Eklemeli imalat yöntemi ile üretilen farklı kalınlıklarda daimi kron materyallerinin artık monomer içeriğinin karşılaştırılması
Comparison of residual monomer content in permanent crown materials fabricated by additive manufacturing at different thicknesses
- Tez No: 975470
- Danışmanlar: DR. ÖĞR. ÜYESİ AYŞE RENÇBER KIZILKAYA
- Tez Türü: Diş Hekimliği Uzmanlık
- Konular: Diş Hekimliği, Dentistry
- Anahtar Kelimeler: 3 boyutlu yazıcı, daimi kron reçinesi, yüksek performanslı sıvı kromatografisi, artık monomer, 3D printing, permanent crown resin, high-performance liquid chromatography, residual monomer
- Yıl: 2025
- Dil: Türkçe
- Üniversite: Fırat Üniversitesi
- Enstitü: Diş Hekimliği Fakültesi
- Ana Bilim Dalı: Protetik Diş Tedavisi Ana Bilim Dalı
- Bilim Dalı: Belirtilmemiş.
- Sayfa Sayısı: Belirtilmemiş.
Özet
Günümüzde dijital dünyanın gelişmesiyle, insanların daha hızlı ve estetik çözümler arayışı artmaktadır. Diş hekimliğinde geleneksel yöntemlerle protez üretiminin zaman alıcı ve teknik bilgi gerektirmesi farklı üretim yöntemlerini gündeme getirmektedir. 3B baskı teknolojisi ile dijital iş akışı takip edilerek, hastalardan elde edilen taramalar ile sabit restorasyonun tasarım ve üretimi gerçekleştirilir. 3B yazıcılar sayesinde kişiselleştirilmiş ve daha hassas sabit restorasyonlar elde edilebilmektedir. Ancak bu yöntem ile üretilen sabit restorasyonların uzun vadeli performansı ve biyouyumluluğu üzerine daha fazla araştırmaya ihtiyaç duyulmaktadır. Bu çalışmada, diş hekimliğinde 3B yazıcı ile daimi kron restorasyonlarının üretiminde kullanılan farklı daimi kron reçineleri ve kontrol grubu olarak Cerasmart Nano Hibrit Seramik Blok materyali kullanıldı. Toplam 6 farklı materyal ve her bir materyal için 4 ayrı alt grup belirlendi. Her bir grupta n=8 olmakla birlikte toplamda oluşturulan 24 grup ve 192 adet örnek belirlendi. Her bir markadan 2 mm ve 4 mm'lik farklı kalınlıklarda üretilen numuneler 1 hafta ve 1 ay olmak üzere farklı zamanlarda etanol/su karışımında bekletildi ve elde edilen çözeltilerin HPLC cihazı kullanılarak monomer salınımları incelendi. Çalışmada parametrelerin gruplar arası karşılaştırmalarında Kruskal Wallis testi ve farklılığa neden çıkan grubun tespitinde Dunn's test kullanıldı. Parametrelerin kalınlık ve süreye göre iki grup arası karşılaştırmalarında Mann Whitney U test kullanıldı. Bis-GMA monomerinin, en yüksek ortalama salınım değeri Bego – 4 mm – 1 ay grubunda (360.16±133.71 ppm) ve en düşük ortalama salınım değeri DentaFab – 2 mm – 1 hafta grubunda (7.88±3.1 ppm) ölçüldü. TEGDMA monomerinin, en yüksek ortalama salınım değeri Bego – 4 mm – 1ay grubunda (1250.74±92.02 ppm) ve en düşük ortalama salınım değeri DentaFab – 2 mm – 1 hafta grubunda (12.67±3.69 ppm) ölçüldü. UDMA monomerinin, en yüksek ortalama salınım değeri Bego – 2 mm – 1 ay grubunda (20.03±4.43 ppm) ve en düşük ortalama salınım değeri Formlabs – 2mm – 1 hafta grubunda (1.84±0.97 ppm) ölçüldü. HEMA monomerinin, en yüksek ortalama salınım değeri Bego – 2 mm – 1 ay grubunda (6.85±5.33 ppm) ve en düşük ortalama salınım değeri DentaFab – 2 mm – 1 hafta grubunda (0.47±0.48 ppm) ölçüldü. Bego grubunda kalınlık arttıkça göreceli olarak en çok salınımı artan monomer TEGDMA ve süre ile birlikte göreceli olarak en hızlı salınımı olan monomer UDMA'dır. NextDent grubunda kalınlık arttıkça göreceli olarak en çok salınımı artan monomer ve süre ile birlikte göreceli olarak en hızlı salınımı olan monomer TEGDMA'dır. Formlabs grubunda kalınlık arttıkça göreceli olarak