Lazer sinter ile üretimde kullanılan Co-Cr alaşım tozlarının yeni toz ilavesi yapılmadan tekrar kullanımının alaşım tozunun kimyasal, fiziksel özelliklerine ve metal seramik bağlantısı üzerine etkisinin incelenmesi
The effect of reusing metal powders in laser sinter production without adding new powder on the chemical properties of the metal and the metal-porcelain connection
- Tez No: 913211
- Danışmanlar: PROF. DR. ORHUN EKREN
- Tez Türü: Diş Hekimliği Uzmanlık
- Konular: Diş Hekimliği, Dentistry
- Anahtar Kelimeler: Belirtilmemiş.
- Yıl: 2025
- Dil: Türkçe
- Üniversite: Çukurova Üniversitesi
- Enstitü: Diş Hekimliği Fakültesi
- Ana Bilim Dalı: Protetik Diş Tedavisi Ana Bilim Dalı
- Bilim Dalı: Belirtilmemiş.
- Sayfa Sayısı: Belirtilmemiş.
Özet
Amaç: Bu in vitro çalışmanın amacı, lazer sinter ile üretimde kullanılan Co-Cr alaşım tozlarının yeni toz ilavesi olmadan yeniden kullanımının alaşım tozunun kimyasal, fiziksel özelliklerine ve metal seramik bağlantısı üzerine etkisini değerlendirmektedir. Gereç ve Yöntem: Araştırmada metal örneklerin tamamının hazırlanmasında EOSINT M 270 (EOS GmbH, Krailling, Almanya) DMLS cihazı ve metal alaşım tozu olarak AdorBond CC PLus (Ador Dental GmbH, Hilden, Almanya) kullanıldı. 20 kg işlenmemiş bir toz lazer sinterleme cihazına yüklendi. Numuneler birinci (Grup 1) dördüncü (Grup 2), yedinci (Grup 3), onuncu (Grup 4) ve on üçüncü (Grup 5) üretim döngülerinde (N=15) üretildi. Numunelerin üretiminden önce toz yatağından analiz için toz alaşım örnekleri toplandı. Numunelere porselen uygulandıktan sonra elastik modül ve metal-porselen bağlantı dayanımı üç nokta bükme testi kullanılarak hesaplandı. Alaşım tozu numunelerinin kimyasal özellikleri SEM-EDS, lazer tanecik boyut dağılımı, Xrd Mikroanaliz Faz Analiz, ICP-MS – Eser element analizi ile incelendi. İstatiksel analiz için tek yönlü ANOVA ve Tukey testleri kullanıldı. Bulgular: Bağlantı dayanımı açısından gruplar arasında istatistiksel olarak anlamlı fark bulunamadı. (P>0.05) En yüksek bağlantı dayanımı değeri, 5. Grup'ta (78.26 ± 39.5 MPa), en düşük bağlantı dayanımı değeri 3. Grup'ta (56.86 ± 8.2 MPa) gözlenmiştir. Lazer tanecik boyutu analizleri, taramalı elektron mikroskop görüntüleri ve XRD testi açısından gruplar arasında belirgin farklar bulunamadı. ICP-MS sonuçlarına baktığımızda Mo, W ve Co iyonları 5. Grupta en yüksek değere ulaşmıştır. Si iyonu için en yüksek değer 4. Grupta ve Nb iyonu için de 3. Grupta en yüksek değerler tespit edilmiştir. Grupların hiçbirinde Cr iyonuna rastlanmamıştır. Sonuç: Çalışmanın sınırları dahilinde alaşım tozunun tekrar kullanılmasının metal-seramik bağlantısına etkisi yoktur. Metal alaşım tozunun fiziksel ve kimyasal özelliklerinde, yeniden kullanım sonucunda anlamlı bir değişiklik bulunmamıştır.
