Maraging 300 çeliğin frezelenmesinde kesici takım kaplamasının ve kesme parametrelerinin işleme performansı üzerindeki etkisinin deneysel ve istatiksel araştırılması

Experimental and statistical investigation of the effect of cutting tool coating and cutting parameters on machining performance in milling of maraging 300 steel

PDF İndir

  1. Tez No: 884821
  2. Yazar: ALİ ÇELİK
  3. Danışmanlar: PROF. DR. HALİL DEMİR
  4. Tez Türü: Yüksek Lisans
  5. Konular: Endüstri ve Endüstri Mühendisliği, Industrial and Industrial Engineering
  6. Anahtar Kelimeler: Belirtilmemiş.
  7. Yıl: 2024
  8. Dil: Türkçe
  9. Üniversite: Karabük Üniversitesi
  10. Enstitü: Lisansüstü Eğitim Enstitüsü
  11. Ana Bilim Dalı: İmalat Mühendisliği Ana Bilim Dalı
  12. Bilim Dalı: Belirtilmemiş.
  13. Sayfa Sayısı: 79

Özet

Bu çalışmada, Maraging 300 çeliğinin frezelenmesinde kesici takım kaplamasının ve kesme parametrelerinin işleme performansı üzerindeki etkileri araştırılmıştır. Ayrıca çıktı parametrelerinin en iyi değerleri için girdi parametreleri Taguchi yöntemi ile istatiksel analizi yapılmıştır. Deneyler sabit kesme derinliğinde (1 mm) ve kuru işleme şartlarında CNC dik işleme merkezinde gerçekleştirilmiştir. Deneyler tasarımı Taguchi L27 ortogonal dizinine göre hazırlanmıştır. Kontrol faktörleri olarak üç farklı kesici takım kaplaması (TiAlN, TiCrN+Al2O3+TiN ve AlTiCrN), üç farklı kesme hızı (80 m/dak, 130 m/dak ve 180 m/dak) ve üç farklı ilerleme miktarı (0,07 mm/dev, 0,12 mm/dev ve 0,17 mm/dev) seçilmiştir. Deneysel ve istatiksel sonuçlara göre en düşük kesme sıcaklığı A3B1C1 (AlTiCrN kaplı takım, 80 m/dak kesme hızı ve 0,07 mm/dev ilerleme miktarı) deney kombinasyonunda 34 °C olmuştur. En iyi yüzey pürüzlülüğü ve en düşük yüzey sertliği A3B3C1 (AlTiCrN kaplı takım, 180 m/dak kesme hızı ve 0,07 mm/dev ilerleme miktarı) deney kombinasyonunda sırası ile 0,07 µm ve 328 Hv ölçülmüştür. En yüksek takım ömrü AlTiCrN kaplı takımla ve 80 m/dak kesme hızında yapılan deneylerde elde edilmiştir. Varyans analiz sonuçlarına göre kesme sıcaklığı, yüzey pürüzlülüğü ve yüzey sertliği üzerine en etki parametre sırası ile %72,18 ile kesme hızı, %78,41 ile ilerleme miktarı ve %83,42 ile kesme hızı olduğu görülmüştür. Kesme sıcaklığı, yüzey pürüzlülüğü ve yüzey sertliği için yapılan doğrulama deneylerinin kabul edilebilir sınırlar içerisinde olduğu görülmüştür.

Özet (Çeviri)

In this study, the effects of cutting tool coating and cutting parameters on machining performance in milling Maraging 300 steel were investigated. Additionally, the input parameters were statistically analysis using the Taguchi method to find the best values of the output parameters. The experiments were carried out on a CNC vertical machining center at a constant depth of cutting (1 mm) and dry machining conditions. The experimental design was prepared according to the Taguchi L27 orthogonal array. Three different cutting tool coatings (TiAlN, TiCrN+Al2O3+TiN ve AlTiCrN), three different cutting speeds (80 m/min, 130 m/min ve 180 m/min) and three different feed rates (0,07 mm/rev, 0,12 mm/rev ve 0,17 mm/rev) were selected as control factors. According to experimental and statistical results, the lowest cutting temperature was 34 °C in the A3B1C1 (AlTiCrN coated tool, 80 m/min cutting speed and 0.07 mm/rev feed rate) experimental combination. Best surface roughness and lowest surface hardness in test combination A3B3C1 (AlTiCrN coated tool, 180 m/min cutting speed and 0.07 mm/rev feed rate) has been measured 0.07 µm and 328 Hv respectively. The highest tool life was obtained in experiments performed with AlTiCrN coated tool and 80 m/min cutting speed. According to the variance analysis results, the most effective parameters on cutting temperature, surface roughness and surface hardness were cutting speed with 72.18%, feed rate with 78.41% and cutting speed with 83.42%, respectively. Verification tests for cutting temperature, surface roughness and surface hardness were found to be within acceptable limits.

Benzer Tezler

  1. Tez No

    75617

    İmalatta kalite kontrol ve toplam kalite yönetimi

    Başlık çevirisi yok

    MURAT BAYKAL

    Yüksek Lisans

    Türkçe

    Türkçe

    1998

    Makine Mühendisliğiİstanbul Teknik Üniversitesi

    Makine Mühendisliği Ana Bilim Dalı

  2. Tez No

    66838

    GT yöntemlerinin sınıflandırması, performans ölçütleri, üretimle ilgili verileri kullanan yeni yöntemlere örnekler ve genetik algoritmalar

    Taxonomy of GT methods, performance measures,some new GT methods that is able to incorporate pertinent manufacturing data and genetic algorithms

    HATİCE DERİCİ

    Yüksek Lisans

    Türkçe

    Türkçe

    1997

    Endüstri ve Endüstri Mühendisliğiİstanbul Teknik Üniversitesi

    Endüstri Mühendisliği Ana Bilim Dalı

    DOÇ. DR. M. BÜLENT DURMUŞOĞLU

  3. Tez No

    20569

    Material requirements planning (MRP) manufacturing resource planning (MRP II) and the implementation of a dynamic production and inventory control system in a manufacturing company

    Başlık çevirisi yok

    AYŞE PEKER

    Yüksek Lisans

    İngilizce

    İngilizce

    1992

    İşletmeMarmara Üniversitesi

    Mühendislik Yönetimi Ana Bilim Dalı

    YRD. DOÇ. DR. LALE DURUİZ

  4. Tez No

    132876

    Manas'ın Semetey kolunda (İsa Cumabek Uulu Varyantı) çekimli fiiller

    Finite verbs in Semetey version (By İsa Cumabek Uulu) of Manas

    YASİN ŞERİFOĞLU

    Yüksek Lisans

    Türkçe

    Türkçe

    2003

    Türk Dili ve EdebiyatıNiğde Üniversitesi

    Türk Dili ve Edebiyatı Ana Bilim Dalı

    YRD. DOÇ. DR. HİKMET KORAŞ

  5. Tez No

    614003

    Şehir park donatılarının operasyonel coğrafi bilgi sistemiyle izlenmesi ve işletilmesi

    Monitoring and managing city park equipments with operational geographical information system

    SERKAN YEĞNİDEMİR

    Yüksek Lisans

    Türkçe

    Türkçe

    2019

    Jeodezi ve FotogrametriGebze Teknik Üniversitesi

    Harita Mühendisliği Ana Bilim Dalı

    PROF. DR. TAŞKIN KAVZOĞLU

    PROF. DR. MEHMET HALİS SAKA

Geri Dön