en çok salınımı artan monomer HEMA ve süre ile birlikte göreceli olarak en hızlı salınımı olan monomer UDMA'dır. Saremco grubunda kalınlık arttıkça göreceli olarak en çok salınımı artan monomer Bis-GMA ve süre ile birlikte göreceli olarak en hızlı salınımı olan monomer TEGDMA'dır. Ayrıca 1 aylık HEMA salınım değeri kalınlık artışıyla birlikte azalan tek değerdir. DentaFab grubunda kalınlık arttıkça göreceli olarak en çok salınımı artan monomer HEMA ve süre ile birlikte göreceli olarak en hızlı salınımı olan monomer Bis-GMA'dır. Artık monomer salınımının, kullanılan daimi kron reçinesinin markasına, numunelerin bekletilme süresine ve materyal kalınlığına bağlı olarak değişkenlik gösterdiği belirlenmiştir. Çalışmada en düşük salınım yapan monomerlerin UDMA ve HEMA olduğu, bunların toksik sınırın altında kaldığı ve klinik açıdan güvenli kabul edilebileceği görülmüştür. Buna karşılık, Bis-GMA (Bego ve Formlabs) ve TEGDMA (Bego) monomerleri bazı gruplarda toksik değerin üzerinde bulunmuş, bu da bu materyallerin kullanımında biyolojik risklerin dikkate alınması ve alternatif materyal seçiminde sonuçların göz önünde bulundurulması gerektiğini göstermiştir.
Özet (Çeviri)
With the development of the digital world today, the demand for faster and more esthetic solutions has increased. In dentistry, the time-consuming nature of conventional prosthesis fabrication and the requirement for technical expertise have brought alternative production methods to the forefront. Following a digital workflow with 3D printing technology, fixed restorations can be designed and manufactured using scans obtained from patients. Thanks to 3D printers, more personalized and precise fixed restorations can be achieved. However, further research is needed regarding the long-term performance and biocompatibility of restorations produced with this method. In this study, different permanent crown resins used in dentistry for the fabrication of permanent crown restorations with 3D printers were investigated, while Cerasmart Nano Hybrid Ceramic Block material was included as the control group. A total of six different materials and four subgroups for each material were defined. Each group contained n=8 specimens, yielding a total of 24 groups and 192 specimens. Samples of two different thicknesses (2 mm and 4 mm) were produced from each brand and immersed in an ethanol/water solution for either 1 week or 1 month. The eluates obtained were analyzed for monomer release using an HPLC device. For intergroup comparisons of the parameters, the Kruskal–Wallis test was used, while Dunn's test was applied to identify the groups responsible for the differences. For pairwise comparisons based on thickness and time, the Mann–Whitney U test was performed. The highest mean release value of Bis-GMA was measured in the Bego – 4 mm – 1 month group (360.16 ± 133.71 ppm), while the lowest was in the DentaFab – 2 mm – 1 week group (7.88 ± 3.1 ppm). For TEGDMA, the highest mean release was observed in the Bego – 4 mm – 1 month group (1250.74 ± 92.02 ppm), and the lowest in the DentaFab – 2 mm – 1 week group (12.67 ± 3.69 ppm). The highest mean release value of UDMA was in the Bego – 2 mm – 1 month group (20.03 ± 4.43 ppm), whereas the lowest was in the Formlabs – 2 mm – 1 week group (1.84 ± 0.97 ppm). For HEMA, the highest mean release was measured in the Bego – 2 mm – 1 month group (6.85 ± 5.33 ppm), while the lowest was in the DentaFab – 2 mm – 1 week group (0.47 ± 0.48 ppm). In the Bego group, the