Zirkonya seramiğe uygulanan farklı yüzey işlemlerinin faz değişimi ve bağlanma dayanımı üzerine etkileri
Effects of different surface treatments on phase change and bond strength of zirconia ceramics
- Tez No: 959475
- Danışmanlar: DOÇ. DR. MERAL ARSLAN MALKOÇ
- Tez Türü: Diş Hekimliği Uzmanlık
- Konular: Diş Hekimliği, Dentistry
- Anahtar Kelimeler: Femtosaniye lazer, Tribokimyasal Silika Kaplama, MDP, X-ışını kırınımı, Makaslama bağlanma dayanımı, Femtosecond laser, Tribochemical silica coating, MDP, X-ray diffractometers, Shear bond strength
- Yıl: 2023
- Dil: Türkçe
- Üniversite: Akdeniz Üniversitesi
- Enstitü: Diş Hekimliği Fakültesi
- Ana Bilim Dalı: Protetik Diş Tedavisi Ana Bilim Dalı
- Bilim Dalı: Belirtilmemiş.
- Sayfa Sayısı: Belirtilmemiş.
Özet
Amaç: Bu çalışmanın amacı, femtosaniye lazer (Fs) ve/veya tribokimyasal silika kaplama protokollerinin monolitik zirkonya üzerinde pürüzlülük, bağlanma mukavemeti ve faz dönüşümü üzerindeki etkilerini araştırmaktır. Yöntem: Yüz kırk dört zirkonya, yüzey işleme protokollerine göre rastgele dokuz alt gruba ayrıldı: Kontrol (C) (Grup 1), sinterleme öncesi tribokimyasal silika kaplama (SÖT) (Grup 2), sinterleme öncesi femtosaniye lazer (SÖF) (Grup 3), sinterleme öncesi ve sonrası tribokimyasal silika kaplama (SÖT+SST) (Grup 4), sinterleme öncesi femtosaniye lazer + sinterleme sonrası tribokimyasal silika kaplama (SÖF+SST) (Grup 5), sinterleme sonrası tribokimyasal silika kaplama (SST) (Grup 6), sinterleme sonrası femtosaniye lazer (SSF) (Grup 7), femtosaniye lazer ve sinterleme sonrası tribokimyasal silika kaplama (SSF+SST) (Grup 8), tribokimyasal silika kaplama ve sinterleme sonrası femtosaniye lazer (SST+SSF) (Grup 9). Panavia V5 dual cure self adeziv rezin siman zirkonya örneklerine yapıştırıldı. Yüzey morfolojik özellikleri ve pürüzlülük, taramalı elektron mikroskobu (SEM) ve optik (3D) profilometre ile değerlendirildi. Örneklerin simantasyonu sonrası 1 mm/dk çapraz kafa hızında kuvvet uygulanarak makaslama bağlanma dayanımı testi yapıldı. Faz dönüşümünü belirleyebilmek için her gruptan birer örnek X-ışını kırınımı analizine (XRD) tabi tutuldu. Veriler tek yönlü ANOVA ve Tukey HSD testleri ile analiz edildi. İstatistiksel anlamlılık düzeyi p<0,05 olarak kabul edildi. Bulgular: Grup 7 (SSF), Grup 4 (SÖT+SST), Grup 8 (SSF+SST), Grup 9 (SST+SSF), Grup 5 (SÖF+SST) grupları en yüksek SBS'yi gösterirken (P<0,05), kontrol ve Grup 2 (SÖT) grupları en düşük SBS'yi gösterdi (p<0,05). Femtosaniye lazer uygulanan gruplar en yükek pürüzlülüğü gösterdi. Yapılan XRD analizine göre monolitik zirkonya örneklerde, sinterden önce yapılan yüzey işlemleri sonucunda faz dönüşümü olmamıştır. Sinterden sonra uygulanan femtosaniye lazerin ise tribokimyasal silika kaplama uygulamasına göre çok daha az faz dönüşümüne neden olduğu görülmüştür. Sonuç: Klinik uygulamalar için sinterden önce ve sonra yüzey işlemlerinin (femtosaniye lazer ve tribokimyasal silika kaplama) kombine olarak uygulanması önerilebilir. Fs lazerin diş hekimliğinde klinik kullanımı henüz mümkün değildir. Bu nedenle Grup 4 (SÖT+SST), klinik uygulama için önerilebilir. Grup 4, Fs lazer uygulanan gruplarla aynı oranda yüksek SBS değeri vermiştir ancak Fs uygulanan gruplara göre daha fazla faz dönüşümüne neden olmuştur.