Özet (Çeviri)
Purpose: The aim of this in vitro study is to evaluate the effect of reusing Co-Cr alloy powders used in laser sinter production without adding new powder on the chemical, physical properties and metal-ceramic bonding of the alloy powder. Material and methods: In the research, EOSINT M 270 (EOS GmbH, Krailling, Germany) DSLM device was used to prepare all metal samples and AdorBond CC Plus (Ador Dental GmbH, Hilden, Germany) was used as metal alloy powder. 20 kg of unprocessed powder was loaded into the laser sintering device. Samples were produced in the first (Group 1), fourth (Group 2), seventh (Group 3), tenth (Group 4), and thirteenth (Group 5) production cycles (N=15). Powder alloy samples were collected from the powder bed for analysis before the production of the samples. After porcelain was applied to the samples, elastic modulus and metal-porcelain bond strength were calculated using the three-point bending test. The chemical properties of the alloy powder samples were examined by SEM-EDS, laser particle size distribution, Xrd Microanalysis Phase Analysis, ICP-MS - trace element analysis. One-way ANOVA and Tukey tests were used for statistical analysis. Results: No statistically significant difference was found between the groups in terms of bond strength (P>0.05). The highest bond strength value was observed in Group 5 (78.26 ± 39.5 MPa), and the lowest bond strength value was observed in Group 3 (56.86 ± 8.2 MPa). No significant differences were found between the groups in terms of laser particle size analysis, scanning electron microscope images, and XRD test results. According to the ICP-MS results, Mo, W, and Co ions reached the highest value in Group 5. The highest value for Si ion was detected in Group 4, and for Nb ion in Group 3. No Cr ions were found in any of the groups. Conclusion: Within the limitations of the study, it was concluded that reusing alloy powder have no effect on metal-ceramic bond strength. There has been no significant change in the physical and chemical properties of the metal alloy powder as a result of reuse.
Benzer Tezler
- Lazer sinter ile üretimde kullanılan Co-Cr alaşım tozlarının yenileme yöntemi ile yeniden kullanımının alaşım tozunun kimyasal, fiziksel özelliklerine ve metal- seramik bağlantısı üzerine etkisinin incelenmesi
Evaluation of the effect of reuse of Co-Cr alloy powders used in laser sinter production on the chemical and physical properties of the alloy powder and the metal-ceramic bond strength
BURÇE AKTAN
Diş Hekimliği Uzmanlık
Türkçe
2024
Diş HekimliğiÇukurova ÜniversitesiProtetik Diş Tedavisi Ana Bilim Dalı
PROF. DR. ORHUN EKREN
- Selektif lazer sinterizasyonu ile oluşturulan Co-Cr alaşımların invitro olarak değerlendirilmesi
Invitro assesments of selective laser sintered Co-Cr alloys
GÖZDE ANIL GÜRBÜZ
Doktora
Türkçe
2011
Diş HekimliğiÇukurova ÜniversitesiProtetik Diş Tedavisi Ana Bilim Dalı
YRD. DOÇ. DR. YURDANUR UÇAR
- Farklı materyal ve tekniklerle üretilen implant abutment materyallerinin AFM ve SEM ile yüzey pürüzlülüklerinin karşılaştırılması ve mikrobiyolojik tutulumlarının incelenmesi
Surface roughness comparison of implant abutments produced with different materials and techniques by AFM and SEM and investigation of microbiological retention
SERTER MERT SELAMET
Diş Hekimliği Uzmanlık
Türkçe
2023
Diş HekimliğiEge ÜniversitesiProtetik Diş Tedavisi Ana Bilim Dalı
PROF. DR. TOMURCUK ÖVÜL KÜMBÜLOĞLU
- Nikel ve kobalt katkılı seydişehir alümina tozlarından sinter seramik esaslı malzemelerin geliştirilmesi ve karakterizasyon çalışmaları
Development of sintered ceramic based materials from seydi̇şehi̇r alumina powders with nickel and cobalt additives and pertinent characterization investigations
CEREN ERGÜNEŞ
Yüksek Lisans
Türkçe
2016
Mühendislik Bilimleriİstanbul Teknik ÜniversitesiMalzeme Bilimi ve Mühendisliği Ana Bilim Dalı
PROF. DR. MUSTAFA LÜTFİ ÖVEÇOĞLU
- Kobalt esaslı alaşımların bağlayıcı matris olarak kullanıldığı doğal taş kesiminde kullanılan elmas kesici uçların karakterizasyonu
Characterization of diamond cutting tools using cobalt base alloys as the binding matrices
FERİT TOPALOĞLU
Yüksek Lisans
Türkçe
2013
Metalurji Mühendisliğiİstanbul Teknik ÜniversitesiMetalurji ve Malzeme Mühendisliği Ana Bilim Dalı
PROF. DR. EYÜP SABRİ KAYALI