monomer that showed the most relative increase with thickness was TEGDMA, and the fastest release with time was observed for UDMA. In the NextDent group, TEGDMA showed the greatest relative increase with thickness as well as the fastest release with time. In the Formlabs group, HEMA showed the most relative increase with thickness, while UDMA had the fastest release with time. In the Saremco group, Bis-GMA showed the greatest relative increase with thickness, whereas TEGDMA exhibited the fastest release with time. Additionally, the 1-month HEMA release value was the only parameter that decreased with increasing thickness. In the DentaFab group, HEMA showed the most relative increase with thickness, while Bis-GMA demonstrated the fastest release with time. It was determined that residual monomer release varies depending on the brand of permanent crown resin used, the storage period, and the material thickness. The study showed that UDMA and HEMA were the monomers with the lowest release, remaining below toxic thresholds and therefore considered clinically safe. In contrast, Bis-GMA (Bego and Formlabs) and TEGDMA (Bego) exceeded toxic limits in some groups, highlighting the importance of considering potential biological risks in clinical applications of these materials and underlining the need to take these findings into account when selecting alternative materials.
Benzer Tezler
- Experimental investigation of laser parameters in molded interconnect devices manufacturing via laser direct structuring
Lazerle doğrudan yapılandırma yoluyla kalıplanmış ara bağlantı cihazlarının üretiminde lazer parametrelerinin deneysel incelenmesi
CANSU GİZEM AKAGÜNDÜZ
Yüksek Lisans
İngilizce
2023
Makine Mühendisliğiİstanbul Teknik ÜniversitesiMakine Mühendisliği Ana Bilim Dalı
DOÇ. DR. EMRECAN SÖYLEMEZ
- Eklemeli imalat yöntemi ile üretilen cam fiber katkılı kompozit malzemelerin yorulma davranışının deneysel olarak incelenmesi
Experimental investigation of fatigue behavior of glass fibre reinforced composite materials produced by additive manufacturing method
İBRAHİM ŞAMİL ŞENGÜLOĞLU
Yüksek Lisans
Türkçe
2025
Makine MühendisliğiMarmara ÜniversitesiMakine Mühendisliği Ana Bilim Dalı
DOÇ. DR. SELİM HARTOMACIOĞLU
- Değişken gözenekli hücresel yapıların metal eklemeli imalat için tasarımı ve üretilen yapıların tasarım ile uyumluluğunun araştırılması
Design for metal additive manufacturing of graded porous cellular structures and the i̇nvestigation of compatibility manufactured structures with design
AHMET MURAT DURSUN
Yüksek Lisans
Türkçe
2019
Makine MühendisliğiGazi ÜniversitesiMakine Mühendisliği Ana Bilim Dalı
PROF. DR. RAHMİ ÜNAL
- Numerical and experimental investigation on the crushing behaviour of auxetic lattice cells produced with additive manufacturing techniques
Eklemeli imalat teknikleri ile üretilmiş ökzetik kafes yapıların ezilme davranışlarının nümerik ve deneysel olarak incelenmesi
KADİR GÜNAYDIN
Doktora
İngilizce
2020
Makine Mühendisliğiİstanbul Teknik ÜniversitesiUçak ve Uzay Mühendisliği Ana Bilim Dalı
PROF. DR. HALİT SÜLEYMAN TÜRKMEN
DR. ÖĞR. ÜYESİ ANTONIO MATTIA GRANDE
- Çeşitli kafes yapıların dinamik ve yarı-statik yükleme koşulları altında enerji emilimlerinin incelenmesi
Investigation of energy absorption characteristics of various lattice structures under dynamic and quasi-static loading conditions
SALİH EMRE TUĞCU
Yüksek Lisans
Türkçe
2023
Makine MühendisliğiBursa Teknik ÜniversitesiMakine Mühendisliği Ana Bilim Dalı
DR. ÖĞR. ÜYESİ EMRE DEMİRCİ