Özet (Çeviri)
Aim: The aim of this study was to investigate the effects of femtosecond laser (Fs) and/or tribochemical silica coating protocols on roughness, bond strength and phase transformation to monolithic zirconia. Materials and methods: One hundred forty four zirconia were randomly divided into nine subgroups according to surface treatment protocols: Control (C), tribochemical silica coating before sintering (TBS), Fs laser before sintering (FBS), tribochemical silica coating before and after sintering (TBS+TAS), Fs laser before sintering + tribochemical silica coating after sintering (FBS+TAS), tribochemical silica coating after sintering (TAS), Fs laser after sintering (FAS), Fs laser and tribochemical silica coating after sintering (FAS+TAS), tribochemical silica coating and Fs laser after sintering (TAS+FAS). Panavia V5 dual cure self adhesive resin cement was bonded to zirconia samples. Surface morphological properties and roughness were evaluated by scanning electron microscopy (SEM) and optical (3D) profilometer. After cementation of the samples, shear bond strength test was performed by applying force at a crosshead speed of 1 mm/min. One sample from each group was subjected to X-ray diffraction analysis (XRD) to determine the phase transformation.The data were analyzed with one-way ANOVA, and Tukey HSD tests at 0.05. significance level. Results: While the groups FAS, TBS+TAS, FAS+TAS, TAS+FAS, FBS+TAS had showed the highest SBS (P<0,05), control and TBS groups demonstrated the lowest SBS (p<0,05). Surface roughness value was found to be higher in femtosecond applied groups compared to other groups. According to the XRD analysis, there was no phase transformation in monolithic zirconia samples as a result of surface treatments before sintering. Femtosecond laser applied after sintering caused much less phase transformation than tribochemical silica coating. Conslusions: For clinical applications, a combination of surface treatments (femtosecond laser and tribochemical silica coating) before and after sintering may be recommended. Clinical use of the FS laser in dentistry is not yet possible. Therefore, Group 4 (SST+SST) can be recommended for clinical application. Group 4 gave the same high SBS value as the Fs laser treated groups, but caused more phase transformation than the Fs treated groups.
Benzer Tezler
- Farklı yüzey işlemi uygulanmış zirkonyum oksit esaslı alt yapıların üst yapı porselenine olan bağlanma dayanımının değerlendirilmesi
Evaluation of bond strength between veneering porcelains and different surface treated zirconium oxide based frameworks
NEVRİYE AKSU
Doktora
Türkçe
2015
Diş HekimliğiKaradeniz Teknik ÜniversitesiProtetik Diş Tedavisi Ana Bilim Dalı
PROF. DR. LÜTFÜ İHSAN ALADAĞ
- Farklı yüzey işlemlerinin ve yapay yaşlandırmanın y-tzp zirkonya seramiklerin faz dönüşümüne ve eğilme dayanımına etkisi
Effect of different surface treatments and artificial aging on the phase transformation and flexural strength of y-tzp zirconia ceramics
YENER OKUTAN
Doktora
Türkçe
2015
Diş HekimliğiSelçuk ÜniversitesiProtetik Diş Tedavisi Ana Bilim Dalı
DOÇ. DR. MÜNİR TOLGA YÜCEL
- Farklı yüzey işlemleri uygulanan y-tzp zirkonya ile veneer seramik arasındaki bağlanma dayanımının termal siklus öncesi ve sonrası değerlendirilmesi
Evaluation of surface treatments on shear bond strength between zirconia and veneer ceramic: Before and after thermal cyclic
AYŞEGÜL NAGEHAN ÖZEVCİMEN
Diş Hekimliği Uzmanlık
Türkçe
2018
Diş HekimliğiAkdeniz ÜniversitesiProtetik Diş Tedavisi Ana Bilim Dalı
DOÇ. DR. ÖMER KIRMALI
- Farklı yüzey işlemleri uygulanan zirkonya seramiğe üç farklı rezin simanın bağlanmasının incelenmesi
Investigation of bond strength of three different resin cements to zirconia ceramics which different surface treatments are applied
MERYEM GÜLCE SUBAŞI
Doktora
Türkçe
2011
Diş HekimliğiSelçuk ÜniversitesiProtetik Diş Tedavisi Ana Bilim Dalı
PROF. DR. ÖZGÜR İNAN
- Farklı yüzey işlemlerinin yeni nesil zirkonyanın makaslama bağlantı dayanımına etkisi
The effect of different surface treatments on the shear bond strength of new generation zirconia
MERVE BUSE KULTAŞ KALELİ
Diş Hekimliği Uzmanlık
Türkçe
2022
Diş HekimliğiSelçuk ÜniversitesiProtetik Diş Tedavisi Ana Bilim Dalı
PROF. DR. OĞUZ ERASLAN