Çeşitli katkı maddelerinin (mermer tozu, grafen, titanyum dioksit) ağaç malzemelerin verniklenme ve yaşlandırma özellikleri üzerine etkisi
Effect of various additives (marble powder, graphene, titanium dioxide) on varnishing and aging properties of wood materials
- Tez No: 904258
- Danışmanlar: PROF. DR. TURGAY ÖZDEMİR
- Tez Türü: Doktora
- Konular: Ormancılık ve Orman Mühendisliği, Forestry and Forest Engineering
- Anahtar Kelimeler: Belirtilmemiş.
- Yıl: 2024
- Dil: Türkçe
- Üniversite: Karadeniz Teknik Üniversitesi
- Enstitü: Fen Bilimleri Enstitüsü
- Ana Bilim Dalı: Orman Endüstri Mühendisliği Ana Bilim Dalı
- Bilim Dalı: Belirtilmemiş.
- Sayfa Sayısı: Belirtilmemiş.
Özet
Bu çalışmada farklı oranlarda çeşitli katkı maddelerinin verniklerle karıştırılarak, ağaç malzemelerin radyal ve teğet kesitler üzerine püskürtme yöntemi ile uygulanarak yüzey işlem testleri ve UV yapay yaşlandırma performansları belirlenmiştir. Çalışmada dört ağaç türü (Doğu kayını (Fagus orientalis L.), Anadolu kestanesi (Castanea sativa) , Sarıçam (Pinus sylvestris), Doğu ladini (Picea orientalis)), iki vernik türü ( su bazlı ve poliüretan vernik), üç katkı maddesi grafen (%0.25, %0.50, %1), mermer tozu (% 2,5, %5) ve titanyum dioksit (%1, %2) çeşitli oranlarda kullanılmıştır. Yüzey işlem testleri yapışma direnci, aşınma direnci, aşınmada ağırlık kayıpları, salınımsal sertlik direnci ve parlaklık testi yapılmıştır. UV yapay yaşlandırma testi 0-200-400-600 saatlik zaman dilimlerinde yapılarak, öncesi, sırası ve sonrasında örneklerin salınımsal sertlik direnci, parlaklık testi, yüzey pürüzlülük, aşınma direnci ve yapışma direnci testi yapılmıştır. Sonuç olarak su bazlı verniklerin performansı poliüretan verniklerin performansından düşüktür. Grafen teğet kesitte poliüretan vernikle beraber aşınma direncini arttırmış, parlaklığı düşürmüştür.Titanyum dioksit yapışma direncini,salınımsal sertlik direncini arttırmıştır. Mermer tozu aşınma direncini, salınımsal sertlik direncini arttırmıştır. UV yapay yaşlandırma sonrası yüzey pürüzlülüğünü titanyum dioksit azaltırken, grafen ve mermer tozu arttırmıştır.
Özet (Çeviri)
In this study, surface treatment tests and UV artificial aging performances were determined by mixing various additives with varnishes at different ratios and applying them by spraying method on radial and tangential sections of wood materials. Four wood species (Eastern beech (Fagus orientalis L.), Anatolian chestnut (Castanea sativa), Yellow pine (Pinus sylvestris), Eastern spruce (Picea orientalis)), two varnish types (water-based and polyurethane varnish), three additives graphene (0.25%, 0.50%, 1%), marble powder (2.5%, 5%) and titanium dioxide (1%, 2%) were used at various rates. Surface treatment tests were performed for adhesion resistance, abrasion resistance, weight loss in abrasion, oscillatory hardness resistance and gloss test. UV artificial aging test was performed in 0-200-400-600 hours time periods and oscillatory hardness resistance, gloss test, surface roughness, abrasion resistance and adhesion resistance tests were performed before, during and after the samples. As a result, the performance of water-based varnishes is lower than that of polyurethane varnishes. Graphene increased the abrasion resistance and decreased the gloss with polyurethane varnish in the tangential section. Titanium dioxide increased the adhesion resistance, oscillatory hardness resistance. Marble powder increased wear resistance, oscillatory hardness resistance. Titanium dioxide decreased the surface roughness after UV artificial aging, while graphene and marble powder increased it.
Benzer Tezler
- İzmir'de bazı yolların kapatılarak yaya bölgeleri oluşturma da kent peyzajını geliştirme açısından yeniden planlanması üzerinde araştırmalar
Başlık çevirisi yok
BAHAR TÜRKYILMAZ
Yüksek Lisans
Türkçe
1985
Şehircilik ve Bölge PlanlamaEge ÜniversitesiŞehir ve Bölge Planlama Ana Bilim Dalı
- Diesel motorları yakıt püskürtme sistemlerinin dinamik simülasyonu
Başlık çevirisi yok
İRFAN KARAGÖZ
Yüksek Lisans
Türkçe
1986
Makine MühendisliğiUludağ ÜniversitesiMakine Mühendisliği Ana Bilim Dalı
PROF. DR. OĞUZ BORAT
- Nükleer rezonasta moleküler yapıların incelenmesi (yapısal faz geçiş kuramları üzerine bir inceleme)
Başlık çevirisi yok
ABDURRAHMAN ANDİÇ
Yüksek Lisans
Türkçe
1986
Fizik ve Fizik MühendisliğiUludağ ÜniversitesiFizik Ana Bilim Dalı
PROF. DR. AYTAÇ YALÇINER
- Bazı yer ve sırık fasulye çeşitlerinde optimal melezleme şartlarının tespiti üzerine bir araştırma
Başlık çevirisi yok
TÜRKAN KOÇLU
- Landsat uydusu aracılığı ile elde edilen görüntülerin sınıflandırılmaları ve bunlara ilişkin bilgisayar programlarının hazırlanması
Başlık çevirisi yok
G. FERZAN KÜÇÜKA
Yüksek Lisans
Türkçe
1985
Bilgisayar Mühendisliği Bilimleri-Bilgisayar ve KontrolEge ÜniversitesiBilgisayar Bilimleri ve Mühendisliği Ana Bilim Dalı
DOÇ. DR. HALİS PÜSKÜLCÜ
- Peyzaj düzenleme çalışmalarında kullanılan ve kullanılmaya uygun çeşitli taşların özellikleri ile İzmir ve yakın çevresinde bunlara ilişkin kaynaklar üzerinde araştırmalar
Başlık çevirisi yok
E. VECDİ KÜÇÜKERBAŞ
Yüksek Lisans
Türkçe
1985
Peyzaj MimarlığıEge ÜniversitesiPeyzaj Mimarlığı Ana Bilim Dalı
DOÇ. DR. İLÇİN ASLANBOĞA