklerinin incelenmesi
Coating of Al 5052 alloy by adding different additives by micro arc oxidation method and investigation of tribological properties at high temperature
- Tez No: 842933
- Danışmanlar: PROF. DR. BÜLENT ÖZTÜRK
- Tez Türü: Yüksek Lisans
- Konular: Metalurji Mühendisliği, Metallurgical Engineering
- Anahtar Kelimeler: Mikro ark oksidasyon, Al 5052, Grafit, h-BN, ZnO, Aşınma, Micro arc oxidation, Al 5052, Graphite, h-BN, ZnO, Wear
- Yıl: 2023
- Dil: Türkçe
- Üniversite: Karadeniz Teknik Üniversitesi
- Enstitü: Fen Bilimleri Enstitüsü
- Ana Bilim Dalı: Metalurji ve Malzeme Mühendisliği Ana Bilim Dalı
- Bilim Dalı: Malzeme Bilim Dalı
- Sayfa Sayısı: 99
Özet
Bu çalışmada, Al 5052 alaşımın yüzeyine mikro ark oksidasyon yöntemi ile kaplama işlemi uygulanmıştır. Alkali elektrolit başta olmak üzere mevcut elektrolit içerisine grafit, hegzagonal bor nitrür, çinko oksit partikülleri katılarak dört farklı elektrolit çözeltisi hazırlanmıştır. Kaplama sonrası numunelerin yüzey özellikleri ve yüksek sıcaklıklardaki tribolojik davranışları incelenmiştir.Numunelerin yüzey pürüzlülük değerleri kaplama sonrası artmış olup, en düşük grafit katkılı numunede 8,82 μm olarak elde edilmiştir. Kaplama kalınlık değerleri farklı elektrolit türleri ile değişiklik göstermiş olup en yüksek 230,1 μm olarak çinko oksit katkılı numunede, en düşük ise 118,5 μm olarak grafit katkılı numunede bulunmuştur. Numunelerin XRD analizlerinden, yapılarında Al, γ-Al2O3, α-Al2O3 θ-Al2O3, grafit, h-BN ve ZnO fazları tespit edilmiştir. Ortalama por boyutu ve por sayısı en az grafit katkılı numunede görülmüştür. Oda sıcaklığı (25 ºC) ve yüksek sıcaklıklarda (90, 150 ve 250 ºC) yapılan sürtünme ve aşınma deneylerinde numunelerin ortalama sürtünme katsayıları artan sıcaklıkla azalmış, özgül aşınma oranları ise artmıştır. Tüm sıcaklıklarda en düşük sürtünme katsayısı ve aşınma oranı grafit katkılı numunede meydana gelmiş olup, bu değerlerin sırasıyla 0,25 - 0,35 ve 1,495x10-2 - 2,185x10-2 mm3/(N.m) aralıklarında olduğu belirlenmiştir.
Özet (Çeviri)
In this study, coating process was applied to the surface of Al 5052 alloy by micro arc oxidation method. Four different electrolyte solutions were prepared by adding graphite, hexagonal boron nitride, zinc oxide particles to the existing electrolyte, especially the alkaline electrolyte. The surface properties of the samples after coating and their tribological behavior at high temperatures were studied. The surface roughness values of the samples increased after coating and were obtained as 8,82 µm in the lowest graphite doped sample. The coating thickness values varied with different electrolyte types and the highest was found in the zinc oxide doped sample as 230,1 µm and the lowest was found in the graphite doped sample as 118,5 µm. From the XRD analysis of the samples Al, γ-Al2O3 and α-Al2O3 phases were detected in addition to the existing contributions in the structure. The average por size and por number were observed in the least graphite-doped sample. In friction and wear experiments conducted at room temperature (25 ºC) and high temperatures (90, 150 and 250 ºC), the average friction coefficients of the samples decreased with increasing temperature, and the specific wear rates increased. The lowest coefficient of friction and wear rate at all temperatures occurred in the graphite doped sample, these values were determined in the ranges of 0,25-0,35 and 1,495x10-2 - 2,185x10-2 mm3/(N.m) respectively.
Benzer Tezler
- Application of fracture mechanical approach to study the environmentally assisted cracking of aluminium 5052 in 3% NaCl
Başlık çevirisi yok
KHURRAM SAJJAD KHAWAJA
- Alüminyum sürekli döküm yöntemi ile üretilmiş 5052-5182 alüminyum alaşımlarının şekillendirilebilirlik kabiliyetlerinin belirlenmesi
Determination of formability behaviours of 5052 and 5182 aluminium allaoys producet by continuous casting method
GÖKHAN ALPER
Yüksek Lisans
Türkçe
2003
Metalurji Mühendisliğiİstanbul Teknik ÜniversitesiMetalurji ve Malzeme Mühendisliği Ana Bilim Dalı
PROF. DR. SABRİ KYALI
- T4 ve T6 ısıl işlemli 6061 alüminyum levhanın iki eksenli gerilmeler altında şekil değiştirmesinin incelenmesi
Investigation of deformation of T4 & T6 heat treated 6061 aluminum plate under biaxial stress
EGEMEN UZ
Yüksek Lisans
Türkçe
2022
Makine Mühendisliğiİstanbul Teknik ÜniversitesiMakine Mühendisliği Ana Bilim Dalı
PROF. DR. ŞAFAK YILMAZ
- Otomotiv sektöründe kullanılan sac metal malzemelerin farklı teknikler ile oluşturulan birleşimlerinin yorulma özelliklerinin araştırılması
Investigation of fatigue properties of joints of sheet metal materials used in automotive industry with different joining techniques
YILMAZ BAYDEMİR
Yüksek Lisans
Türkçe
2023
Makine MühendisliğiAfyon Kocatepe ÜniversitesiMakine Mühendisliği Ana Bilim Dalı
DR. ÖĞR. ÜYESİ AHMET ÇETKİN
- 5052 alüminyum alaşım oranı 0, 6 olan metal matrisli kompozit malzeme ile mekanik araç krikosu gerilme analizi ve Taguchi metodu
Metal matrix composite material which contains 60 % al 5052 and mechanical jack structure analysis and Taguchi methode
MERVE KORAL
Yüksek Lisans
Türkçe
2018
Makine MühendisliğiEskişehir Osmangazi ÜniversitesiMakine Mühendisliği Ana Bilim Dalı
DOÇ. MELİH CEMAL KUŞHAN